Mixed-Mode Static and Fatigue Failure Criteria for Adhesively-Bonded FRP Joints

Fiber-reinforced polymer (FRP) composites are increasingly used in many load-bearing structures. Joints are the most critical structural elements as they often become the weak links in engineering structures. Bonding and bolting are two of the main joining techniques used for composite elements but, although bolted and bonded joints have their advantages and disadvantages, adhesively-bonded joints are often preferred. This is thanks to their better performance in terms of cost-effective structures with uniformly distributed stresses without the need for cutting fastener holes that result in high stress concentrations in the FRP adherends at the edges of the holes. In addition, due to the absence of stress concentrations, adhesively-bonded joints exhibit better fatigue behavior. However, the efficient and reliable use of adhesively-bonded joints requires a thorough understanding of their failure mechanisms under mixed-mode quasi-static and fatigue loading conditions. In real structural applications, failure of adhesively-bonded joints occurs due to crack initiation and propagation under varying mixed-mode ratios. Since it is difficult to describe this progressive fracture in a structural joint, fracture joints with constant mode-mixity ratios are used to determine the strain energy release rates for crack initiation and propagation. Subsequently, mixed-mode failure criteria based on the determined strain energy release rates can be established and used to model/predict the fatigue and fracture behaviors of structural joints. The main objectives of this thesis were to understand the fracture and fatigue behaviors of adhesively-bonded FRP fracture joints under Mode I, Mode II, and mixed-Mode I/II loading conditions and, consequently, develop mixed-mode static and fatigue failure criteria applicable to structural joints. To fulfill these objectives a combined experimental-analytical-numerical study was undertaken. Double cantilever beam (DCB-Mode I), end-load split (ELS-Mode II), and mixed-mode bending (MMB-Mode I/II) specimens were examined under quasi-static and constant amplitude fatigue loading. Analytical approaches were used to determine the strain energy release rates under quasi-static and fatigue loading, whereas phenomenological models were developed to characterize the fatigue and fracture behaviors of the joints. A new approach designated the “extended global method” was established and applied for the analysis of the quasi-static and fatigue experimental data and the fracture mode partitioning in the mixed-mode experiments. In parallel, non-linear finite element models were developed to simulate the quasi-static fracture behavior and investigate the effects of both the existing asymmetry and the observed fiber bridging on the fracture behavior of the examined joints. The bridging zone was modeled by zero-thickness cohesive elements. An exponential traction-separation description of the cohesive zone model wa