Hydrogen embrittlement (HE), also known as hydrogen-assisted cracking or hydrogen-induced cracking (HIC), is a reduction in the ductility of a metal due to absorbed hydrogen. Hydrogen atoms are small and can permeate solid metals. Once absorbed, hydrogen lowers the stress required for cracks in the metal to initiate and propagate, resulting in embrittlement. Hydrogen embrittlement occurs most notably in steels, as well as in iron, nickel, titanium, cobalt, and their alloys.
The creep properties of a cast gamma-alpha-2 lamellar titanium aluminide of type Ti-46Al-2W-0.5Si (at. %) containing beta-particles was investigated using both helium-implanted and non-implanted mater
Embrittlement by helium was investigated in a lamellar TiAl alloy under two conditions: Specimens were implanted to various amounts of helium up to 762 appm at temperatures from 630 °C to 1000 °C and