Publications by Jean-Marie Drezet

Investigation of residual stresses in planar dissimilar magnetic pulse welds by neutron diffraction

Residual stresses are investigated for the first time in a dissimilar AA1050-DP450 steel magnetic pulse weld using neutron diffraction. Close to the joint interface, tensile residual stresses are observed in the Al sheet and compressive residual stresses a ...

ELSEVIER SCI LTD2021

Residual stresses of friction melt bonded aluminum/steel joints determined by neutron diffraction

Jean-Marie Drezet

Near interfacial residual stresses are investigated in a joint composed of aluminum alloy and dual phase steel. A small step neutron diffraction scan was initially performed to determine the weld interface position along the measured transverse cross secti ...

ELSEVIER SCIENCE SA2019

On the Prediction of Hot Tearing in Al-to-Steel Welding by Friction Melt Bonding

Jean-Marie Drezet

Aluminum alloy AA6061 was welded to dual-phase steel 980 (DP980) by the friction melt bonding (FMB) process. Hot tears have been suppressed by controlling the thermomechanical cycle. In particular, the welding speed and the thermal conductivity of the back ...

2018

Miniaturized tube fixed plug drawing: determination of the friction coefficients and drawing limit of 316 LVM stainless steel

Jean-Marie Drezet, Stefano Mischler, Nicolas Paul Henry Chobaut, Bastien De Marco, Vance Nguyen, Stéphane Dobler

Tube drawing with a ﬁxed plug is investigated experimentally and numerically in order to optimise an industrial pass sequence. Tube drawings are performed on a laboratory drawing bench equipped with force, displacement and temperature sensors. The drawing ...

2018

Stress generation during the quenching of large AA2618 forgings: Finite element computations and validation against neutron diﬀraction measurements

Jean-Marie Drezet, Nicolas Paul Henry Chobaut, Denis Carron

Solutionising and quenching are key steps in the fabrication of heat treatable aluminium parts such as AA2618 compressor impellers for turbochargers. Quenching not only dictates the mechanical characteristics of the product but also induces residual stress ...

Elsevier2017

Characterisation of precipitation upon cooling of an AA2618 Al-Cu-Mg alloy

Jean-Marie Drezet, Nicolas Paul Henry Chobaut, Denis Carron

The precipitation of an AA2618 Al-Cu-Mg alloy is monitored during isothermal holdings and continuous coolings. The Time-Temperature-Property and Continuous-Cooling-Precipitation diagrams of AA2618 are obtained using in-situ resistivity and differential sca ...

Elsevier2016

Modeling of GP (I) zone formation during quench in an industrial AA7449 75mm thick plate

Jean-Marie Drezet, Charles-André Gandin, Patrick Schloth

The GP(I) zone formation during quench is simulated in an industrial Aluminumalloy AA7449 75mmthick plate by using a multi-class precipitation model. For this purpose, results of in situ SAXS experiments are reported. A methodology is presented that takes ...

Elsevier Sci Ltd2016

Measurements and Modeling of Stress in Precipitation-Hardened Aluminum Alloy AA2618 during Gleeble Interrupted Quenching and Constrained Cooling

Jean-Marie Drezet, Nicolas Paul Henry Chobaut, Denis Carron

Solutionizing and quenching are the key steps in the fabrication of heat-treatable aluminum parts such as AA2618 compressor impellers for turbochargers as they highly impact the mechanical characteristics of the product. In particular, quenching induces re ...

Springer Verlag2016

Early cluster formation during rapid cooling of an Al-Cu-Mg alloy: In situ small-angle X-ray scattering

Jean-Marie Drezet, Helena Van Swygenhoven, Patrick Schloth

The formation of Cu-Mg clusters in an Al-Cu-Mg aluminum alloy is observed by small-angle X-ray scattering during cooling. Cooling rates are choosen to mimic the different conditions obtained at the surface and in the center of large forgings. Clusters of 0 ...

Elsevier2015

Measurement of Mechanical Coherency Temperature and Solid Volume Fraction in Al-Zn Alloys Using In Situ X-ray Diffraction During Casting

Jean-Marie Drezet, Güven Kurtuldu, Bastien Gilbert Pierre Mireux

During solidification of metallic alloys, coalescence leads to the formation of solid bridges between grains or grain clusters when both solid and liquid phases are percolated. As such, it represents a key transition with respect to the mechanical behavior ...

Springer Verlag2015