Neutron embrittlement of in -core and out-of-core components made of ferritic steels is one of the key parameters limiting the life of power plants. Owing to the small volume of available irradiation facilities and the limited number of neutron-irradiated ...
This paper presents a series of Berkovich indentation results obtained on unirradiated and 7.2 MeV proton irradiated specimens of a Fe9Cr model alloy with an equiaxed ferritic microstructure. Using a energy degrader wheel made of 24 aluminum foils of diffe ...
A substantial amount of research effort has been applied to the field of environmentally assisted fatigue (EAF) due to the requirement to account for the EAF behaviour of metals for existing and new build nuclear power plants. We present the results of the ...
The mean stress effect on the fatigue life of 304L austenitic steel was evaluated at 300 degrees C in air and pressurized water reactor (PWR) environments. Uniaxial tests were performed in strain-control and load-control modes, with zero mean stress and a ...
Mean stress effects on fatigue life of a stainless steel in air and boiling water reactor (BWR) environments were evaluated by load-controlled tests. In stress-life, non-zero mean stresses increase life in low cycle fatigue regime in both environments and ...
Spalling in tantalum has been observed in an experiment aiming at testing an antiproton production target prototype at CERN’s HiRadMat Facility. The experiment consisted in impacting 47 intense and high-energy proton beams onto a target equipped with ten c ...
The study was undertaken to gain insight into the micro-mechanisms controlling plasticity at the micrometer scale of elastic-plastic metallic alloys. Dynamic nano-indentation tests, where a small harmonic force amplitude is superimposed during loading, ref ...
Elastic plastic fracture mechanics tests on different low-alloy reactor pressure vessel (RPV) steels in air and various simulated light water reactor environments revealed a clear, but moderate reduction of the fracture initiation resistance of RPV steels ...