Skip to main content

Search

Show all results for

Home

Person

Charlie Joseph Simon Blondeau

This person is no longer with EPFL

About
Privacy
Disclaimer

Copyright © 2025 EPFL, all rights reserved

Graph Chatbot

About this result

This page is automatically generated and may contain information that is not correct, complete, up-to-date, or relevant to your search query. The same applies to every other page on this website. Please make sure to verify the information with EPFL's official sources.

Related publications (3)

Please note that this is not a complete list of this person’s publications. It includes only semantically relevant works. For a full list, please refer to Infoscience.

Crack propagation in CFRP laminates under mode I monotonic and fatigue loads: A methodological study

John Botsis, Georgios Pappas, Charlie Joseph Simon Blondeau

Delamination in composite materials is often accompanied by fiber bridging that increases resistance to crack growth. Here, delamination of two unidirectional carbon/epoxy systems was studied under monotonic and displacement-controlled fatigue loading. One ...

ELSEVIER SCI LTD2021

Influence of ply-angle on fracture in antisymmetric interfaces of CFRP laminates

John Botsis, Georgios Pappas, Charlie Joseph Simon Blondeau

Laminated composites are prone to fracture at layer interfaces. Such damage impairs their structural response and engenders important constraints in design. In this work, the influence of ply orientation on crack growth resistance was studied for three dif ...

ELSEVIER SCI LTD2019

Experiments and numerical modelling on angle-ply laminates under remote mode II loading

John Botsis, Georgios Pappas, Charlie Joseph Simon Blondeau

Delamination is a very frequent damage mechanism that affects the integrity of laminated composites. In this study, the effect of ply orientation on crack growth resistance was analyzed for three different anti-symmetric interfaces (+/- 30 degrees, +/- 45 ...

ELSEVIER SCI LTD2020