Corrosion is a natural process that converts a refined metal into a more chemically stable oxide. It is the gradual deterioration of materials (usually a metal) by chemical or electrochemical reaction with their environment. Corrosion engineering is the field dedicated to controlling and preventing corrosion. In the most common use of the word, this means electrochemical oxidation of metal in reaction with an oxidant such as oxygen, hydrogen or hydroxide. Rusting, the formation of iron oxides, is a well-known example of electrochemical corrosion.
Tribocorrosion is a material degradation process due to the combined effect of corrosion and wear. The name tribocorrosion expresses the underlying disciplines of tribology and corrosion. Tribology is concerned with the study of friction, lubrication and wear (its name comes from the Greek "tribo" meaning to rub) and corrosion is concerned with the chemical and electrochemical interactions between a material, normally a metal, and its environment.
Wear is the damaging, gradual removal or deformation of material at solid surfaces. Causes of wear can be mechanical (e.g., erosion) or chemical (e.g., corrosion). The study of wear and related processes is referred to as tribology. Wear in machine elements, together with other processes such as fatigue and creep, causes functional surfaces to degrade, eventually leading to material failure or loss of functionality. Thus, wear has large economic relevance as first outlined in the Jost Report.
Tribocorrosion of passivating metals is a dynamic phenomenon causing degradation of materials by a combination of mechanical wear and electrochemical dissolution. The mechanical action typically produ
ELECTROCHEMICAL SOC INC2021
,
This study presents an improvement of an existing tribocorrosion model developed for passive CoCrMo alloys. This model is based on an empirical formalism established by Duncan Dowson in his pioneering
2021
, ,
Tribocorrosion, as the interaction between mechanical wear and electrochemical corrosion, has been found to be the main problem causing the failure and limiting the lifetime of metal-on-metal artifici