We report the formation of arbitrary photoconductive patterns made of tellurium (Te) nanocrystals by exposing a tellurite (TeO2-based) glass to femtosecond laser pulses. During this process, Te/TeO2-glass nanocomposite interfaces with photoconductive prope ...
The formation of elemental trigonal tellurium (t-Te) on tellurite glass surfaces exposed to femtosecond laser pulses is discussed. Specifically, the underlying elemental crystallization phenomenon is investigated by altering laser parameters in common tell ...
Ultrashort laser pulses, i.e., pulses emitted shorter than a picosecond, can tailor material properties by introducing permanent modifications locally in three dimensions. Remarkably, under a certain exposure condition, these modifications are accompanied ...
Chalcogenide glass exhibits a wide transmission window in the infrared range, a high refractive index, and nonlinear optical properties; however, due to its poor mechanical properties and low chemical and environmental stability, producing three-dimensiona ...
The structuring of mid-IR materials, such as chalcogenide glass (ChG), at the micro and nano scales, is of high interest for the fabrication of photonic devices in general, and for spectroscopy applications in particular. One efficient method for producing ...
Nanogratings were fabricated using a fs-laser inside more than 20 oxide glasses. Glass viscosity mostly dictates their thermal stability but deviation from this trend was observed in glasses containing large amount of Al2O3 or ZrO2. ...
We report on a self-organized process initiated on a potassium-tungsten-tellurite glass surface under repetitive femtosecond laser irradiation in a regime where cumulative effects lead to a localized melting. Specifically, we show that self-organized perio ...