Numerical investigation of two-dimensional Mode-II delamination in composite laminates

Thomas Keller, Anastasios Vassilopoulos, Congzhe Wang

Existing standards for delamination tests on composite materials typically employ one-dimensional (1D) beam specimens. However, such specimens may not represent real delamination scenarios in composite structures, where cracks tend to propagate in two dime ...

Elsevier Sci Ltd2024

Two-dimensional quasi-static delamination in composite laminates under Mode-I and Mode-II conditions

Congzhe Wang

Fiber-polymer composites consist of a polymer matrix and reinforcing fibers made of various materials. These composites exhibit exceptional properties, such as a high strength-to-weight ratio and excellent corrosion resistance, which has led to their incre ...

EPFL2024

Experimental investigation of two-dimensional Mode-II delamination in composite laminates

Thomas Keller, Anastasios Vassilopoulos, Congzhe Wang

The two-dimensional (2D) delamination growth in composite laminates under the Mode-II fracture condition was experimentally investigated using a novel set-up. Circular plate specimens with a centrally embedded pre-crack of two sizes were semi-clamped along ...

2023

TWO-DIMENSIONAL MODE-II DELAMINATION GROWTH IN COMPOSITE LAMINATES

Thomas Keller, Anastasios Vassilopoulos, Congzhe Wang

2023

Web buckling mechanism of pultruded GFRP bridge deck profiles subjected to concentrated load

Congzhe Wang, Yun Sun, Yuqing Liu

The web's local buckling is a major failure type of pultruded glass fiber-reinforced polymer (GFRP) bridge deck subjected to concentrated wheel loads. Three kinds of external actions-that is, in-plane shear force, local compressive force and bending moment ...

ELSEVIER SCIENCE INC2021

Numerical modeling of two-dimensional delamination growth in composite laminates with in-plane isotropy

Thomas Keller, Anastasios Vassilopoulos, Congzhe Wang

The two-dimensional (2D) delamination growth in fiber-reinforced polymer (FRP) laminates with in-plane isotropy under Mode I loading condition was numerically investigated using finite element analyses. Two sizes of plate models were developed, focusing on ...

2021