Fracture and Fatigue of Adhesively-Bonded Fiber-Reinforced Polymer Structural Joints
Graph Chatbot
Chat with Graph Search
Ask any question about EPFL courses, lectures, exercises, research, news, etc. or try the example questions below.
DISCLAIMER: The Graph Chatbot is not programmed to provide explicit or categorical answers to your questions. Rather, it transforms your questions into API requests that are distributed across the various IT services officially administered by EPFL. Its purpose is solely to collect and recommend relevant references to content that you can explore to help you answer your questions.
New load-bearing structures made of fiber-reinforced polymer (FRP) composites comprise
adhesively-bonded joints, which are components vulnerable to fatigue failure. These
structural components are frequently subjected to complex cyclic loading histories ...
The optimization of the forming of ODS tubes is linked to the choice of an appropriated constitutive model for modeling the metal forming process. In the framework of a unified plastic constitutive theory, the strain-controlled cyclic characteristics of a ...
This paper describes the numerical analysis method used to estimate welding induced residual stresses in K-shape tubular bridge joints. The knowledge of residual stress distribution is required to design the geometry of K-joints loaded under fatigue stress ...
The influence of welding tensile residual stresses on fatigue crack growth in bridge tubular K-joints is investigated through experimental testing of large-scale specimens. Crack development is monitored using the alternating current potential drop method. ...
Limited reliability of ferroelectric-based actuators restricts their use in high-performance applications, where stress-induced cracking of ferroelectric ceramics often leads to fatal failure. The main limiting factors are the relatively small fracture tou ...
A series of fatigue experiments was performed in order to investigate the effect of the R-ratio on the fatigue/fracture behavior of adhesively-bonded pultruded GFRP double cantilever beam joints. Constant amplitude fatigue experiments were carried out unde ...
Due to the difficulties of fracture mechanics in dealing with multicrack problems, the continuum-based numerical methods always encounter mathematical problems when modeling rock fragmentation, so the alternative discontinuum-based numerical approaches are ...
The uncertainty of the crack tip position inside composite coupons during a delamination test under variable fracture mode conditions reduces the accuracy of the experimental results. In this work a method is presented where the crack tip position is locat ...
This research project experimentally and numerically investigates the growth and coalescence of pre-existing voids for a wide range of stress states in a ductile matrix with a special focus on shear dominated loading conditions and presents quantitative ki ...
Stress relief treatment is often required prior to sawing aluminum DC cast products in order to prevent crack formation and significant safety concerns due to the presence of high residual stresses generated during casting. Numerical models have been devel ...
Carlos E. Suarez TMS (The Minerals, Metals & Materials Society), 20122012