Measurement of effective piezoelectric coefficients of PZT thin films for energy harvesting application with interdigitated electrodes
Graph Chatbot
Chat with Graph Search
Ask any question about EPFL courses, lectures, exercises, research, news, etc. or try the example questions below.
DISCLAIMER: The Graph Chatbot is not programmed to provide explicit or categorical answers to your questions. Rather, it transforms your questions into API requests that are distributed across the various IT services officially administered by EPFL. Its purpose is solely to collect and recommend relevant references to content that you can explore to help you answer your questions.
A review is given on the current state of the art in piezoelectric micromachined ultrasonic transducers (pMUT). It is attempted to quantify the limits of pMUT's with respect to the electromechanical coupling, and to relate current achievements. Main needs ...
Laser metal forming is an attractive process for rapid prototyping or the rebuilding of worn parts. However, large tensile stress may arise in layers deposited by laser melting of powder. A potential solution is to preheat the substrate before and during d ...
Structural investigations of SrTiO3 thin films deposited by pulsed laser ablation onto MgO and LaAlO3 substrates are presented. The residual strain along the c -axis (the growth direction) was evaluated with conventional X-ray diffraction. Evaluation of th ...
Unexpectedly high-longitudinal piezoelectric coefficients have recently been reported in c-axis oriented Pb(Zr,Ti)O-3 thin films with morphotropic phase boundary composition [Fu , Appl. Phys. Lett. 80, 3572 (2002)]. Our analysis and experimental results sh ...
Thin films of neodymium-modified bismuth titanate Bi3.44Nd0.56Ti3O12 (BNT) were grown on Pt/TiO2/SiO2/Si substrates using chemical solution deposition method. The capacitors made by applying top Au electrodes on BNT films showed significantly improved valu ...
We studied polarization switching of 295 nm thick -oriented-Pb(Zr0.45Ti0.55)O-3 (PZT) thin-film capacitors through a polarization hysteresis loop and piezoelectric force microscopy (PFM) on top of the Pt electrode. Positive voltage pulses of 450 kV/cm ...
Three wet chemistry routes were used to synthesize Ba0.99Zr0.8Y0.2O3-delta (BZY20) and to avoid the drawbacks of the conventional mixed oxide route used for its preparation. Pure samples were prepared using the Matrix Trapping and Decomposition (MTD) and P ...
Stress-induced changes in the imprint and switching behavior of (111)-oriented Pb(Zr,Ti)O-3 (PZT)-based capacitors have been studied using piezoresponse force microscopy. Visualization of polarization distribution and d(33)-loop measurements in individual ...
The dynamic piezoelectric response of SrBi4Ti4O15 ceramics with Aurivillius structure was investigated at high alternating stress, low frequencies (0.01 to 100 Hz), and temperatures from 20 to 200 degreesC. The piezoelectric nonlinearity, observed only at ...
The dynamic piezoelectric response of SrBi4Ti4O15 ceramics with Aurivillius structure was investigated at high alternating stress, low frequencies (0.01 to 100 Hz), and temperatures from 20 to 200 degreesC. The piezoelectric nonlinearity, observed only at ...