Preparation and Characterization of High-Surface-Area Bi(1-x)/3V1-xMoxO4 Catalysts

Lioubov Kiwi, Alexandre Nell
2014
Journal paper
Abstract

We report the successful application of a templating approach employing ordered mesoporous carbon to the synthesis of BiVO4, Bi2Mo3O12, and Bi0.85V0.55Mo0.45O4 and the performance of these materials as catalysts for the oxidation of propene to acrolein. Ordered mesoporous carbon templates were used to control the nucleation and growth of the mixed metal oxide crystals, allowing higher final surface areas to be obtained. The resulting materials were characterized by X-ray diffraction, Raman spectroscopy, transmission electron microscopy, X-ray photoelectron spectroscopy, and BET surface area analysis. The surface area of the mixed metal oxide catalysts was found to depend on the type of mesoporous silica used to prepare the carbon template and on the conditions under which the carbon template was formed. Through an appropriate choice of template, the surface areas of the mixed metal oxides exceeded 15 m(2)/g. Catalytic testing revealed that materials produced via templating in ordered mesoporous carbon had per-gram activities that were up to 85 times higher than those produced by a conventional hydrothermal synthesis and exhibited stable catalytic activities over 24 h.

About this result
This page is automatically generated and may contain information that is not correct, complete, up-to-date, or relevant to your search query. The same applies to every other page on this website. Please make sure to verify the information with EPFL's official sources.

Graph Chatbot

Chat with Graph Search

Ask any question about EPFL courses, lectures, exercises, research, news, etc. or try the example questions below.

DISCLAIMER: The Graph Chatbot is not programmed to provide explicit or categorical answers to your questions. Rather, it transforms your questions into API requests that are distributed across the various IT services officially administered by EPFL. Its purpose is solely to collect and recommend relevant references to content that you can explore to help you answer your questions.