Microstructure examination of Fe-14Cr ODS ferritic steels produced through different processing routes

Various thermo-mechanical treatments were applied to refine and homogenise grain size and improve mechanical properties of hot-isostatically pressed (HIP) 14%Cr ODS ferritic steel. The grain size was reduced, improving mechanical properties, tensile strength and Charpy impact, however bimodal-like distribution was also observed. As a result, larger, frequently elongated grains with size above 1 mu m and refined, equiaxed grains with a diameter ranging from 250 to 500 nm. Neutron diffraction measurements revealed that for HIP followed by hydrostatic extrusion material the strongest fiber texture was observed oriented parallel to the extrusion direction. In comparison with hot rolling and hot pressing methods, this material exhibited promising mechanical properties: the ultimate tensile strength of 1350 MPa, yield strength of 1280 MPa, total elongation of 21.7% and Charpy impact energy of 5.8 J. Inferior Charpy impact energy of similar to 3.0J was measured for HIP and hot rolled material, emphasising that parameters of this manufacturing process still have to be optimised. As an alternative manufacturing route, due to the uniform microstructure and simplicity of the process, hot pressing might be a promising method for production of smaller parts of ODS ferritic steels. Besides, the ductile-to-brittle transition temperature of all thermo-mechanically treated materials, in comparison with as-HIPped ODS steel, was improved by more than 50%, the transition temperature ranging from 50 to 70 degrees C (323 and 343 K) remains still unsatisfactory. (C) 2014 Elsevier B.V. All rights reserved.

Development and characterisation of a new ODS ferritic steel for fusion reactor application

Nadine Baluc, Zbigniew Oksiuta

This paper describes the microstructure, tensile properties and Charpy impact resistance of a reduced activation oxide dispersion strengthened ferritic steel Fe-14Cr-2W-0.3Ti-0.3Y(2)O(3) produced by mechanical alloying of a pre-alloyed, gas atomised steel powder with Y2O3 particles, compaction by hot extrusion at 1100 degrees C, hot rolling at 700 degrees C and heat treatment at 1050 degrees C for 1 h. At room temperature the material exhibits a high ultimate tensile strength of about 1420 MPa and high yield strength of about 1340 MPa in the transverse direction. In the longitudinal direction the values are about 10% lower, due to the anisotropy of the microstructure (elongated grains in the rolling direction). At 750 degrees C the material still exhibits relatively high yield strengths of about 325 MPa and 305 MPa in the longitudinal and transverse directions, respectively. The material exhibits reasonable uniform and total elongation values over the temperature range 23-750 degrees C, in both transverse and longitudinal directions. The material exhibits weak Charpy impact properties in the transverse direction. Charpy impact properties are slightly better in the longitudinal direction, with upper shelf energy of about 4.2 J and a ductile-to-brittle transition temperature of about 8.8 degrees C. (C) 2009 Elsevier B.V. All rights reserved.

Elsevier2009

Microstructure and mechanical properties of an ODS RAF steel fabricated by hot extrusion or hot isostatic pressing

Nadine Baluc, Zbigniew Oksiuta

Ingots of an oxide dispersion strengthened reduced activation ferritic steel with the Fe-14Cr-2W-0.3Ti-0.3Y(2)O(3) chemical composition (in wt.%) were synthesized by mechanical alloying of elemental powders with 0.3 wt.% Y2O3 particles in a planetary ball mill, in a hydrogen atmosphere. and compacted by either hot extrusion or hot isostatic pressing. The microstructures of the obtained materials were characterized by means of light microscopy, transmission electron microscopy and chemical analyses. The mechanical properties were evaluated by means of Vickers microhardness measurements and tensile tests. It was found that the microstructure of both materials is composed of ferritic grains having a submicron size and containing nanometric Y-Ti-O oxide particles with a mean size of about 10 nm, uniformly distributed in the matrix. The oxide particles in the hot extruded steel were identified as YTiO3 phase. In larger (>10 nm) oxide particles Cr was found next to Ti, Y and O. The steel produced by hot extrusion exhibits much higher tensile strength and hardness at low to moderate temperatures, as compared to the steel fabricated by hot isostatic pressing, which was mainly attributed to smaller pores but also to more severe work hardening in the case of the hot extruded steel. (C) 2011 Elsevier B.V. All rights reserved.

2011

Influence of hot rolling and high speed hydrostatic extrusion on the microstructure and mechanical properties of an ODS RAF steel

Nadine Baluc, Zbigniew Oksiuta

An argon gas atomized, pre-alloyed Fe-14Cr-2W-0.3Ti (wt.%) reduced activation ferritic (RAF) steel powder was mechanically alloyed with 0.3wt.% Y2O3 nano-particles in an attritor ball mill and consolidated by hot isostatic pressing at 1150 °C under a pressure of 200 MPa for 3 h. In the aim to improve its mechanical properties the ODS steel was then submitted to a thermo-mechanical treatment (TMT): hot rolling (HR) at 850 °C or high speed hydrostatic extrusion (HSHE) at 900 °C, followed by heat treatment (HT). Transmission electron microscopy (TEM) observations of the ODS alloys after TMT and heat treatment revealed the presence of elongated grains in the longitudinal direction, with an average width of 8 μm and an average length of 75 μm, and equiaxed grains, a few microns in diameter, in the transverse direction. Two populations of oxide particles were observed by TEM: large Ti-Al-O particles, up to 250 nm in diameter, usually located at the grain boundaries and small Y-Ti-O nanoclusters, about 2.5 nm in diameter, uniformly distributed in the matrix. Charpy impact tests revealed that the HSHE material exhibits a larger upper shelf energy (5.8 J) than the HR material (2.9 J). The ductile-to-brittle transition temperature of both alloys is relatively high, in the range of 55-72 °C. Tensile mechanical properties of both ODS alloys were found satisfactory over the full range of investigated temperatures (23-750 °C). The HSHE material exhibits better tensile strength and ductility than the HR material. These results indicate that HSHE can be considered as a promising TMT method for improving the mechanical properties of ODS RAF steels. © 2010 Elsevier B.V. All rights reserved.

Elsevier2011