A nanoscale mechanism of hydrogen embrittlement in metals
Graph Chatbot
Chat with Graph Search
Ask any question about EPFL courses, lectures, exercises, research, news, etc. or try the example questions below.
DISCLAIMER: The Graph Chatbot is not programmed to provide explicit or categorical answers to your questions. Rather, it transforms your questions into API requests that are distributed across the various IT services officially administered by EPFL. Its purpose is solely to collect and recommend relevant references to content that you can explore to help you answer your questions.
The observation of cracks in normally functioning reinforced concrete (RC) structures is expected as the tensile strength of concrete is relatively low. However, one or more of those cracks can start to propagate with increasing crack openings, localizing ...
Zirconium alloys used in the nuclear industry are exposed to extreme conditions undergoing high levels of irradiation damage and corrosion. Zircaloy-2 is used as nuclear fuel cladding in boiling water reactors and for the encapsulation of the spallation ta ...
While we fundamentally understand the dynamics of simple cracks propagating in brittle solids within perfect (homogeneous) materials, we do not understand how paths of moving cracks are determined. We experimentally study strongly perturbed cracks that pro ...
When two rough surfaces slide against each other, two main behaviors can be observed at the asperity level: A ductile behavior where the asperities tend to smooth out or a brittle behavior where the asperities detach and form debris. Recently, a critical l ...
The demand for metal alloys with superior structural performance in industrial applications continues to increase, as does the need for more-energy efficient materials and methods. Many materials that are otherwise attractive for structural applications ar ...
Atomistic simulations are a powerful complement to experimental probes for understanding the nanoscale processes associated with the effects of hydrogen (H) on plasticity and fracture that are the underlying causes of hydrogen embrittlement (HE). Current e ...
Pure magnesium (Mg) is an attractive metal for structural applications due to its low density, but also has low ductility and low fracture toughness. Dilute alloying of Mg with rare earth elements in small amounts improves the ductility, but the effects of ...
We study numerically the deformation of a dynamic crack propagating through a planar heterogeneous interface. We investigate the evolution of the front shape due to variations of fracture toughness, represented by weak and strong stripes parallel to the ru ...
Hydrogen embrittlement (HE) is a ubiquitous and catastrophic mode of fracture in metals. Here, embrittlement is considered as an intrinsic ductile-brittle transition at the crack tip, where H at the crack tip can reduce the stress intensity K-Ic for cleava ...
The structural integrity of the reactor pressure vessel (RPV) of light water reactors (LWR) is of utmost importance regarding operation safety and lifetime. High-temperature water (HTW) and hydrogen absorbed from environment, in synergy with irradiation em ...