A nanoscale mechanism of hydrogen embrittlement in metals
Graph Chatbot
Chat with Graph Search
Ask any question about EPFL courses, lectures, exercises, research, news, etc. or try the example questions below.
DISCLAIMER: The Graph Chatbot is not programmed to provide explicit or categorical answers to your questions. Rather, it transforms your questions into API requests that are distributed across the various IT services officially administered by EPFL. Its purpose is solely to collect and recommend relevant references to content that you can explore to help you answer your questions.
Limited reliability of ferroelectric-based actuators restricts their use in high-performance applications, where stress-induced cracking of ferroelectric ceramics often leads to fatal failure. The main limiting factors are the relatively small fracture tou ...
The edge strength of glass is affected by the load history. To quantify this effect, 12 series of glass specimens were subjected to either linearly increased (reference value), constant or cyclic loading. For constant loading the experimental values could ...
This paper discusses the development of drift-based and dual-parameter fragility curves for steel braces as part of concentrically braced frames designed in seismic regions. The experimental results from 24 different research programs are compiled into a d ...
Fracture tests have been performed on 333 flexure hinges of various shapes machined in monocrystalline silicon by Deep Reactive Ion Etching. The results show the significant effects of stress concentration, crystalline orientation and surface treatments on ...
Being good structural replacement for other conventional material, the pultruded glass fiber reinforced polymer (GFRP) profiles are being increasingly used in civil engineering structures. The connection between components is considered the most suspect ar ...
A series of fatigue experiments was performed in order to investigate the effect of the R-ratio on the fatigue/fracture behavior of adhesively-bonded pultruded GFRP double cantilever beam joints. Constant amplitude fatigue experiments were carried out unde ...
We introduce an augmented Becker-DeGroot-Marschak mechanism for the revelation of willingness-to-accept and willingness-to-pay in transaction cycles. The mechanism can be used to test for a behavioral anomaly. (C) 2011 Elsevier B.V. All rights reserved. ...
A framework for accurately modeling fatigue crack growth in ductile crystalline solids is necessarily multiscale The creation of new free surface occurs at the atomistic scale, where the material's cohesive strength is controlled by the local chemistry On ...
Hydrogen embrittlement is a pervasive mode of degradation in many metallic systems that can occur via several mechanisms. Here, the competition between dislocation emission and cleavage at a crack tip is evaluated in the presence of H. At this level, embri ...
The Mode I and II fracture behaviors of adhesively-bonded joints composed of pultruded glass fiber-reinforced polymer (GFRP) laminates were experimentally investigated using Double-Cantilever-Beam (DCB) and End-Loaded-Split (ELS) specimens. The large speci ...