Nanoscale Selective Passivation of Electrodes Contacting a 2D Semiconductor

Michael Graf, Martina Lihter, Aleksandra Radenovic
WILEY-V C H VERLAG GMBH, 2019
Journal paper

Abstract

2D semiconducting materials have become the central component of various nanoelectronic devices and sensors. For sensors operating in liquid, it is crucial to efficiently block the electron transfer that occurs between the electrodes contacting the 2D material and the interfering redox species. This reduces current leakages and preserves a good signal-to-noise ratio. Here, a simple electrochemical method is presented for passivating the electrodes contacting a monolayer of MoS2, a representative of transition metal dichalcogenide semiconductors. The method is based on blocking the electrode surface by a thin and compact layer of electronically nonconductive poly(phenylene oxide), PPO, formed by electrochemical polymerization of phenol. Since the phenol polymerization occurs in the potential window where MoS2 is electrochemically inactive, the PPO deposition is area-selective, limited to the electrode surface. The deposited PPO film is characterized by electrochemical, X-ray photoelectron spectroscopy, scanning electron microscopy, and atomic force microscopy techniques. The applicability of this method is demonstrated by coating the electrodes of a MoS2-based field-effect transistor coupled with a nanopore. The highly selective deposition, the simple approach, and the compatibility with MoS2 makes this method a good strategy for efficient insulation of micro- and nanoelectrodes contacting 2D semiconductor-based devices.

Official source

https://infoscience.epfl.ch/record/273422?ln=en

About this result

This page is automatically generated and may contain information that is not correct, complete, up-to-date, or relevant to your search query. The same applies to every other page on this website. Please make sure to verify the information with EPFL's official sources.

Related concepts

Related publications

Electrochemical and morphological engineering of 2D materials for nanopore sensing

Martina Lihter

Nanopores are nanometer-sized holes that were initially proposed for DNA sequencing. Several years ago sequencing was made possible with biological nanopores. However, solid-state nanopores have plenty of advantages to offer compared to their biological counterparts. This thesis focuses on nanopores made in 2D materials, and their sensing capabilities. They provide an outstanding spatial resolution and a good signal-to-noise ratio (SNR) for sensing. As a 2D semiconductor, molybdenum disulfide (MoS2) exhibits unique (opto)electronic and electrochemical properties. The electronic band structure of a semiconducting MoS2 results in highly sensitivity to its chemical environment and external electric field. Therefore, monitoring the transverse current through the MoS2 during analyte translocation can provide a powerful sensing mechanism. As an n-type semiconductor, MoS2 exhibits a characteristic electrochemical behavior: it shows electrochemical activity when polarized cathodically, while in the anodic region becomes electrochemically inactive. This thesis covers five topics in which I demonstrate how the properties of 2D materials can be used for designing advanced sensing platforms for biosensing. Fabrication of MoS2 Nanopores. Here, we give an overview of a reliable fabrication process optimized for the production of high-quality devices. We discuss the main issues, how to solve and avoid them. In the end, we demonstrate applications of MoS2 nanopores for sensing and for osmotic power generation. Geometrical Effect in 2D Nanopores. We compare two different pore geometries: triangular pores in hexagonal boron-nitride (h-BN) vs. approximately circular pores in MoS2. In h-BN nanopores, we observe a lower conductance drop caused by DNA translocation, than expected from a conventional conductance model. As an explanation, we propose a reduced ion-concentration and ion-mobility inside the pore, supported by molecular dynamics simulations. Transverse Detection of DNA in MoS2 Nanopore. This chapter presents the realization of a hybrid nanopore-FET device, consisting of an MoS2 ribbon and a nanopore drilled in it. Such a device acts as a field-effect transistor (FET), where the transverse current through the MoS2 is modulated by the translocating molecule and the ionic voltage applied across the pore. We show that the transverse current is more sensitive to DNA translocation than the ionic current. Passivation of Electrodes Contacting MoS2. The method is based on the electrochemical deposition of a polymer, which blocks the electron transfer from the surface of the electrodes to ions in solution. To avoid the deposition on MoS2, we used poly(phenylene oxide) (PPO) that polymerizes in the potential window where MoS2 is inactive. Deposition is compatible with MoS2 and highly area-selective, even at the nanoscale, as we demonstrate on the nanoelectrodes of a nanopore-FET device. Electrochemical Modification of MoS2. By polarizing MoS2 cathodically, it is possible to electrochemically deposit a thin layer of aryl-diazonium compounds on MoS2 surface. This approach allows to introduce specific chemical groups on MoS2 and nanopore rim, which could be used for specific recognition of analytes as they translocate through the pore. Furthermore, since the deposition occurs only on the MoS2 to which the voltage was applied, this could enable specific functionalization of adjacent nanoribbons in nanopore-FET devices.

EPFL2020

The subject of this work is the study of the electrochemical promotion of catalysis (EPOC), also called non-Faradaic electrochemical modification of catalytic activity (NEMCA). In this phenomenon, application of small currents or potentials on catalysts in contact with solid electrolytes leads to very pronounced strongly non-Faradaic and reversible changes in catalytic activity and selectivity. This work concerns the system composed of platinum film electrodes, deposited on the YSZ electrolyte (ZrO2 doped with 8% Y2O3), in contact with an oxygen containing atmosphere (the O2(g),Pt/YSZ system). The aim of this work was to focus on two points in the phenomenon of EPOC: 1) The nature of the species present on the surface of the catalyst and their impact on the catalytic activity. 2) The phenomenon of permanent promotion of catalysis (P-EPOC), for which the catalytic rate enhancement is not totally reversible, leading to a long lasting activated state. The Pt electrodes were prepared via three different methods (sputtering, thermal decomposition and screen-printing) and, as expected, the resulting microstructure, observed by scanning electron microscopy (SEM), was found to depend greatly on the preparation technique. The electrochemical response of each electrode was characterized by the technique of cyclic voltammetry. Due to the occurrence of different site-related electrochemical reactions, the voltammogram shape was highly influenced by the microstructure of the Pt/YSZ contact. Based on the preliminary studies, the cermet electrode was chosen for additional electrochemical experiments, using chronoamperometry, chronopotentiometry, cyclic voltammetry, steady state polarization and impedance spectroscopy. The results of all these techniques suggest that under anodic polarization, two parallel reactions take place. The first reaction is the oxygen evolution, giving rise to a steady state current under a constant applied potential. The other reaction is the oxygen storage (oxygen injection) in the form of Pt-O species. This second process gives rise to a time dependant current under a constant applied potential, and is therefore responsible for the pseudocapacitive behavior of the electrode. Moreover, linear sweep voltammetry measurements indicated that, by application of an anodic potential, at least three types of Pt-O species were stored, following distinct kinetics. Based on the amount of stored Pt-O and on the corresponding storage kinetics, they were attributed to three different locations on the electrode: 1) at the Pt/YSZ interface, 2) diffusing from the tpb toward the Pt/gas interface, 3) diffusing from the Pt/YSZ interface toward the bulk of the platinum electrode. It has been shown that the Pt film exhibited various activity states toward the catalytic oxidation of ethylene, depending on the oxygen species present at its surface. As evidenced by XPS measurements and in agreement with the thermodynamic data for the given system, the inactive (deactivated) state has been attributed to the formation of surface platinum oxide at T > 550°C. Decreasing the reaction temperature to 525°C caused the slow spontaneous reactivation of the catalyst and several days were necessary to reach the active state, where most of the catalyst was present in its metallic state. The catalyst activity recovery could be accelerated by the application of anodic potential pulses. In agreement with the mechanism of EPOC, this was explained by the oxide destabilizing effect of the anodically produced Oδ- species. Anodic polarization also caused reversible electrochemical promotion of catalysis at unusual high temperature (600°C). In addition, very intriguing catalytic relaxation transients were observed after prolonged anodic polarization times. Indeed, it was found that enhanced catalytic activity could be maintained for up to 10 hours after current interruption. Combination of these latter results, the related literature, the state of the art model of EPOC, and the results obtained by electrochemical techniques led to the proposition of an original model based on the processes of Pt-O storage/release at various locations of the O2(g),Pt/YSZ system. According to this model, anodic polarization produces Oδ- back-spillover species, promoting the catalytic activity, in agreement with the mechanism of EPOC. In parallel, hidden oxygen species are stored at the Pt/YSZ interface and diffuse toward the Pt phase. When the polarization is switched off, these hidden oxygen species diffuse to the gas-exposed surface and cause non-Faradaic promotion, as back-spillover Oδ- do. The large amount of stored charge and its slow diffusion controlled emergence causes the rate enhancement to last for hours.

EPFL2007

Ripples and Layers in Ultrathin MoS2 Membranes

Duncan Alexander, Jacopo Brivio, Andras Kis

Single-layer MoS2 is a newly emerging two-dimensional semiconductor with a potentially wide range of applications in the fields of nanoelectronics and energy harvesting. The fact that it can be exfoliated down to single-layer thickness, makes MoS2 interesting both for practical applications and for fundamental research, where the structure and crystalline order of ultrathin MoS2 will have a strong influence on electronic, mechanical and other properties. Here, we report on the transmission electron microscopy study of suspended single and few-layer MoS2 membranes with thicknesses previously determined using both optical identification and atomic force microscopy. Electron microscopy shows that monolayer MoS2 displays long-range crystalline order although surface roughening has been observed with ripples which can reach 1 nm in height, just as in the case of graphene, implying that similar mechanisms are responsible for the stability of both 2D materials. The observed ripples could also explain the degradation of mobility in MoS2 due to exfoliation. We also find that symmetry breaking due to the reduction of the number of layers results in distinctive features in electron-beam diffraction patterns of single and multilayer MoS2 which could be used as a method for identifying single layers using only electron microscopy. The isolation of suspended single-layer MoS2 membranes will improve our understanding of two-dimensional systems, their stability and the interplay between their structures, morphologies, electrical and mechanical properties.

2011

Electrochemical and morphological engineering of 2D materials for nanopore sensing

Martina Lihter

EPFL2020

EPFL2007