DISCLAIMER: The Graph Chatbot is not programmed to provide explicit or categorical answers to your questions. Rather, it transforms your questions into API requests that are distributed across the various IT services officially administered by EPFL. Its purpose is solely to collect and recommend relevant references to content that you can explore to help you answer your questions.
There is a need for chemically resistant coatings that protect the exposed surface of microfluidics components. Pinhole free films with low stress and a good uniformity on flat and inclined surfaces are required. In this study, amorphous silicon carbide (S ...
Light Induced Chemical Vapour Deposition (LICVD) of titanium dioxide thin films is studied in this work. It is shown that this technique enables to deposit locally and selectively a chosen crystalline phase with a precise controlled thickness at low substr ...
Electronic device-quality Cu was deposited on Pt-patterned oxidized Si wafers from hexafluoroacetylacetonate-copper(I)-trimethylvinylsilane by using low-pressure chem. vapor deposition at 150-250 Deg in He carrier gas. Smooth Cu films ?0.8 mm thick have be ...
Hydrogenated polymorphous silicon (pm-Si:H) is a new material obtained by plasma-enhanced chemical vapour deposition by running the plasma close to powder formation. Preliminary studies have revealed the presence of silicon nanocrystallites embedded in an ...
The anodic oxidn. of H2SO4 to H2S2O8 was investigated on B-doped synthetic diamond electrodes obtained by hot filament chem. vapor deposition. High current efficiency for H2S2O8 formation can be achieved in concd. H2SO4 (7.5 mol dm-3) and using high curren ...
The deposition of copper by low pressure chem. vapor deposition (CVD) from Cu bis-hexafluoroacetylacetonate is monitored in real time and in situ by the measurement of the optical reflectivity and elec. resistance of the growing metal film. Changes of the ...
A 351-363 nm wavelength argon laser is used to induce pyrolytic laser chem. vapor deposition of platinum, using platinum bishexafluoroacetylacetonate as a precursor. The deposit thicknesses and diams. are presented according to exposure time, precursor pre ...
The photolytic laser chem. vapor deposition (LCVD) rate of Pt from its hexafluoroacetylacetonate complex precursor was measured in situ and in real time. Optical transmission of the 350 nm photolysis light through the deposited Pt film and a transparent gl ...
The photothermal laser-induced chem. vapor deposition of Cu was studied as a function of the writing speed, the light intensity, and the diam. of the focal spot on the substrate, at three different pressures of the Cu bishexafluoroacetylacetonate precursor ...
The laser chem. vapor deposition of platinum from its bishexafluoroacetylacetonate deriv. is studied with a cw Ar ion laser at 458 and 514 nm. The height, the width, as well as the elec. cond. of the deposited stripes are reported as a function of the vapo ...