Publication

Transfer of Graphene under Ultra-High Vacuum

Darius Constantin Merk
2022
EPFL thesis
Abstract

This thesis reports on a novel method for graphene transfer that is fully UHV compatible, which has remained a challenge for a long time due to the necessity of supporting graphene for transfer and most often requiring supporting layer removal post-transfer. Our graphene transfer method is based on the wafer-bonding approach, where graphene is stamped onto a target surface, from a support to which it is weakly bound. We use a bilayer of graphene supported by a teflon tape for the low adhesion between graphene layers and the flexibility of teflon tape to allow adaptability to the target surface.We demonstrate successful transfer onto Cu(100) and Ir(111) single crystal surfaces as well as on gr/Ir(111), thus forming a (partial) graphene bilayer on Ir(111). For in-situ characterization, we use Auger electron spectroscopy and STM. Auger measurements confirm that we are able to transfer an average 0.8-0.9 ML of carbon, by comparison to CVD grown samples. After transfer onto Ir(111), we show that by annealing to 1000 °C, we are able to observe by STM the characteristic moiré pattern formed by CVD grown graphene on Ir(111). Auger spectra show that the graphene-Iridium interaction undergoes a change from physisorption to chemisorption upon annealing. XAS and Raman spectroscopy demonstrate that the annealing step taken post transfer to observe the moiré by STM is only necessary to induce a change in interaction strength but not to heal graphene defects, to increase its domain size, or to make it flat. After transfer onto Cu(100), Raman spectra show that the transferred graphene is of the same quality as the CVD grown graphene before transfer, without further annealing. Comparison of synchrotron based high resolution XAS spectra of transferred gr/Ir(111) to CVD grown samples confirms that the transferred graphene is flat on top of the Ir(111) crystal surface.This enables sample and device fabrication, usually hampered by impurities, to be carried out in UHV leading to fully reproducible results. Clean twisted bilayer graphene samples can be made and studied in UHV. Further, surface science can be extended to the third dimension, by capping layers and continuing growth, etc., all under clean conditions.

About this result
This page is automatically generated and may contain information that is not correct, complete, up-to-date, or relevant to your search query. The same applies to every other page on this website. Please make sure to verify the information with EPFL's official sources.
Related concepts (32)
Graphene
Graphene (ˈgræfiːn) is an allotrope of carbon consisting of a single layer of atoms arranged in a hexagonal lattice nanostructure. The name is derived from "graphite" and the suffix -ene, reflecting the fact that the graphite allotrope of carbon contains numerous double bonds. Each atom in a graphene sheet is connected to its three nearest neighbors by σ-bonds and a delocalised π-bond, which contributes to a valence band that extends over the whole sheet.
Potential applications of graphene
Potential graphene applications include lightweight, thin, and flexible electric/photonics circuits, solar cells, and various medical, chemical and industrial processes enhanced or enabled by the use of new graphene materials. In 2008, graphene produced by exfoliation was one of the most expensive materials on Earth, with a sample the area of a cross section of a human hair costing more than 1,000asofApril2008(about1,000 as of April 2008 (about 100,000,000/cm2). Since then, exfoliation procedures have been scaled up, and now companies sell graphene in large quantities.
Graphene nanoribbon
Graphene nanoribbons (GNRs, also called nano-graphene ribbons or nano-graphite ribbons) are strips of graphene with width less than 100 nm. Graphene ribbons were introduced as a theoretical model by Mitsutaka Fujita and coauthors to examine the edge and nanoscale size effect in graphene. Large quantities of width-controlled GNRs can be produced via graphite nanotomy, where applying a sharp diamond knife on graphite produces graphite nanoblocks, which can then be exfoliated to produce GNRs as shown by Vikas Berry.
Show more
Related MOOCs (5)
Micro and Nanofabrication (MEMS)
Learn the fundamentals of microfabrication and nanofabrication by using the most effective techniques in a cleanroom environment.
Microstructure Fabrication Technologies I
Learn the fundamentals of microfabrication and nanofabrication by using the most effective techniques in a cleanroom environment.
Micro and Nanofabrication (MEMS)
Learn the fundamentals of microfabrication and nanofabrication by using the most effective techniques in a cleanroom environment.
Show more

Graph Chatbot

Chat with Graph Search

Ask any question about EPFL courses, lectures, exercises, research, news, etc. or try the example questions below.

DISCLAIMER: The Graph Chatbot is not programmed to provide explicit or categorical answers to your questions. Rather, it transforms your questions into API requests that are distributed across the various IT services officially administered by EPFL. Its purpose is solely to collect and recommend relevant references to content that you can explore to help you answer your questions.