Interaction of polyelectrolytes with oppositely charged surfaces

Vesela Malinova
EPFL, 2005
EPFL thesis

Abstract

Despite progress during the last decade, the behavior of charged macromolecules, polyelectrolytes, including their interactions is not yet completely understood. In particular, interactions with oppositely charged surfaces, which play a significant role in many practical applications and are of central importance in life processes, need more investigation. This situation has motivated the selection of the topic of this doctoral thesis. The study is dedicated to interactions of positively charged polyelectrolytes with negatively charged surfaces considering two types of surfaces, flat amphiphile monolayers and porous surfaces of microspheres. The research aimed at quantitative evaluation of the influence of macromolecular dimensions, chemical structure, electrostatic parameters, and surface characteristics on the adsorption process. As a prerequisite, a series of poly(vinylbenzyltrialkylammonium chloride) model polyelectrolytes has been synthesized. The characteristics were five defined contour lengths with three different types of substituents at the quaternary ammonium group each in addition to uniform charge density and narrow chain length distribution. The final polyelectrolytes were the quaternization products of precursors synthesized by controlled radical polymerization. Two experimental techniques were employed to quantify the influence of chemical, macromolecular, and electrostatic parameters as well as geometrical characteristics on the adsorption of polyelectrolytes on porous microsphere surfaces. These were adsorption on microspheres suspended in aqueous phase and microspheres packed in a chromatography column. During the first technique the total surface comes immediately in contact with the polyelectrolyte molecules, whereas the second technique followed the rules of chromatography. For the first time, the contour length of the polyelectrolyte, the Debye length, the pore dimensions, as well as the chemical structure were likewise considered in a comprehensive study to describe the interaction of polyelectrolytes with well-characterized porous surfaces. A polyelectrolyte charge to surface charge ratio was defined and served to classify different adsorption behavior. Three models have been proposed to illustrate the adsorption behavior based on experimental findings and model calculations. The first one identifies the Debye length in addition to the contour length as dominating parameter, which decides whether a polyelectrolyte molecule can enter a pore or not. The second quantifies the influence of the contour length. Finally, the third describes the concentration influence on the type of molecule organization, layer formation, on the outer surface or inside of pores with diameters exceeding considerably the contour length. For amphiphile monolayer, for the first time, the influence of chain length and substituent at the quaternary ammonium group on the adsorption process was quantified. Based on the surface pressure, pressure-area and pressure-time isotherms measured, a model describing the monolayer arrangement on polyelectrolyte solutions was proposed. A second model correlates the increase of the area per amphiphile molecule and the decrease of the surface pressure with the size and hydrophobicity of the substituents. In addition chain length influence was evident. The results of the thesis contribute to progress in basic research in the field of polyelectrolytes, while also an impact on technical applications such as surface modification, chromatographic processes or improvement of materials is expected. Precise data for comparison with theoretical model calculations are provided, which were not available before.

Official source

https://infoscience.epfl.ch/record/33728?ln=en

About this result

This page is automatically generated and may contain information that is not correct, complete, up-to-date, or relevant to your search query. The same applies to every other page on this website. Please make sure to verify the information with EPFL's official sources.

Related concepts

Related publications

Vesela Malinova
EPFL, 2005
EPFL thesis

Abstract

Official source

https://infoscience.epfl.ch/record/33728?ln=en

About this result

Related concepts (27)

Related concepts

Related publications (12)

Related publications

The term polymer brush refers to a well defined arrangement of polymer chains, which are tethered with one end to an interface and usually the surface of a solid substrate. Due to steric repulsion the polymer chains furthermore adopt a defined, stretched chain conformation, which significantly differs from the random walk conformation of free polymer chains in solution or in conventionally solution casted polymer coatings. From a structural point of view polymer brushes can therefore be regarded as the most defined type of polymer coating that can currently be realized. Especially the combination of surface-initiated polymerizations (SIP) with modern, controlled polymerization methods thereby allows tailoring the structure of the polymer brushes almost on the molecular level. Specifically precise control over the thickness, composition, chain architecture, grafting density and via the use of lithographic techniques also over the topography of the brushes can be achieved. This high degree of control over the structural and implicated (physico-)chemical properties of the brush allows at the same time tailoring and fine tuning the interfacial properties of the brush. This thesis describes the systematic exploitation of well-defined polymer brushes as functional coatings with fine-tuned physicochemical properties to direct and control the interaction with and the response of specific biological, bioanalytical and even reactive chemical environments. In detail the use of surface-initiated atom transfer radical polymerization (SI-ATRP) for the fabrication of functional polymer brushes will be presented. These brushes were used as highly defined coatings in various applications ranging from biomedical and bioanalytical applications to biomimetic materials fabrication (Figure 1). Figure 1 Numerous synthetic approaches for the preparation of polymer brushes have been described in the literature. Chapter 2 will therefore present a summary of the most important types of surface-initiated polymerizations, focusing especially on controlled SIP methods and SI-ATRP. Chapter 3 describes a chemoselective and specific immobilization strategy to decorate intrinsically bioinert polymer brushes with proteins of interest in a defined orientation and density. Specifically the resulting substrates represent attractive candidates for the realization of protein microarrays. In view of this application protein-small molecule and protein-protein interactions as well as posttranslational modifications were analyzed within a feasibility study. Due to their well-defined structure polymer brushes represent also attractive candidates for the realization of molecularly defined cell adhesion substrates for tissue engineering or as highly defined biophysical model system to analyze cell adhesion and mechanics. Chapter 4 describes the decoration of intrinsically bioinert polymer brushes with small peptide ligands with defined density to induce integrin specific cell adhesion on the brushes. Peptide functionalized polymer brushes could be readily endothelialized and adhering cell layers have shown to preserve their homeostatic ability to respond to an applied mechanical stimulus in a physiological manner. In Chapter 5 the limitations of high density polymer brushes in biomedical applications were assessed by analyzing their stability under in vitro cell culture conditions. Intrinsically bioinert high density polymer brushes were found to degraft from glass or silicon substrates upon swelling in good solvents, which lead to deterioration of the bioinert properties of the substrate. The degrafting of the brushes might be connected to swelling induced mechanical activation of chemical bonds, which link the brushes to the substrate. Chapter 6 describes the transfer of the developed SIP approach onto flexible PDMS substrates by exploiting the formation of interpenetrating networks of ATRP-initiator siloxane and PDMS. The modification of the PDMS substrates with hydrophilic brushes effectively reduces the unspecific protein adsorption on the substrates. This approach might therefore represent an attractive and facile route for the surface modification of miniaturized PDMS devices for biomedical or bioanalytical applications. In Chapter 7 the systematic development of a reliable and robust protocol for the aqueous SI-ATRP of sodium methacrylate is presented, which gives access to poly(methacrylic acid) (PMAA) brushes with defined molecular weight and grafting density. The resulting brushes were assessed for their ability to direct the mineralization of calcium carbonate. Chapter 8 describes the use of photolithographically patterned poly(methacrylic acid) brushes as biomimetic, acidic macromolecular matrix to fabricate microstructured calcite thin films that are an exact 3D replica of the PMAA brush. The presented strategy relies on three key elements: (i) the use of photolithographic techniques to prepare microstructured PMAA brushes; (ii) the ability of PMAA brushes to stabilize amorphous calcium carbonate (ACC) and (iii) the possibility to convert the metastable ACC phase into a polycrystalline calcite film via a thermal treatment.

EPFL2007

Interactive Surfaces Based on Polymer Brushes

Dusko Paripovic

While the bulk structure of a material determines its mechanical properties, its surface plays a key role when interactions with the environment are important. Nowadays materials in bio- and nanotechnology are required to possess very complex functionalities and to interact specifically to the stimuli they receive from their surroundings. Thus, their surface modifications are becoming very demanding. In recent years surface initiated controlled radical polymerization techniques have emerged as very versatile strategies that provide a powerful toolbox to tackle the challenges that are set to material scientists. The attractiveness of these methods lies in the possibility to create well defined surface arrangements of polymer chains, which we refer to as polymer brushes, with precise control over thickness, composition and architecture. In addition, these techniques can be applied to very challenging substrates with respect to the chemical composition and geometry, which also includes porous materials. This Thesis, therefore, exploits the possibilities that surface-initiated controlled radical polymerization techniques offer to finely tune interfacial properties of materials and render them capable to interact with chemical and biological species in a desired way. Its paramount aim is to demonstrate how the functionalities and geometry of a polymer brush matrix can be employed to influence inorganic film deposition using synthetic, biomimetic and purely biological mechanism or enhance polymer brushed stability in aqueous media. This Thesis is divided into five distinct chapters, which will be briefly summarized in following paragraphs. Chapter 1 describes the preparation of polymer brushes and strategies that are used to control their chemical composition and architecture. Additionally, it will give an overview on the use of brushes as cell adhesive surfaces as well as templates for the production of nanoparticles and thin inorganic films. Chapter 2 explores a new strategy to guide the chemical solution deposition of thin, microstructured metal films. The proposed strategy is based on the use of poly(2-(methacryloyloxy)ethyl ammonium chloride) (PMETAC) brushes grown via surface-initiated atom transfer radical polymerization as a template. Thin films are prepared by first loading the PMETAC brushes with an appropriate precursor, followed by its reduction by NaBH4 and finally an oxygen plasma treatment to remove the stabilizing polymer brush matrix and generate the desired thin metallic film. Of particular interest is the question whether the thickness and lateral dimensions of the deposited metallic films can be controlled by micropatterning the polymer brush template and varying the brush thickness. In addition, this concept will be extended to the preparation of bimetallic (gold/palladium) films using a single polymer brush matrix. A similar strategy is explored in Chapter 3 to control the deposition of thin calcium carbonate films using a biomimetic process. The process is characterized by the stabilization of amorphous calcium carbonate, the geometry and localication of which can be controlled by the poly(methacrylic acid) brush template. A special focus of this Chapter is to examine the influence of the polymer brush thickness on the mineral deposition and to determine to which extent is the mineral phase is integrated into the polymer brush film. The aim of Chapter 4 is to develop a general approach for the modification of implantable materials with a polymer brush based coating that promotes bone formation. The proposed coatings are prepared via surface-initiated copolymerization of 2-hydoxyethyl methacrylate and 2-(methacryloyl)ethyl phosphate, which results in a thin hydrogel layer that mimics the negatively charged matrix macromolecules involved in natural bone formation. To further emulate the properties of the natural bone extracellular matrix, the coatings will be functionalized with the cell adhesive GGGRGDS peptide. The ability of the proposed coatings to induce bone formation is investigated in in vitro experiments on MC3T3-E1 pre-osteoblasts and evaluated using an ALP and alizarin red assays. Finally, Chapter 5 focuses on studying the parameters that could prevent the hydrolytic cleavage of Si-O bond, which tethers the polymer brushes grafted from SiOx in aqueous media. In the first part of the study, the length of the organosilane initiator's alkyl spacer will be varied, in order to evaluate to which extent it can insulate the site that anchors the hydrophilic polymer brush to the substrate. In the second part, a short, hydrophobic block will be introduced between the silicon oxide substrate and the hydrophilic polymer in order to more efficiently protect the underlying Si-O bond from the surrounding aqueous media and prevent the chain detachment.

EPFL2011

Effect of Surface Charge on Surface-Initiated Atom Transfer Radical Polymerization from Cellulose Nanocrystals in Aqueous Media

Harm-Anton Klok, Xingyu Xu, Justin Orazio Zoppe

Cellulose nanocrystals (CNCs) with different charge densities were utilized to examine the role of electrostatic interactions on surface-initiated atom transfer radical polymerization (SI-ATRP) in aqueous media. To this end, growth of hydrophilic uncharged poly(N,N-dimethylacrylamide) (PDMAM) brushes was monitored by electrophoresis, H-1 NMR spectroscopy, and dynamic light scattering (DLS). Molecular weight and polydispersity of PDMAM brushes was determined by GPC analysis of hydrolytically cleaved polymers. Initiator and polymer brush grafting densities, and thus, initiator efficiencies were derived from elemental analysis. Higher initiator efficiency of polymer brush growth was observed for CNCs with higher anionic surface sulfate half-ester group density, but at the expense of high polydispersity caused by inefficient deactivation. PDMAM grafts with number-average molecular weights up to 530 kDa and polydispersity indices

American Chemical Society2016

Interactive Surfaces Based on Polymer Brushes

Dusko Paripovic

EPFL2011

EPFL2007