Characterization of the effective electrostriction coefficients in ferroelectric thin films
Graph Chatbot
Chat with Graph Search
Ask any question about EPFL courses, lectures, exercises, research, news, etc. or try the example questions below.
DISCLAIMER: The Graph Chatbot is not programmed to provide explicit or categorical answers to your questions. Rather, it transforms your questions into API requests that are distributed across the various IT services officially administered by EPFL. Its purpose is solely to collect and recommend relevant references to content that you can explore to help you answer your questions.
Pb(Mg1/3Nb2/3)O-3 thin films were prepared from modified alkoxide solution precursors and their dielectric and electromechanical characteristics were investigated. Preparation of the films is very sensitive to processing parameters. The influence of differ ...
The present study aims at a better understanding of the high piezoelectric properties encountered in lead-based ferroelectrics by focusing on the extrinsic contributions to the response. The main characteristics of these materials are the highly nonlinear ...
Through the use of relations analogous to that of the Rayleigh law, it is demonstrated that the ac electric field dependence of the permittivity of ferroelectric thin films can be described. It is further shown that both reversible and irreversible compone ...
Pb(Zr,Ti)O-3 (PZT) and Pb(Zr,Ti,Nb)O-3 (PNZT) thin films were grown on platinized silicon substrates by r.f. magnetron sputtering followed by a post-annealing treatment. The Niobium, Nb, concentration varied from 1 to 7 at.% by increment of 1 at.%. The eff ...
In the present study, piezoelectric, conductivity and dielectric measurements have been performed on virgin and fatigued ferroelectric PZT thin films prepared by spin-on sol-gel deposition process on Si/SiO2/Ti/Pt substrates. By fatiguing, the polarisation ...
The effective piezoelectric coefficient e(31) has been measured on sol-gel processed Pb(ZrxTi1-x)O-3 thin films with Zr concentrations ranging from 45 to 60%. The largest value was observed at 45% Zr, although dielectric constant and effective d(33) peak a ...
The dielectric and piezoelectric response of ferroelectric thin films and ceramics was investigated as a function of the driving field amplitude. Detailed analysis of the amplitude and phase angle of the third harmonic of the dielectric displacement and pi ...
Transient photocurrents are investigated in ferroelectric lead zirconate titanate (PZT) films illuminated by laser pulses in the spectral range of 340-380 nm. At low electric fields, the photocurrent is sensitive to the ferroelectric polarization state and ...
Weak field piezoelectric coefficient and strain were investigated in ferroelectric SrBi2Ta2O9 (SET) thin films by means of optical interferometry. Though the maximum polarization and dielectric constant were small enough (7 mu C/cm(2) and 150, respectively ...
Interferometric measurements of electric field-induced displacements in piezoelectric thin films using single-beam and double-beam optical detection schemes are reported. It is shown that vibrational response measured with a single-beam interferometer incl ...