Pewter (ˈpjuːtər) is a malleable metal alloy consisting of tin (85–99%), antimony (approximately 5–10%), copper (2%), bismuth, and sometimes silver. Copper and antimony (and in antiquity lead) act as hardeners, but lead may be used in lower grades of pewter, imparting a bluish tint. Pewter has a low melting point, around , depending on the exact mixture of metals. The word pewter is probably a variation of the word spelter, a term for zinc alloys (originally a colloquial name for zinc). Pewter was first used around the beginning of the Bronze Age in the Near East. The earliest known piece of pewter was found in an Egyptian tomb, c. 1450 BC, but it is unlikely that this was the first use of the material. Pewter was used for decorative metal items and tableware in ancient times by the Egyptians and later the Romans, and came into extensive use in Europe from the Middle Ages until the various developments in pottery and glass-making during the 18th and 19th centuries. Pewter was the chief material for producing plates, cups, and bowls until the making of porcelain. Mass production of pottery, porcelain and glass products have almost universally replaced pewter in daily life, although pewter artifacts continue to be produced, mainly as decorative or specialty items. Pewter was also used around East Asia. Although some items still exist, Ancient Roman pewter is rare. Lidless mugs and lidded tankards may be the most familiar pewter artifacts from the late 17th and 18th centuries, although the metal was also used for many other items including porringers (shallow bowls), plates, dishes, basins, spoons, measures, flagons, communion cups, teapots, sugar bowls, beer steins (tankards), and cream jugs. In the early 19th century, changes in fashion caused a decline in the use of pewter flatware. At the same time, production increased of both cast and spun pewter tea sets, whale-oil lamps, candlesticks, and so on. Later in the century, pewter alloys were often used as a base metal for silver-plated objects.