Ultra-thin (10–500 nm) photo-polymerized γ-methacryloxypropyltriethoxysilane (MPMS) and vinyltrimethoxysilane (VTS) layers applied to SiO2 coatings on polyethylene terephthalate films improved the oxygen barrier performance of the oxide coated films by mor ...
Aminosilane solutions with pH equal to 8 and to 11 were applied and cured on SiO2 coated poly(ethylene terephthalate) (PET) films. The permeability of the silane-silica hybrid coating on PET was reduced twofold compared to that of the SiO2/PET film, at sol ...
The oxygen transmission rate of 48 nm thick SiO2 coatings on a poly(ethylene terephthalate) (PET) substrate was reduced by a factor of three after applying an 8 nm thick layer of oligomerized gammaaminopropyltriethoxysilane (γ-APS). Increasing the thicknes ...
The aim of this study is to develop coatings on polymer substrates with a combined increase in oxygen barrier performance and toughness, based on SiOx coatings modified with multifunctional organo-silane polymers of controlled polarity and reactivity. As a ...
The mechanical properties of ultrathin silicon oxide (SiOx ) coatings plasma-deposited on poly(ethylene terephthalate) (PET) films were investigated with particular attention paid to the effect of additives located in the superficial layers of the polymer ...
Thin silicon oxide (SiOx) barrier coatings formed by plasma enhanced chemical vapor deposition on poly(ethylene terephthalate) (PET) substrates were subjected to post-deposition annealing treatments in the temperature range for orientation relaxation of th ...