Atomistic modeling of fracture is intended to illuminate the complex response of atoms in the very high stressed region just ahead of a sharp crack. Accurate modeling of the atomic scale fracture is crucial for describing the intrinsic nature of a material ...
Dislocation emission from a crack tip is a necessary mechanism for crack tip blunting and toughening. A material is intrinsically ductile under Mode I loading when the critical stress intensity KIe for dislocation emission is lower than the critical s ...
The mounting bolt of helicopter main gearbox support strut was fractured into two pieces during the flight mission. The fracture occurred at the root of the first engaged thread of the bolt-nut assembly. Visual inspection of the fracture zone revealed crac ...
A material is intrinsically ductile under Mode I loading when the critical stress intensity K-Ie for dislocation emission is lower than the critical stress intensity K-Ic for cleavage. K-Ie is usually evaluated using the approximate Rice theory, which pred ...