Advanced materials characterization and modeling using synchrotron, neutron, TEM, and novel micro-mechanical techniques-A European effort to accelerate fusion materials development

For the realization of fusion as an energy source, the development of suitable materials is one of the most critical issues. The required material properties are in many aspects unique compared to the existing solutions, particularly the need for necessary resistance to irradiation with neutrons having energies up to 14 MeV. In addition to withstanding the effects of neutrons, the mechanical stability of structural materials has to be maintained up to high temperatures. Plasma-exposed materials must be compatible with the fusion plasma, both with regard to the generation of impurities injected into the plasma and resistance to erosion and hydrogen isotope retention. The development of materials fulfilling these and other criteria is a large-scale and long-term activity which involves basic materials science, materials development, characterization under both loading conditions and off-line, as well as testing under neutron flux-induced conditions. For the realization of a DEMO power plant, the materials solutions must be available in time. The European initiative FEMaS-CA-Fusion Energy Materials Science - Coordination Action - aims at accelerating materials development by integrating advanced materials characterization techniques, among them the efficient use of neutron and synchrotron-based techniques, into the fusion materials community. Further, high-end transmission electron microscopy and mechanical characterization (also on a microscopic level in order to facilitate tests of small material volumes, such as from neutron irradiation campaigns) are to be more extensively applied in fusion materials research. Finally, irradiation facilities for neutron damage benchmarking are contributing to the understanding of radiation effects. This overview demonstrates by means of a few examples the recent advancements in fusion materials research, e. g. by applying synchrotron X-ray and neutron tomography to novel materials and components. Deeper understanding of radiation effects is achieved by in situ TEM of materials under irradiation. Modeling of irradiation effects is closely linked to activities at irradiation facilities. Finally, new developments in mechanical testing on micro-and nano-scales are addressed. (C) 2013 Elsevier B.V. All rights reserved.

Contribution to the Production and Characterization of W-Y, W-Y2O3 and W-TiC Materials for Fusion Reactors

Lyubomira Veleva

This PhD Thesis work was aimed at investigating the potentiality of tungsten-base materials as structural materials for the future thermonuclear fusion reactors in attempting to develop reduced activation tungsten-base materials with high strength and sufficient ductility, especially in terms of fracture toughness and ductile-to-brittle transition temperature, on the basis of the following ideas: (1) nano-grained materials are expected to show an improved ductility with respect to normal grain-sized materials, and (2) nano-grained materials and materials reinforced with either oxide or carbide particles are expected to show improved strength and radiation resistance, as (i) the particles should act as obstacles for the propagation of mobile dislocations, (ii) the numerous grain boundaries and interfaces between the matrix and the particles should act as sinks for the irradiation-induced defects, and (iii) the particles should also help stabilizing the numerous grain boundaries upon thermal annealing and/or irradiation. A variety of W-base materials, namely W-(0.3-1.0-2.0)Y2O3, W-(0.3-1.0-2.0)Y and W-(0.3-0.9-1.7)TiC materials (in weight percent), have been successfully produced at the laboratory scale by powder metallurgy techniques including mechanical alloying followed by either cold pressing and sintering or hot isostatic pressing (HIPping). X-ray diffractometry and scanning and transmission electron microscopy observations combined with density and microhardness measurements as well as with tensile, Charpy impact, fracture toughness and non-standard three point bending tests allowed the identification of optimal chemical compositions and manufacturing conditions, among those investigated and on the basis of the experimental devices at disposal. Microscopic investigations showed that the materials produced at the laboratory scale are composed of small grains, with sizes between a few tens and a few hundreds nanometers, and contain a high density of small Y2O3 or TiC particles, with sizes between 1 and 50 nm. In the case of W-Y materials, all the Y transformed into Y2O3 during mechanical alloying, due to the high amount of O (around 1 wt.%) present in the milled powders, which is beneficial for reducing the excess O content in the materials. All materials also contain a residual porosity of a few percents, which is typical of materials compacted by HIPping. Macroscopic investigations showed that the HIPped materials exhibit high strength values and a promising resistance to irradiation but poor fracture properties up to a very high temperature of about 1100 °C, due mostly to air contamination of the mechanically alloyed powders and to residual porosity of the compacted materials. The materials produced entirely at the laboratory scale by mechanical alloying and HIPping are of better quality than a W-2Y material that was produced by mechanical alloying at the laboratory scale and compacted by sintering and forging at the Plansee company (Austria). Further studies should focus on reducing the O content in the mechanically alloyed powders and the residual porosity of the compacted materials. The grain size should be also optimized as well as the size distribution, number density and crystallographic features of the oxide and carbide particles.

EPFL2011

Analysis of nano-sized irradiation-induced defects in Fe-base materials by means of small angle neutron scattering and molecular dynamics simulations

Gang Yu

Thermonuclear fusion of light atoms is considered since decades as an unlimited, safe and reliable source of energy that could eventually replace classical sources based on fossile fuel or nuclear fuel. Fusion reactor technology and materials studies are important parts of the fusion energy development program. For the time being, the most promising materials for structural applications in the future fusion power reactors are the Reduced Activation Ferritic/Martensitic (RAFM) steels for which the greatest technology maturity has been achieved, i.e., qualified fabrication routes, welding technology and a general industrial experience are almost available. The most important issues concerning the future use of RAFM steels in fusion power reactors are derived from their irradiation by 14 MeV neutrons that are the product, together with 3.5 MeV helium ions, of the envisaged fusion reactions between deuterium and tritium nuclei. Indeed, exposure of metallic materials to intense fluxes of 14 MeV neutrons will result in the formation of severe displacement damage (about 20-30 dpa per year) and high amounts of helium, which are at the origin of significant changes in the physical and mechanical of materials, such as hardening and embrittlement effects, for instance. This PhD Thesis work was aimed at investigating how far the Small Angle Neutron Scattering (SANS) technique could be used for detecting and characterizing nano-sized irradiation-induced defects in RAFM steels. Indeed, the resolution limit of Transmission Electron Microscopy (TEM) is about 1 nm in weak beam TEM imaging, and it is usually thought that a large number of irradiation-induced effects have a size below 1 nm in RAFM steels and that these very small defects actually contribute to the irradiation-induced hardening and embrittlement of RAFM steels occurring at irradiation temperatures below about 400°C. The aim of this work was achieved by combing SANS experiments on unirradiated and irradiated specimens of RAFM steels with Molecular Dynamics (MD) simulations of main expected nano-sized defects in irradiated pure Fe and Fe-He alloys, as model materials for RAFM steels, and simulations of their corresponding TEM images and SANS signals. In particular, the SANS signal of various types of defects was simulated for the first time. The methodology used in this work was the following: SANS experiments were performed by applying a strong saturating magnetic field to unirradiated and irradiated specimens of three types of RAFM steels, namely the European EUROFER 97, the Japanese F82H and the Swiss OPTIMAX A steels. The available irradiated specimens included specimens which had been irradiated with 590 MeV protons in the Proton IRradiation EXperiment (PIREX) facility at the Paul Scherrer Institute (PSI) at temperatures in the range of 50-350°C to doses in the range of 0.3-2.0 dpa. SANS spectra as well as values of the so-called A ratio, which represents the ratio of the total scattered intensity to the nuclear scattered intensity, were obtained for the various irradiation doses and temperatures investigated. MD simulations of atomic displacement cascades in pure Fe and in Fe-He alloys were performed using Embedded Atom Method (EAM) many-body interatomic potentials. The main nano-sized defects that should be produced in RAFM steels under irradiation were created by means of MD in pure Fe. These included dislocation loops of various types, voids, helium bubbles with various He concentration and Cr precipitates. TEM images of cascade damage and all the defects created by MD were simulated in the dark field/weak beam imaging modes by using the Electron Microscopy Software (EMS) developed by P.A. Stadelmann (EPFL) and analyzed in terms of variations of contrast intensities versus depth inside the specimen. The SANS signal provided by cascade damage and all the defects created by MD was simulated by using a slightly modified version of EMS, accounting for neutrons instead of electrons. The SANS technique has been proven in this work to be a very powerful tool for detecting nano-sized irradiation-induced defects and a tool well complementary to TEM for characterizing such very small irradiation-induced defects. Indeed, TEM appears most adapted to investigate structural defects, such as dislocation loops and helium bubbles with high helium concentration, which yield significant lattice deformation of the surrounding matrix, while SANS is most adapted to investigate phase defects, such as voids, helium bubbles with low helium concentration and Cr precipitates. By combining the results of SANS experiments with those of MD simulations, TEM image simulations and SANS signal simulations, the nano-sized irradiation-induced defects were tentatively identified as small helium bubbles. While the radiation hardening measured for RAFM steels cannot be explained by accounting only for the defects observed in TEM, it could be successfully modeled by accounting also for a reasonable number density of the nano-sized defects evidenced using the SANS technique.

EPFL2008

Finite element modeling and experimental study of brittle fracture in tempered martensitic steels for thermonuclear fusion applications

Pablo Federico Mueller

In this work we have studied brittle fracture in high-chromium reduced activation tempered martensitic steels foreseen as structural materials for thermonuclear fusion reactors. Developing the adequate materials that can withstand the severe irradiation conditions of the burning plasma in a future fusion reactor is one of the major challenges to be solved in order to make profit from the great advantages of thermonuclear fusion as an energy source. High-chromium tempered martensitic steels such as F82H and the most advanced version Eurofer97 are among the main candidate materials for structural applications in future fusion power plants due to low irradiation-induced swelling, good mechanical and thermal properties, and reasonably fast radioactive decay. The most concerning drawback of these kind of steels is irradiation embrittlement, which is manifested by a ductile-to-brittle transition temperature shift to higher temperatures after irradiation whose amplitude depends on the irradiation conditions (temperature, neutron flux, neutron fluence, etc). The aim of this work was to study and model brittle fracture in the ductile-brittle transition region of this kind of steels in the as-received unirradiated conditions. It is necessary to be able to transfer laboratory specimen fracture data to real components and structures in order to assess the performance of these steels in the different operating and transient conditions they could find during the operation life of a fusion reactor. In order to do so, the specimen geometry effects and specimen size effects on measured fracture toughness need to be properly understood, taken into account and predicted with an appropriate model. In particular, specimen size effect on measured toughness is a major concern for the nuclear materials research community owing to the limited irradiation volume in current and planed materials irradiation facilities. The main results of this PhD work are summarized below. The microstructure of Eurofer97 and F82H has been characterized and compared by means of optical microscopy, scanning electron microscopy, transmission electron microscopy and energy-dispersive X-ray spectroscopy in order to identify microstructural features that could play a role in the measured fracture toughness. Both steels have similar but slightly different chemical composition and final heat-treatments but the prior austenitic grain size measured in F82H is approximately 8 times larger than in Eurofer97. It was shown that the alloying element Tantalum, added to stabilize the austenite grain size, played a different role in both steels. After a careful analysis of the particles present in both steels, it was found that Tantalum in Eurofer97 formed carbides of an average size around 100 nanometers. In contrast in F82H it did not form small carbides but formed big oxide inclusions with a size up to 30 µm. These large particles do not effectively pin the grain boundaries. The different behavior of Tantalum in these steels is believed to be mainly a consequence of the larger content of Oxygen present and the smaller amount of Aluminum in F82H compared to Eurofer97. The Master-Curve ASTM-E1921 standard is a method initially developed to determine the ductile-to-brittle transition reference temperature, T0, in fission reactor ferritic steels from a small number of experiments. In this work the applicability of the Master-Curve method to reduced activation tempered martensitic steels such as Eurofer97 and F82H was studied in detail. Fracture tests with pre-cracked sub-sized compact tension specimens (three different sizes, 0.18T, 0.35T and 0.87T of Eurofer97) were carried out in the temperature range [-196 °C, -40 °C]. The toughness-temperature behavior and scatter were shown to deviate from the ASTM-E1921 standard predictions near the lower shelf. Using the method of maximum likelihood, the athermal component of the Master-Curve was calculated to better fit our fracture toughness data from the lower to the middle transition region. We showed that these Master-Curve adjustments are necessary to make the T0 values obtained near the lower shelf with 0.35T size C(T) specimens consistent with those obtained in the middle transition region with 0.87T C(T) specimens. The ASTM-E1921 specimen size limitations, setting the maximum toughness measurable with a given specimen size, were found to be too lenient for this kind of steels. This problem was especially evident in fracture toughness data of Eurofer97 and F82H obtained in the upper transition temperature range with two different specimen sizes. Thus a more stringent specimen size requirement was proposed to avoid inconsistent transition temperature determinations. A promising local fracture model with the potential of predicting cleavage fracture toughness was studied. Finite element simulations were undertaken for compact specimens, notched specimens and tensile specimens of Eurofer97 steel tested from 20 °C down to -197 °C. Three and two dimensional as well as axisymmetric simulations were run in order to calculate the stress and strain fields at the onset of brittle fracture. For each tested temperature, the calculated load-displacement curves were found to reproduce very well those of the experiments. A local approach fracture criterion was studied. This criterion states that when the maximum principal stress is larger than a critical stress within a critical volume ahead of the crack tip, notch or neck, cleavage is triggered leading to macroscopic fracture of the specimen. It was shown that this model is able to predict the minimum fracture load of the notched specimens with the same values of critical stress and critical volume that were calibrated to predict the lower bound of fracture in compact specimens. This local approach model was also successfully used to predict the strong size effect observed experimentally in pre-cracked compact tension specimens in the upper transition region. The critical fracture stress determined in the standard tensile specimens was found higher than that of the fracture specimens. It was suggested that this difference stems from a significant difference in the stress state between the different specimens (triaxiality). Finally, the comparison between the overall fracture behavior in the transition between F82H and Eurofer97 steels indicated that these two materials are quite similar. A difference in the reference temperature T0 of about 20 °C was found, with a nominal value of -100 °C and -80 °C for F82H and Eurofer97 respectively. However, some excessive scatter in the toughness data was found in F82H with more data points than expected lying below the 1% tolerance bound; this was not observed in Eurofer97. From an engineering point of view, the entire fracture databases of these two steels are encompassed practically by the same lower tolerance bound.

EPFL2009