Effect of Steam-to-Carbon Ratio on Degradation of Ni-YSZ Anode Supported Cells

Résumé

Internal steam reforming (IR) of methane was investigated on Ni- YSZ anode supported cells, looking in particular at the effect of the steam to carbon (S/C) ratio on the degradation rate. The cells were fed with different H2O/CH4 mixtures during 100 hours sequences, alternating with sequences of dry H2 feeding. V-I characterization was performed before and after each sequence, and EIS measurements were performed regularly. A marked degradation was observed during the IR sequences while it was negligible under dry H2 feed. The observed degradation, attributed to carbon deposition on the anode active sites, was partially reversible for S/C >1.5, whereas it became irreversible at lower S/C.

À propos de ce résultat
Cette page est générée automatiquement et peut contenir des informations qui ne sont pas correctes, complètes, à jour ou pertinentes par rapport à votre recherche. Il en va de même pour toutes les autres pages de ce site. Veillez à vérifier les informations auprès des sources officielles de l'EPFL.

Graph Chatbot

Chattez avec Graph Search

Posez n’importe quelle question sur les cours, conférences, exercices, recherches, actualités, etc. de l’EPFL ou essayez les exemples de questions ci-dessous.

AVERTISSEMENT : Le chatbot Graph n'est pas programmé pour fournir des réponses explicites ou catégoriques à vos questions. Il transforme plutôt vos questions en demandes API qui sont distribuées aux différents services informatiques officiellement administrés par l'EPFL. Son but est uniquement de collecter et de recommander des références pertinentes à des contenus que vous pouvez explorer pour vous aider à répondre à vos questions.