Two-dimensional crack growth in FRP laminates and sandwich panels
Graph Chatbot
Chattez avec Graph Search
Posez n’importe quelle question sur les cours, conférences, exercices, recherches, actualités, etc. de l’EPFL ou essayez les exemples de questions ci-dessous.
AVERTISSEMENT : Le chatbot Graph n'est pas programmé pour fournir des réponses explicites ou catégoriques à vos questions. Il transforme plutôt vos questions en demandes API qui sont distribuées aux différents services informatiques officiellement administrés par l'EPFL. Son but est uniquement de collecter et de recommander des références pertinentes à des contenus que vous pouvez explorer pour vous aider à répondre à vos questions.
Prestressed composite patch bonded on cracked steel section is a promising technique to reinforce cracked details or to prevent fatigue cracking on steel structural elements. It introduces compressive stresses that produce a crack closure effect. Moreover, ...
The mechanical behavior of an aluminum alloy during uniaxial cyclic loading is examined using finite element simulations of aggregates with individually resolved crystals. The aggregates consist of face centered cubic (FCC) crystals with initial orientatio ...
Pre-stress bonded composite patch is a promising technique to reinforce steel member damaged by fatigue. ifhe effectiveness of this technique was verified by fatigue tests on notched steel plates. Results showed that the application of carbon fibre reinfor ...
The mode I inter-laminar fracture toughness of advanced knitted textile composites was investigated. Two complex weft-knitted glass fabrics were selected for the study: a triple rib knit and a Milano knit were impregnated with a tough epoxy resin and teste ...
The dimensional stability of V-shaped composite parts made from polyamide-12/carbon fibre (PA12/CF) commingled yarn has been studied. An anisotropic, thermoviscoelastic material model was implemented in a finite element solver to predict the internal stres ...
Low-cycle fatigue failure in titanium metal matrix composites is caused by two separate damage mechanisms: fatigue crack growth in the Ti matrix and fiber breakage. Here, a coupled numerical model for predicting both crack growth and fiber breakage is deve ...
Viscoelasticity and crack growth govern the long-term deformability of concrete and thus its service behaviour and its durability. For low load levels, viscoelasticity behaves quasilinearly and crack growth is inactive. On the other hand, for high load lev ...
The crack growth across a boundary between two colonies, i.e. regions of differing lamellar orientation, in two-phase lamellar Ti-Al is studied computationally to quantify the influence of such boundaries on toughening, as observed in recent in-situ fractu ...
The present work investigated the effects of physical aging on interfacial adhesion and internal stresses using single-fibre model composites. First, the stress state of the interface and its evolution upon aging were studied for the microbond geometry. Th ...
The influence of particle size and particle type on the fracture toughness of aluminium matrix composites is investigated using model composites of 99.99% purity aluminium reinforced with particles of alumina and boron carbide. These composites are produce ...