Peritectic equilibrium in Fe-Co alloys

Wilfried Kurz
2022
Article
Résumé

Recent results of directional solidification experiments with Fe-Co alloys were not consistent with the presently accepted peritectic phase diagram. Therefore, the Fe-rich part of this phase diagram was re-examined. High-temperature gradient plane front solidification was carried out at a low velocity. After quenching of the specimen from the peritectic temperature, the compositions of the phases close to the solid/liquid interface were determined through electron probe microanalysis. Using these results together with previously published phase diagram information, an improved phase diagram is proposed with the peritectic equilibrium at T-p = 1774 K, C-delta = 17.7, C-gamma = 18.1 and C-L = 19.5 at.% Co.

À propos de ce résultat
Cette page est générée automatiquement et peut contenir des informations qui ne sont pas correctes, complètes, à jour ou pertinentes par rapport à votre recherche. Il en va de même pour toutes les autres pages de ce site. Veillez à vérifier les informations auprès des sources officielles de l'EPFL.

Graph Chatbot

Chattez avec Graph Search

Posez n’importe quelle question sur les cours, conférences, exercices, recherches, actualités, etc. de l’EPFL ou essayez les exemples de questions ci-dessous.

AVERTISSEMENT : Le chatbot Graph n'est pas programmé pour fournir des réponses explicites ou catégoriques à vos questions. Il transforme plutôt vos questions en demandes API qui sont distribuées aux différents services informatiques officiellement administrés par l'EPFL. Son but est uniquement de collecter et de recommander des références pertinentes à des contenus que vous pouvez explorer pour vous aider à répondre à vos questions.