Publication
Full-area passivating contacts based on SiOx/poly-Si stacks are key for the new generation of industrial silicon solar cells substituting the passivated emitter and rear cell (PERC) technology. Demonstrating a potential efficiency increase of 1 to 2% compared to PERC, the utilization of n-type wafers with an n-type contact at the back and a p-type diffused boron emitter has become the industry standard in 2024. In this work, variations of this technology are explored, considering p-type passivating contacts on p-type Si wafers formed via a rapid thermal processing (RTP) step. These contacts could be useful in conjunction with n-type contacts for realizing solar cells with passivating contacts on both sides. Here, a particular focus is set on investigating the influence of the applied thermal treatment on the interfacial silicon oxide (SiOx) layer. Thin SiOx layers formed via UV-O3 exposure are compared with layers obtained through a plasma treatment with nitrous oxide (N2O). This process is performed in the same plasma enhanced chemical vapour deposition (PECVD) chamber used to grow the Si-based passivating layer, resulting in a streamlined process flow. For both oxide types, the influence of the RTP thermal budget on passivation quality and contact resistivity is investigated. Whereas the UV-O3 oxide shows a pronounced degradation when using high thermal budget annealing (T > 860 °C), the N2O-plasma