Identification of Passive Layer in Ferroelectric Thin-Films from Their Switching Parameters

Enrico Colla, Nava Setter, Alexander Tagantsev
1995
Article

Résumé

The switching of the sandwich structure ''ferroelectric+thin dielectric layer'' is theoretically studied. The behavior of the remanent polarization, P-r, coercive field, E(c), maximal polarization on the loop, P-s, and the slope of the hysteresis loop at E(c) as a function of both, the relative thickness of the layer (the thickness of the dielectric divided by the thickness of the ferroelectric) and the amplitude of the measuring field, is analyzed. It is shown that the effect of the layer on P-r and the slope at E(c) is qualitatively different from that on E(c) and P-s. As the result of this analysis the set of characteristic features of the sandwich with the variable relative thickness of the dielectric layer have been have formulated. These characteristic features can be used for the identification of the presence of such a dielectric layer using the data on the switching parameters of the system. It is shown that the increase of the coercive field with increasing relative thickness of the dielectric layer, which was considered as an important sign of the presence of the dielectric layer, is not a real property of the sandwich structure but rather an artifact of the approximations which were used in the analysis performed by the previous workers. In fact, E(c) is a decreasing function of the relative thickness of the dielectric layer. (C) 1995 American Institute of Physics.

Official source

https://infoscience.epfl.ch/record/88839?ln=fr

À propos de ce résultat

Cette page est générée automatiquement et peut contenir des informations qui ne sont pas correctes, complètes, à jour ou pertinentes par rapport à votre recherche. Il en va de même pour toutes les autres pages de ce site. Veillez à vérifier les informations auprès des sources officielles de l'EPFL.

Concepts associés

Chargement

Publications associées

Chargement

The integration of ferroelectrics in electronic devices requires that they be used in the form of thin films, which implies that for such systems finite-size effects related to the presence of a ferroelectric-electrode interface become important. In this thesis, a number of theoretical studies are presented on the properties of metal-ferroelectric-metal structures, focusing on the impact of the metal-ferroelectric interface on the polarization response of the system. First, a model for reverse domain nucleation in ferroelectrics is introduced, which takes into account the ferroelectric-electrode coupling in both the homogeneous and random cases. The model provides a solution to the coercivity paradox—i.e., the large discrepancy between the observed and predicted coercive fields. The possibility of non-thermally activated nucleation of reverse domains is demonstrated. It is found that small inhomogeneities in the ferroelectric-electrode interface may lead to an exponentially wide spectrum of waiting times for switching. The model predicts that switching is facilitated near morphotropic phase boundaries in perovskite-type ferroelectrics. In order to quantitatively analyze the size-effect problem in metal-ferroelectric-metal systems, an approach is developed which combines first-principles calculations and phenomenological theory. The parameters of the model can be extracted from calculations on ultrathin films, while experimentally verifiable predictions can be made on thick films. Using the developed approach, it is demonstrated how the size effect can be separated into two distinct contributions: a long-range electrostatic and a short-range "chemical" one. By considering symmetric SrRuO3/BaTiO3/SrRuO3 heterostructures with different types of termination (TiO2–TiO2 or RuO2–RuO2), it is shown that the balance between the long-range and the short-range contribution to the size effect can be essentially affected by the type of termination of the ferroelectric and by the polarization hardness of the electrode. The leading role of the long-range contribution to the size effect in SrRuO3/BaTiO3/SrRuO3 heterostructures is demonstrated. Application of the approach to the case of SrRuO3/BaTiO3/SrRuO3 heterostructures with asymmetric interfaces enables to provide a quantitative description of a number of manifestations of such asymmetry in films of technologically meaningful thickness. In particular, it is found that the asymmetry exerts a poling effect on the films, leading to a smearing of the phase transition, to an induced piezoelectric response above the transition temperature, and to the reversal of the polarization asymmetry by application of biaxial strain. Another important result of such calculations is the observation that the ionic relaxations in the metal-oxide electrode play a crucial role in stabilizing the ferroelectric phase of the films. Comparison with frozen-phonon calculations shows that the degree of softness of the SrRuO3 lattice has an essential impact on the screening of ferroelectric polarization, reducing the critical thickness for ferroelectricity of the system. These results provide a possible explanation for the observed beneficial impact of oxide electrodes on the switching and dielectric properties of ferroelectric capacitors.

EPFL2008

Chargement

, , ,

Lead zirconate titanate (PZT) thin films on insulator-buffered silicon substrates with interdigitated electrodes (IDEs) have the potential to harvest more energy than parallel plate electrode (PPE) structures because the former exploit the longitudinal piezoelectric effect, which is about twice as high as the transverse piezoelectric effect used by PPE structures. In this work, both options are compared with respect to dielectric, ferroelectric, and piezoelectric properties, leakage currents, and figure of merit (FOM) for energy harvesting. The test samples were silicon beams with {100} PZT thin films in the case of the PPE geometry, and random PZT thin films for the IDE geometry. Both films were obtained by an identical sol-gel route. Almost the same dielectric constants were derived when the conformal mapping method was applied for the IDE capacitor to correct for the IDE geometry. The dielectric loss was smaller in the IDE case. The ferroelectric loops showed a higher saturation polarization, a higher coercive field, and less back-switching for the IDE case. The leakage current density of the IDE structure was measured to be about 4 orders of magnitude lower than that of the PPE structure. The best FOM of the IDE structures was 20% superior to that of the PPE structures while also having a voltage response that was ten times higher (12.9 mV/mu strain).

Ieee-Inst Electrical Electronics Engineers Inc2013

Chargement

Domain nucleation behavior in ferroelectric films with thin and ultrathin top electrodes versus insulating top layers

Ludwig Feigl, Nava Setter

The effect of varying the thickness of Pt top electrodes made by the electron beam induced deposition technique on the domain nucleation characteristics of Pb(Zr,Ti)O-3 films has been investigated by piezoresponse force microscopy. The advantage of this experimental setup is that the nucleation position can be precisely controlled allowing comparison between two capacitor structures with different top electrode thicknesses and negating the role of defect-induced polarization switching scenarios. In the ultrathin limit (< 5 nm), the coercive biases of polarization switching change substantially relative to thicker electrodes, from - 4.6 to -2.6 V and from + 3.5 to 5.5 V respectively, which we link to a work function size effect. The evolution of the piezoresponse and coercive biases as a function of hysteresis loop cycling is presented and contrasted with that obtained on the bare film surface with no top electrode. To provide a counterpoint to the observed effects with top electrodes, we have demonstrated the variation in switching due to a top silicon oxide insulating layer. This work has revealed a method which could be used to control nucleation bias in ferroelectric thin film systems. (C) 2017 Published by Elsevier B.V.

Elsevier Science Sa2017