The effect of magnesium addition on the phase formation, microstructure and electric and ferroelectric properties of LiNbO3 thin films prepared through polymeric precursors was analyzed. By X ray diffraction no secondary phase was observed with the increase of magnesium concentration. Comparing to pure LiNbO3, the addition of 0.5 and 1.0 mol% of Mg+2 increased of the dielectric constant, while 2.0 mol% decreased it. It was noticed that the increase in additive concentration decreases the ferroelectric remanent polarization and increases the coercive field.