A Ga2O3 underlayer as an isomorphic template for ultrathin hematite films toward efficient photoelectrochemical water splitting

Hematite photoanodes for photoelectrochemical (PEC) water splitting are often fabricated as extremely-thin films to minimize charge recombination because of the short diffusion lengths of photoexcited carriers. However, poor crystallinity caused by structural interaction with a substrate negates the potential of ultrathin hematite photoanodes. This study demonstrates that ultrathin Ga2O3 underlayers, which were deposited on conducting substrates prior to hematite layers by atomic layer deposition, served as an isomorphic (corundum-type) structural template for ultrathin hematite and improved the photocurrent onset of PEC water splitting by 0.2 V. The benefit from Ga2O3 underlayers was most pronounced when the thickness of the underlayer was approximately 2 nm. Thinner underlayers did not work effectively as a template presumably because of insufficient crystallinity of the underlayer, while thicker ones diminished the PEC performance of hematite because the underlayer prevented electron injection from hematite to a conductive substrate due to the large conduction band offset. The enhancement of PEC performance by a Ga2O3 underlayer was more significant for thinner hematite layers owing to greater margins for improving the crystallinity of ultrathin hematite. It was confirmed that a Ga2O3 underlayer was applicable to a rough conducting substrate loaded with Sb-doped SnO2 nanoparticles, improving the photocurrent by a factor of 1.4. Accordingly, a Ga2O3 underlayer could push forward the development of host-guest-type nanocomposites consisting of highly-rough substrates and extremely-thin hematite absorbers.

On the Morphology and Interfaces of Nanostructured Hematite Photoanodes for Solar-Driven Water Splitting

Florian Le Formal

A sustainable route to store the energy provided by the Sun, is to directly convert sunlight into molecular hydrogen using a semiconductor performing water photolysis. Hematite (α-Fe2O3) is promising for this application due to its ample abundance, chemical stability and significant light absorption (with a band gap of 2.0 - 2.2 eV). Despite these advantageous properties, several drawbacks restrain the utilization of iron oxide for photoelectrochemical water splitting. The first limitation, namely the conduction band edge lower than the water reduction potential, can be straightforwardly overcome by adding a second solar system in tandem, which can absorb a complementary part of the solar spectrum and bring the electron at an energetic level higher than the hydrogen evolution potential. The second drawback arises from the disaccord between the short charge carrier diffusion length and the large light penetration depth. It is therefore necessary to control the hematite morphology on a length scale similar to the hole transport length. To further enhance the photoelectrochemical performance, a new concept for water splitting is introduced in this thesis. The host-guest approach consists in decoupling the different tasks of the photoanode (on one side light harvesting and water oxidation center, on the other side electron conduction to the substrate) by depositing a thin layer of hematite onto a mesoporous host (WO3 in this study). This concept has been demonstrated to increase the photocurrent by ca. 20% due to enhanced quantum efficiencies at long wavelengths. This demonstration has been nonetheless limited by the iron oxide thin films overall efficiency. Thin films photoactivity is then investigated by two means: first by controlling their nucleation on a modified substrate and secondly by incorporating plasmonic nanoparticles aimed to localize absorption in the thin film. The formation of a SiOx buffer layer on the substrate prior to deposition of hematite by Fe(acac)3 spray is shown to modify the film formation mode and its physical properties. These films exhibit photoactivity from an optical thickness of 12.5 nm (as compared to 25 nm without underlayer). The study of hematite photoanodes with gold nanoparticles, embedded or deposited on its surface, establish that charge transfer from metal nanoparticles is occurring only at overlapping wavelengths between the plasmonic resonance and the semiconductor absorption. Nevertheless, photoelectrochemical performances are reduced because of high recombination rate at the metal/semiconductor interface. Finally the third limitation, i.e. the large overpotential required to observe the onset of water splitting photocurrent, is tackled in the last part. The onset potential of photocurrent is decreased by a very thin coating of Al2O3 (0.1 - 2 nm), deposited by ALD, on the nanostructured photoanode. The subsequent application of the Co2+ catalyst further reduces the overpotential and results in a record photocurrent at 0.9 VRHE of over 0.4 mA cm-2. This investigation clearly distinguishes two causes for this energy loss: surface traps and slow oxidation kinetics. The charge accumulation and the Fermi level pinning, observed at low bias potential and assigned to these surface states were further rationalized in an investigation on photocurrent and photovoltage transients.

EPFL2011

Passivating surface states on water splitting hematite photoanodes with alumina overlayers

Maurin Cornuz, Michael Graetzel, Florian Le Formal, Thomas Moehl, Kevin Sivula, Nicolas Tétreault

Hematite is a promising material for inexpensive solar energy conversion via water splitting but has been limited by the large overpotential (0.5-0.6 V) that must be applied to afford high water oxidation photocurrent. This has conventionally been addressed by coating it with a catalyst to increase the kinetics of the oxygen evolution reaction. However, surface recombination at trapping states is also thought to be an important factor for the overpotential, and herein we investigate a strategy to passivate trapping states using conformal overlayers applied by atomic layer deposition. While TiO2 overlayers show no beneficial effect, we find that an ultra-thin coating of Al2O3 reduces the overpotential required with state-of-the-art nano-structured photo-anodes by as much as 100 mV and increases the photocurrent by a factor of 3.5 (from 0.24 mA cm(-2) to 0.85 mA cm(-2)) at + 1.0 V vs. the reversible hydrogen electrode (RHE) under standard illumination conditions. The subsequent addition of Co2+ ions as a catalyst further decreases the overpotential and leads to a record photocurrent density at 0.9 V vs. RHE (0.42 mA cm(-2)). A detailed investigation into the effect of the Al2O3 overlayer by electrochemical impedance and photoluminescence spectroscopy reveals a significant change in the surface capacitance and radiative recombination, respectively, which distinguishes the observed overpotential reduction from a catalytic effect and confirms the passivation of surface states. Importantly, this work clearly demonstrates that two distinct loss processes are occurring on the surface of high-performance hematite and suggests a viable route to individually address them.

2011

Cathodic shift in onset potential of solar oxygen evolution on hematite by 13-group oxide overlayers

Jérémie Minh-Châu Brillet, Maurin Cornuz, Michael Graetzel, Takashi Hisatomi, Florian Le Formal, Kevin Sivula, Nicolas Tétreault

The onset potential of photoelectrochemical water oxidation on ultrathin hematite was improved by up to 200 mV by the chemical bath deposition of 13-group oxides as overlayers. It is proposed that the corundum-type overlayers released lattice strain of the ultrathin hematite layer and decreased the density of surface states. Particularly, a Ga2O3 overlayer exhibited an enhanced photocurrent attributed to stoichiometric water splitting near the onset potential. The photocurrent was sustained over a day, attesting to its outstanding performance and durability for water splitting.

2011

On the Morphology and Interfaces of Nanostructured Hematite Photoanodes for Solar-Driven Water Splitting

Florian Le Formal

EPFL2011