Development of Adsorbents for Selective Volatile Organic Compounds Removal from Diluted Gas Streams

Contamination of the environment by anthropogenic volatile organic compounds (VOC) became of major concern during the last decades. Present in gas streams of many industrial exhausts, they are harmful and detrimental for both human health and environment even at low concentration. Several techniques have been developed and applied for VOC abatement, e.g.: absorption, condensation, bio-filtration, photo-, thermal or catalytic oxidation. Although good performances were reported, they suffer from different drawbacks such as low efficiency at diluted concentration, difficult handling or low throughput. In this sense adsorption appears to be the most efficient method for complete removal of VOC from diluted streams. Various adsorbents were developed for VOC abatement such as activated carbon (AC), zeolites, silica or polymers. Although their efficiencies for certain VOC was shown, their abatement capacities can be reduced due to the lack of specific interactions. The approach taken in this thesis is based on the development of specific adsorbents towards VOC. The surface of commercial adsorbents is functionalized depending on the VOC physical properties aiming to create specific interactions. Activated carbon is a widely used adsorbent and received great attention for VOC removal due to their low cost and versatility. Because of their well-developed microporosity AC show large abatement capacity for non-polar VOC such as benzene or toluene even at low concentration. Generally used in the form of granules, powder or pellets, AC can present mass transfer limitations and flow mal-distribution (preferential gas passage or bypass through the adsorbent bed). To circumvent these drawbacks, activated carbon fibers (ACFs) consisting of arranged microfilaments are used in this work. First, the adsorption of toluene, as a model of non-polar high boiling point VOC, was studied over ACFs. The influence of the ACFs microporosity on the toluene adsorption capacity was addressed using two samples with different microporosity but similar surface chemistry. The influence of the pore size on the enthalpy of adsorption was evaluated through the modelling of adsorption isotherms measured experimentally. The adsorption enthalpy was also evaluated using simulation of toluene temperature-programmed desorption (TPD). The values obtained were then compared. Besides morphology, surface chemistry is known to influence the VOC adsorption capacity of ACFs. The influence of the surface oxygen content on the toluene and the acetaldehyde removal capacity was then evaluated. The increased concentration of O-containing groups affects toluene adsorption whereas it promotes the acetaldehyde removal. Specific functionalization of the ACFs surface was performed for the removal of polar VOC represented by formaldehyde and acetaldehyde. Taking advantage of their large specific surface area, ACFs were functionalized by diethylene triamine (DETA) via liquid layer deposition. ACFs with different DETA loading were synthesized and their adsorption capacity towards formaldehyde was evaluated. The influence of DETA loading on the adsorption capacity was measured and an adsorption mechanism was suggested. The deposition of nano-particles (NPs) of basic metal oxide on the ACFs surface was used for increased acetaldehyde abatement. By combining the high intrinsic adsorption capacities of metal oxide NPs and the large specific surface area of ACFs, an effective acetaldehyde adsorbent was

Novel structured adsorber and oxidation catalysts for the removal of VOCs in low concentration

Kim Martin Nikolajsen

One possibility for the removal of volatile organic compounds (VOCs) is catalytic oxidation. For the removal of VOCs in low concentration (≲ 3000 ppmv for propane) it is not possible to sustain the required oxidation temperature over the catalyst without external heating. An approach to overcome this problem is to concentrate the VOC by adsorption, in a "two-step adsorption-incineration" process. This is an unsteady state process in which the VOC laden effluent gas is cleaned by passing it through an adsorber. Once the adsorber is saturated the VOC is desorbed by heating and purging. The concentrated VOC from the desorber can then be oxidized over the catalyst, producing enough heat to sustain the oxidation temperature. Conventional adsorbents have some drawbacks such as tailing during desorption due to the large particle size, high pressure drop and hot-spot formation. The objective of this work was to develop, characterize and test the adsorbent and catalyst, with low resistance to mass transfer resulting from thin films of active material, for the two-step adsorption-incineration process. Both the adsorbent and the oxidation catalysts were supported on sintered metal fibers (SMF). This is a novel, structured support offering several advantages over conventional randomly packed beds: Low pressure drop, due to the high porosity of the SMF, which is important where large flow rates and/or high quantities of gas must be treated. High thermal conductivity, due to the metallic nature, leading to smaller temperature gradients in the fixed-bed. A very high geometric surface area, due to the small fiber size. On the order of 200,000 m2/m3 with a fiber diameter of 20 µm. Furthermore, a mathematical model was developed to show the feasibility of the coupling of the two steps in the process. The adsorber was made from a thin, homogeneous film of MFI-type zeolite covering the fibers of the SMF. The film was grown by the seed-film method by hydrothermal treatment. A 3 µm film was obtained with 10 wt.% zeolite on the fiber after 24 h synthesis at 125 °C. This material had a specific surface area of 30 m2/g. The adsorption equilibrium of propane was described well by the Langmuir isotherm and the heat of adsorption was found to be ΔH0ads = - 43.1 kJ/mol. Isothermal breakthrough curves were measured as a function of temperature and film thickness. A mathematical model, comprised of a tanks-in-series model with a linear driving force (LDF) mass transfer description, successfully described the breakthrough behavior. The overall mass transfer was found to be solely due to diffusion in the zeolite film. However, the thin films show very low resistance to mass transfer leading to low internal concentration gradients and efficient utilization of the adsorbent. The pressure drop was measured and compared to that of a randomly packed fixed-bed of spheres. The equivalent diameter for a constant volumetric flow rate and superficial cross sectional area was dp = 180 µm, for a fiber diameter of df = 26 µm at 10 wt.% zeolite loading. The oxidation catalysts were all supported on SMF and cobalt oxide was used as the active phase. Three different groups of catalysts were developed. The support was modified by coating the fibers either with a thin film of fine powder (alumina or catalyst powder) or with a MFI-type zeolite film identical to the adsorbent. The third group was made from cobalt oxide impregnated directly on the oxidized fibers. The latter type of catalyst was found to be the most active during the screening experiments. The base support composition was varied (stainless steel (SS), FeCrAlloy and inconel) to investigate the support effect on the kinetics. The stainless steel and FeCrAlloy supports had similar activities, surpassing that of the inconel supported catalyst, which might be attributed to a Co3O4 surface enriched with iron from the support. Between the 1.1 wt.%Co3O4/SMFSS and 1.5 wt.%Co3O4/SMFFeCrAlloy catalyst the FeCrAlloy based had the highest normalized activity at low temperature (< 310 °C), low propane mole fraction (0.13 %) and high oxygen mole fraction (16.7 %). The chemical kinetics were determined from a novel and efficient experimental design. The apparent activation energy for this catalyst was found to be 87.5 ± 2.6 kJ/mol, with reaction orders in propane of 0.38 ± 0.04 and in oxygen of 0.30 ± 0.08. The catalysts were tested up to 350 °C. Mass transfer limitations were absent and the kinetics was described well with the power rate law as compared to the Mars-van Krevelen model. Catalysts based on Co3O4, supported directly on oxidized SMF, are very active catalysts, simple to prepare, withstand deactivation due to hot-spot formation and show great potential in comparison to the industrial reference catalyst (copper and manganese oxide supported on alumina). The adiabatic desorption process was investigated by mathematical modeling. Simply purging the adsorption bed with the hot exhaust gas from the reactor cannot result in the concentration of the VOC due to the high heat capacity of the fixed-bed. Hence, it will be necessary to use either a high heat carrier like steam, with the adverse effects of drying and separation of water and VOC, or an approach in which the desorber is heated prior to purging the bed, changing the adsorption equilibrium in favor of high gas concentrations. For the latter method, the minimum theoretical propane mole fraction for an autothermal process was found to be 350 ppmv to sustain a catalytic incinerator at 250 °C. Finally, it can be concluded that for the first time zeolite films on SMF were used as structured adsorbents, leading to very low internal mass transfer and increased process efficiency. Furthermore, the advantages of the SMF can be exploited in a catalytic oxidizer, which can be combined with the adsorber to annihilate VOCs in low concentrations. A novel method for the deposition of fine powder catalyst on SMF was also developed for the first time.

EPFL2007

Activated carbon fibers for efficient VOC removal from diluted streams: the role of surface functionalities

Guillaume Bastien Baur, Oliver Anthony Beswick, Lioubov Kiwi, Jonathan Spring

The effect of surface functionalities, specific surface area and pore size of activated carbon fibers (ACFs) on the adsorption of toluene and acetaldehyde, two volatile organic compounds (VOC), at low concentrations (similar to 80 ppmv) and short contact time (20 ms) has been studied. Two different types of ACFs characterized by low temperature N-2 adsorption: ultramicroporous (d (pore) < 1 nm) and supermicroporous (d (pore) similar to 1-2 nm) were tested. Both ACFs were effective for the removal of toluene attaining the adsorption capacity as large as 51 wt%. The surface chemistry of ACFs (O-containing functional groups) was characterized by temperature-programmed desorption monitoring the CO/CO2 evolved. Oxidative treatment of ACFs by nitric acid increased the surface concentration of O-groups. This resulted in lower adsorption capacity towards toluene but higher one towards acetaldehyde. This result was rationalized based on different type of VOC interactions with the carbon surface.

Springer2015

Novel catalytic applications of carbon nanofibers on sintered metal fibers filters as structured supports

Marina Ruta

Supported metal catalysts are important from both an industrial and a scientific point of view. They are used, amongst others, in large-scale processes such as catalytic reforming, hydrotreating, polymerization reactions and hydrogenations. Often, these catalysts consist of nanosized metal particles deposited on a suitable support, which acts as an anchor for the active phase and, in several cases, contributes to improve the overall catalyst performances. The growth of carbon nanofibers on sintered metal fibers filters (CNF/SMF) by hydrocarbons catalytic decomposition results in a structured composite material presenting all the suitable characteristics for its application as catalyst support. The main objective of this thesis was to develop novel catalytic systems based on CNF/SMF as catalytic support for continuous gas-phase hydrogenations. At first, the synthesis of CNF/SMF was optimized to tailor the properties of the material for further applications as catalytic support. The use of ethylene as carbon precursor and high synthesis temperature (973K) provided high yields of well-ordered CNF with increased specific surface area (SSA), up to 516 m2/g. On the other hand, the synthesis of CNF by ethane decomposition, which is less reactive than ethylene, resulted in a support with higher permeability, minimizing the pressure drop and being more suitable in a continuous-flow reactor. After the synthesis, the CNF surface was activated by treatment with O3 or H2O2. A novel technique, which consist of XPS analysis after step-wise TPD in UHV conditions, was developed and applied for the surface characterization. It allowed to assess the nature of the functional groups created on the CNF surface. The O3-activation was found the most effective for increasing the acidity of the CNF/SMF surface, yielding a relatively high amount of carboxylic functional groups. These groups are important because involved in the chemical anchoring and stabilization of the active metal deposited on the support. Industrially, many hydrogenations are performed over supported metal catalyst. The majority of these reactions are known to be structure sensitive reactions, so the control of the metal particle size is crucial in order to study the catalyst activity and selectivity. We prepared monodisperse-sized Pd nanoparticles (8, 11 and 13 nm) via the reverse microemulsion method and deposited on CNF/SMF and activated-CNF/SMF for a two-fold study: the effect of the nanoparticles size and the effect of the support nature on the selective hydrogenation of acetylene. The antipathetic size dependence of the TOF disappeared at particle size bigger than 11 nm. The initial selectivity to ethylene (∼60%) was found size-independent. The structure-sensitivity relations have been discussed in terms of "geometric" and "electronic" nature of the size-effect and rationalized assuming a Pd-Cx phase formation which is known to be size-dependent. CNF/SMF supports with increased acidity diminished the formation of coke and changed the by-products distribution, diminishing the catalyst deactivation. Subsequently, CNF/SMF was applied to develop a new catalytic system: the Structured Supported Ionic Liquid Phase (SSILP) catalyst, embedding an active Rh complex. The selective gas-phase hydrogenation of 1,3-cyclohexadiene to cyclohexene was used as model reaction. The SSILP based on CNF/SMF supports showed a high turnover frequency, up to 250 h-1 and selectivity > 96%. Multiple advantages of supporting a homogeneous active phase, dissolved in IL, on CNF/SMF have been demonstrated: the thin layer of IL was homogeneously distributed over the mesoporous support, so mass transfer limitations could be avoided, furthermore the chemical inertness of the CNF prevented any interaction between the active phase dissolved in IL ensuring an efficient use of the Rh complex. The SSILP concept can be applied not only for the "heterogenization" of a transition metal catalyst, but also to obtain metal nanoparticles with monodispersed size via the reduction of a metal precursor dissolved in IL. In this case, IL provides a suitable environment for the nucleation and growth of the nanoparticles. By applying the SSILP concept to the selective hydrogenation of acetylene, the influence of IL on the stability of the nanoparticles was investigated. Moreover, the different solubilities of reactants and products in the IL phase allowed to improve the selectivity toward ethylene. Monodispersed Pd nanoparticles of 5 and 10 nm in SILP on CNF/SMF showed excellent long-term stability. The lower solubility of ethylene than acetylene in the IL had the beneficial effect of allowing high selectivity to ethylene up to 85%, due to the inhibition of its consecutive hydrogenation to ethane. In conclusion, a novel catalytic system for continuous-flow, gas-phase hydrogenations was conceived, taking advantage of the suitable characteristics of CNF/SMF supports. The SSILP concept, involving both homogeneous and heterogeneous active phases has been demonstrated, indicating a great potential and flexibility for continuous-flow industrial applications.