DISCLAIMER: The Graph Chatbot is not programmed to provide explicit or categorical answers to your questions. Rather, it transforms your questions into API requests that are distributed across the various IT services officially administered by EPFL. Its purpose is solely to collect and recommend relevant references to content that you can explore to help you answer your questions.
Delamination is a very frequent damage mechanism that affects the integrity of laminated composites. In this study, the effect of ply orientation on crack growth resistance was analyzed for three different anti-symmetric interfaces (+/- 30 degrees, +/- 45 ...
Owing to their high specific stiffness and strength, Carbon Fiber Reinforced Composites (CFRP) are ideal candidates for the development of lightweight high-performance structures. Within this family, thin-ply composites allow for wider design freedom and p ...
In this work, the damage dependency on ply thickness is investigated experimentally for three different thin-ply CFRP quasi-isotropic laminates, with constituents spanning a large range of properties. It is shown that free edge damage mechanisms, observed ...
This paper aims to propose a novel approach to assess the multi-crack behavior of layered fiber-polymer composites. The Compliance and R-curves generated from this novel approach were useful to understand the multiple delamination process, enabling to eval ...
Delamination in composite materials is often accompanied by fiber bridging that increases resistance to crack growth. Here, delamination of two unidirectional carbon/epoxy systems was studied under monotonic and displacement-controlled fatigue loading. One ...
Fiber-reinforced polymer (FRP) composite materials are currently being selected for the design of lightweight and efficient structural members in a wide number of engineering applications. Sandwich panels with glass fiber-reinforced polymer (GFRP) face she ...
The demand for carbon/epoxy laminated composites is continuously increasing due to their high specific modulus and strength. Among them, laminates made of particularly thin layers (from t=0.015 to 0.150 mm) and called thin-ply composites are gaining in int ...
Existing standards for delamination tests on composite materials typically employ one-dimensional (1D) beam specimens. However, such specimens may not represent real delamination scenarios in composite structures, where cracks tend to propagate in two dime ...
Fiber-polymer composites consist of a polymer matrix and reinforcing fibers made of various materials. These composites exhibit exceptional properties, such as a high strength-to-weight ratio and excellent corrosion resistance, which has led to their incre ...
Thin-ply composites were shown to exhibit significantly delayed transverse cracking, but the linear onset of damage scaling with ply thickness reported by Amacher et al. (2014) did not correspond to the established LEFM based in situ strength model. This s ...