Recrystallization behavior of multi-directionally forged over-aged and solution treated Al-Cu-Mg alloy during non-isothermal annealing
Graph Chatbot
Chat with Graph Search
Ask any question about EPFL courses, lectures, exercises, research, news, etc. or try the example questions below.
DISCLAIMER: The Graph Chatbot is not programmed to provide explicit or categorical answers to your questions. Rather, it transforms your questions into API requests that are distributed across the various IT services officially administered by EPFL. Its purpose is solely to collect and recommend relevant references to content that you can explore to help you answer your questions.
The equiaxed solidification of Al-20 wt.% Zn alloys revealed an unexpectedly large number of fine grains which are in a twin, or near-twin, relationship with their nearest neighbors when minute amounts of Cr (1000 ppm) are added to the melt. Several occurr ...
Nickel base superalloys are used for the manufacturing of monocrystalline turbine blades, due to their outstanding mechanical properties at high temperature. The mechanical properties strongly depend on the presence of γ’ precipitates in the γ matrix. Impr ...
The physical basis and a mathematical formulation of a softening model nicknamed Alsoft, accounting for the combined effect of recovery and recrystallization during annealing of heavily deformed aluminium alloys have been presented. The prediction power of ...
In this paper, investigation of the softening behaviour of a supersaturated Al-Mn-Fe-Si alloy during annealing after cold rolling has been carried out. Two different homogenization conditions were considered, of which one gives a condition of a large amoun ...
A conventional way to determine precipitation kinetics in heat treatable aluminium alloys is to monitor the associated solute loss by in-situ resistivity. A Gleeble machine is used to perform so called isothermal quenching (IQ) resistivity measurements. IQ ...
A conventional way to determine precipitation kinetics in heat treatable aluminium alloys is to monitor the associated solute loss by in-situ resistivity. A Gleeble machine is used to perform so called isothermal quenching (IQ) resistivity measurements. IQ ...
The influence of the quench rate after solution treatment on the bendability of AA6016 aluminum alloy sheets was investigated. Crack initiation during bending tests is found to be independent of quench rate whereas crack propagation is decreased after rapi ...
Ferritic ODS steels containing 14 or 18 wt.% Cr are produced by mechanical alloying (MA), hot consolidation and cold working. This study focuses on the evolution of interstitials such as oxygen, nitrogen and carbon at each stage of the fabrication route by ...
Microstructure evolution has been studied in the nickel-based superalloy PER®72 subjected to hot torsion, to annealing below the primary γ' solvus temperature and to annealing at a supersolvus temperature, with a special emphasis on grain size and twin con ...
The aim of the thesis is to obtain more understanding about the influence of plastic deformation on the microstructural changes observed in single crystal (SX) Ni-based superalloys using diffraction techniques. This work was organised around two main probl ...