Are you an EPFL student looking for a semester project?
Work with us on data science and visualisation projects, and deploy your project as an app on top of Graph Search.
Publication
Are you an EPFL student looking for a semester project?
Work with us on data science and visualisation projects, and deploy your project as an app on top of Graph Search.
CeO2-based nanomaterials and their rich redox chemistry provide a possible route to pollutant abatement in various heterogeneous processes, and are in particular used as sorbents for flue gases and as oxygen promoters in three-way catalytic converters. The use of CeO2-based materials as an active compound participating in catalytic processes is associated to its function as an oxygen buffer, a key property of many materials central to a variety of economically and environmentally important technologies, such as automotive pollution control. In fact, due to the rapid interconversion between the Ce3+ and Ce4+ states, oxygen vacancies and highly mobile O2â ions, CeO2 shows a superior oxygen storage capacity - a property which can be further tuned and optimized by synthesis methods and the addition of further compounds. Noble metal catalysts supported on CeO2-based materials are key components for these applications and makes the search for a material with an optimal oxygen storage capacity an important task. This thesis deals with the synthesis and characterization of CeO2-based materials, and the investigation of structure-performance relationships for catalytic applications. The one-pot polyol synthesis is introduced for the preparation of nanosized M/CeO2 (M = Pt or Au) CO oxidation catalysts, for which the parameters for single-batch syntheses were defined. A further investigation of the reaction products led to the remarkable formulation of the incorporation-segregation mechanism: Pt is at first ionically dispersed in the support lattice (incorporation, Pt:CeO2) and then exsolutes in strongly anchored subnanometric entities (segregation, Pt/CeO2), whose size can be controlled by this approach depending on the thermal treatment and atmosphere. Secondly, an in-depth investigation of this segregation process and its kinetics with ex- and in-situ/operando characterization techniques employing synchrotron-based diffraction and X-ray absorption spectroscopy were carried out by observing the growth of the Pt entities, the change of oxidation states and the interaction with a provided gas composition. In addition, the synthesis methodology was extended to other material systems, which led to ionically dispersed Pt on ceria-zirconia (M:CeO2-ZrO2) in a broad compositional range and an investigation of the thermal behaviour and interplay between Pt and the CeO2-ZrO2 support composition was carried out. Growth inhibition of the support crystallites was observed upon Pt-doping, because of a pinning effect of Pt2+/4+ ions. A compromise between Zr (thermal stability) content and Pt load (active sites) needs to be found and correlated with the final catalytic performance, since the incorporation of Zr and Pt-doping have an effect on the stability range of the cubic CeO2-ZrO2 phases and on the solubility limit of ionic Pt. To conclude the studies on polyol syntheses of CeO2-based materials, the amount of the products was successfully increased by carrying out the process in a continuous manner ("outscaling") with the Segmented Flow Tubular Reactor. Finally, CeO2-based materials were prepared via hydrothermal synthesis in an increased volume in autoclave reactors ("upscaling") to obtain preferably rod-like particles for sorption applications. Overall, this thesis presents a number of novel findings, such as new synthesis approaches allowing for materials engineering, characterization methods and properties of CeO2-based materials themselves.