DISCLAIMER: The Graph Chatbot is not programmed to provide explicit or categorical answers to your questions. Rather, it transforms your questions into API requests that are distributed across the various IT services officially administered by EPFL. Its purpose is solely to collect and recommend relevant references to content that you can explore to help you answer your questions.
A composite running-in wear model for metal-on-metal artificial hip joints, which combines tribo-corrosion and lubrication aspects, was published recently. In order to check the quality of the model prediction, wear rates from nineteen well-controlled simu ...
Al-Cr-Fe complex metallic alloys are new intermetallic phases with low surface energy, low friction, and high corrosion resistance down to very low pH values (0-2). Flow microcapillary plasma mass spectrometry under potentiostatic control was used to chara ...
Can microbes be used to preserve archaeological iron objects? Lucrezia Comensolia, J. Maillardb, P. Juniera and E. Josepha,c a Laboratory of Microbiology, Institute of Biology University of Neuchâtel, Switzerland b Laboratory for Environmental Biotechnolog ...
The effect of body fluids inorganic species on element-specific dissolution of a Mg-Y-Rare earth elements (RE) alloy was investigated by flow microcapillary plasma mass spectrometry. A new important aspect of this method is the online monitoring of precipi ...
Knee and hip joint replacement implants involve a sliding contact between the femoral component and the tibial or acetabular component immersed in body fluids, thus making the metallic parts susceptible to tribocorrosion. Micro-motions occur at points of f ...
Wear is a key problem limiting the lifetime and performance of total hip arthroplasty. The synovial fluid, acting as lubricant, can alleviate the wear of implants but also introduces corrosion. The interaction of mechanical wear and electrochemical corrosi ...
In the present study, a forged CoCrMo (ISO 5832-12) has been subjected to pulsed plasma treatment in a N-2/H-2 atmosphere at low temperatures (below 500 A degrees C). This treatment resulted in the formation of a layer composed by dispersed chromium nitrid ...
The present work focuses on stress-corrosion mechanisms in soda-lime silica glass. Four-point beam-bending tests were performed on small specimens, measuring failure time in function of temperature and relative humidity. By using linear elastic fracture me ...
A good biocompatibility, excellent mechanical properties and high corrosion resistance characterize CoCrMo alloys. Therefore they are widely used for artificial joints in biomedical implants. However, the degradation of the implants during service life lea ...
Hundreds of tons of depleted uranium (DU) ammunition were used in previous armed conflicts in Iraq, Bosnia and Herzegovina, and Serbia/Kosovo. The majority (>90%) of DU penetrators miss their target and, if left in the environment, corrode in these postcon ...