Sustainable Hydrogenation of Nitroarenes to Anilines with Highly Active in-situ Generated Copper Nanoparticles

Metal nanoparticles (NPs) are usually stabilized by a capping agent, a surfactant, or a support material, to maintain their integrity. However, these strategies can impact their intrinsic catalytic activity. Here, we demonstrate that the in-situ formation of copper NPs (Cu(0)NPs) upon the reduction of the earth-abundant Jacquesdietrichite mineral with ammonia borane (NH3BH3, AB) can provide an alternative solution for stability issues. During the formation of Cu(0)NPs, hydrogen gas is released from AB, and utilized for the reduction of nitroarenes to their corresponding anilines, at room temperature and under ambient pressure. After the nitroarene-to-aniline conversion is completed, regeneration of the mineral occurs upon the exposure of Cu(0)NPs to air. Thus, the hydrogenation reaction can be performed multiple times without the loss of the Cu(0)NPs' activity. As a proof-of-concept, the hydrogenation of drug molecules "flutamide" and "nimesulide" was also performed and their corresponding amino-compounds were isolated in high selectivity and yield.

Nanostructured Electrocatalysts for Water Splitting Reactions

Lucas-Alexandre Stern

At the dawn of the 21st century, mankind is facing an important energy challenge. Future energy demand can only be met by large scale exploitation of renewable energy resources. Solar energy is abundant, with a sufficient capacity for the growing energy demand. However, it is necessary to implement renewable energy storage means. Hydrogen is considered as the energy carrier of the future. An energy economy based on hydrogen is viable only if hydrogen is produced from sustainable means. Water electrolysis is the most promising technique to produce hydrogen directly from water. Yet, the efficiency is limited and electrocatalysts are required to drive both the hydrogen evolution reaction and oxygen evolution reaction. Scarce and expensive materials are currently used to drive these reactions. It is, thus, imperative that efficient Earth-abundant catalysts are developed. Nanostructuring enhances the performance of inexpensive materials for water splitting and several catalysts were studied for this goal. Chapter 2 describes the application of nanostructuring technique to the archetypical catalysts that are nickel oxides for oxygen evolution. The prepared nanoparticles show superior activity towards oxygen evolution than that of their bulk counterpart. The ultrafine size of nanoparticles synthesized allowed the exposure of a higher number of active sites. The activity for oxygen evolution was, thus, significantly enhanced. We also detailed that short conditioning of the electrode improved the performance of the evaluated materials. In chapter 3 we carefully studied nanoparticles and nanowires of nickel phosphide. The catalysts is known to be really active for hydrogen evolution. Our group suspected that this material was, also, a potential oxygen evolution catalyst. We proved, for the first time, that nickel phosphide is a remarkable oxygen evolution catalyst. Under alkaline conditions, used for oxygen evolution, we observed an in-situ formation of a core-shell heterostructure, a typical nanostructure architecture. The surface oxidation of this material allowed high oxygen evolution capabilities. We concluded that careful oxidation of nanostructured materials, as observed for nickel phosphide, is essential for the preparation of future outstanding oxygen evolution catalysts. Chapter 4 details the fabrication of direct solar-to-fuel electrode using cobalt phosphide as hydrogen evolving catalyst. Instead of using the electrical energy provided by solar energy, solar irradiation on the developed assembly allows direct hydrogen production. The careful design of the light-sensitive electrode (photocathode) is detailed. Simple incorporation of cobalt phosphide by means of photodeposition alleviates the cost of the electrode fabrication. The assembled electrode is active for hydrogen evolution under visible light irradiation. In the chapter 5 we sought to fabricate a 3-dimensional hydrogen evolving catalyst. This nanostructure is based on polymer brushes on a flat conducting substrate. Once the brushes are grown on the substrate, a molybdenum sulfide catalyst is then incorporated by simple soaking technique. We were able to tune the loading of the catalyst and the corresponding activity by changing the polymer properties. The height of the polymer was modified as well as its packing density. The resulting activity proved superior to similar approaches and to previous reports on carefully engineered molybdenum sulfide catalysts.

EPFL2017

Amorphous Molybdenum Sulfide Films as Hydrogen Evolution Catalysts in Water

Daniel Andreas Merki

Molecular hydrogen is a promising candidate to replace fossil fuels as the energy carrier. Hydrogen does not exist in its molecular form on earth and must therefore be generated, starting from hydrogen-rich compounds. Water would be a renewable resource for hydrogen. It can be split into oxygen and hydrogen. Water splitting, however, needs electrical energy. If this energy is produced from renewable resources, such as solar or wind power, water splitting would be a sustainable and green process. One key step in water splitting is the reduction of protons to form hydrogen. To achieve a high efficiency in this reaction, catalysts are required. This dissertation is devoted to the development of hydrogen evolution catalysts that are made of earth-abundant and inexpensive materials. First, transition metal complexes of tetrathiotungstate and tetrathiomolybdate were studied as potential homogeneous catalysts for hydrogen evolution in organic or aqueous solutions (chapter 1). The redox activity of these complexes was investigated by cyclic voltammetry in the absence and presence of an acid in organic solutions. The first reduction peak of (Pr4N)2[Ni(MoS4)2] became more intense and was shifted to less negative potentials upon addition of an acid, e.g. p-cyanoanilinium tetrafluoroborate. This was considered as a sign for catalytic proton reduction. Electrolysis of a solution containing (Pr4N)2[Ni(MoS4)2] and an acid produced hydrogen. However, the complex turned out to be a precursor of the real catalytically active species, which was deposited on the working electrode’s surface during the electrochemical experiment. Consecutive cyclic voltammetric scans were found to be a good method to deposit the catalytically active film in a controllable manner from an aqueous solution of (Pr4N)2[Ni(MoS4)2]. Furthermore, a catalytically active film could be deposited from a solution of MoS42-, i.e. in the absence of Ni2+. Chapter 2 describes the investigation and characterization of films made using MoS42- as the precursor. The films consist of amorphous molybdenum sulfide. They are efficient hydrogen evolution catalysts in water. The films were characterized by XPS and electron microscopy. Whereas the pre-catalysts could be MoS3 or MoS2, the active form of the catalysts was identified as amorphous MoSx, with x close to 2. Significant geometric current densities were achieved at low overpotentials (e.g., ca. 15 mA/cm2 at η = 200 mV) using these catalysts. The catalysis was compatible with a wide range of pH values. The current efficiency for hydrogen production was quantitative. A Tafel slope of 39 mV/dec was observed, suggesting a rate-determining Heyrovsky step. The turnover frequency per active site was estimated.

EPFL2012

Floating conductive catalytic nano-rafts at soft interfaces for hydrogen evolution

Hubert Girault, Micheal Diarmaid Scanlon

Mo2C nanowires and composites of Mo2C nanoparticles formed on multiwalled carbon nanotubes (Mo2C/CNT) were developed as advanced catalysts for hydrogen evolution at a polarised water–1,2-dichloroethane interface. Each catalyst acts as a catalytic nano-raft suspended at the interface to markedly enhance the rates of biphasic proton reduction in the presence of an organic solubilised electron donor, decamethylferrocene. Mo2C nanoparticles were grown in situ on the conductive CNT support, achieving a high dispersion and intimate contact, thereby facilitating electron transfer between the components. The high catalytic activity of each catalyst was successfully demonstrated by their respective impacts on the reaction kinetics. The reaction rate increased more than 1000 times when the Mo2C/CNT composite was present at a very low concentration of 25 μM. CNTs have the ability to act as highly efficient conduits or “transport superhighways” for injected electrons to reach the catalytic sites of the nanoparticle. Electrochemical instabilities, similar to those observed for the transfer of surface-active ions, were observed under experimental conditions that produced an abundance of hydrogen at the interface. Finally, the movement of CNTs floating at the interface under the influence of a cycling applied interfacial Galvani potential difference was vividly captured in a short movie