Towards reproducible lithium-ion battery cycling using liquid-phase transmission electron microscopy

Jing Hou
EPFL, 2021
EPFL thesis

Abstract

Electric vehicles (EVs) have gained widespread attention in recent years as the dominant strategy for curbing CO2 emissions through transport electrification. Lithium-ion batteries (LIBs) are currently the most suitable and almost exclusively employed energy storage device for powering EVs. Nickel-rich layered oxides of the general formula LiNixCoyMnzO2 (NCM) are widely used as the cathode in LIBs due to their high capacity and low cost. However, the increasing nickel content reduces the stability for the higher energy density that is particularly required for meeting the mileage demand. Hence, understanding the degradation mechanisms of Ni-rich NCM is of great importance for optimizing the performance of battery systems. This thesis aims to develop methodologies for reproducible and reliable testing of battery systems using transmission electron microscopy (TEM) in the liquid phase in order to probe, at the nanoscale, the evolution of the cathode materials as they respond to the electrochemical charge/discharge cycling. In detail, this thesis first establishes lithium-ion battery electrochemical processes in a microcell, such as electroplating and charge/discharge analysis. The setup is optimized through the electrode configuration and preparation, while the cycling conditions are adapted for achieving similar electrochemical performance as compared to the conventional bulk cell. With the optimized cell, primary NCM particles are probed using in situ electrochemical cells coupled with a scanning transmission electron microscopy-energy-dispersive X-ray spectroscopy (STEM-EDS). The electrochemically induced evolution of NCM that is analyzed using liquid cell TEM uncovers the various degradation mechanisms for the same material under different cycling conditions and for specimens with different Ni content that are cycled under the same conditions. The results offer insights for controlling the electrochemical parameters in the liquid cell for battery studies. Ultimately, the structural and chemical information on the degradation of NCM cathodes can guide our way for designing more advanced NCM cathodes with desirable capacity and enhanced stability simultaneously.

Official source

https://infoscience.epfl.ch/record/283959?ln=en

About this result

This page is automatically generated and may contain information that is not correct, complete, up-to-date, or relevant to your search query. The same applies to every other page on this website. Please make sure to verify the information with EPFL's official sources.

Related concepts

Related publications

Jing Hou
EPFL, 2021
EPFL thesis

Abstract

Official source

https://infoscience.epfl.ch/record/283959?ln=en

About this result

Related concepts (19)

Related concepts

Related publications (13)

Related publications

The title compds., useful in the prodn. of dye intermediates, are prepd. in acid media in an electrolysis cell whose electrodes are sepd. by a membrane. At the cathode, anthraquinones are reductively cyclized with glycerol [56-81-5] to give the corresponding benzanthrones. In the anode chamber the oxidn. state of a transition metal ion is electrochem. increased by 1 and the resulting ion serves as a chem. oxidant for a planar polycyclic arom. compd. Thus, to the cathode chamber contg. 46.8 g anthraquinone [84-65-1] in 1300 g H2SO4, 31.05 g glycerol was added dropwise while the current was running. On the anodic side 10 g MnSO4.H2O was suspended in 130 g 88% H2SO4. benzanthrone [82-05-3] (85%) Was isolated from the cathodic portion, while the anolyte was used to cyclooxidize 10 g 4,4'-bibenzanthrone [116-90-5] to dioxoviolanthrone [64346-54-9] which was reduced with NaHSO3 to dihydroxyviolanthrone (I) [26545-62-0] in 76.4% yield. I was used as an intermediate in the synthesis of vat dyes. [on SciFinder (R)]

(Ciba-Geigy A.-G., Switz.).1982

, , ,

Among the perovskites used to catalyze the oxygen evolution reaction (OER), Ba0.5Sr0.5Co0.8Fe0.2O3-delta (BSCF) exhibits excellent activity which is thought to be related to dynamic reconstruction at the flexible perovskite surface due to accommodation of large amount of oxygen vacancies. By studying the local structure and chemistry of BSCF surfaces, in detail, via a range of transmission electron microscopy (TEM) methods, we show that the surfaces of the as-synthesized BSCF particles are Co/Fe rich, and remarkably, adopt a spinel-like structure with a reduced valence of Co ions. Post-mortem and identical location TEM analyses reveal that the Co/Fe spinel-like surface retains a stable chemical environment of the Co/Fe ions, although its structure weakens after electrochemical processing. Further, it is verified that prior to the onset of OER, the Co/Fe spinel-like surface promotes the formation of the highly active Co(Fe)OOH phase, which enhances the OER electrocatalytic properties of the underlying conductive BSCF perovskite. This study provides a detailed understanding of the fundamental transformations that oxide catalysts undergo during electrochemical processes and can aid in the development of novel oxide catalysts with enhanced activity.

AMER CHEMICAL SOC2020

, ,

AlN thin films were grown by reactive sputtering on amorphous SiO2 thin films. Film texture, x-ray rocking curve width, mechanical stress, and the clamped piezoelectric constant d33,f were studied as a function of rf bias power and substrate roughness. A high d33,f of 5.0 pm/V was achieved at low substrate roughness and low mechanical AlN film stress. Increasing substrate roughness and stress leads to a deterioration of d33,f, which is correlated with a higher density of opposite polarity grains detected by piezoresponse force microscopy. Extrapolating to 100% uniform polarity, a d33,f of 6.1 pm/V is derived as highest possible value, probably corresponding to the d33,f=e33/cof perfect single crystalline material. Growth mechanisms are proposed and underlined by high resolution transmission electron microscopy to explain the observed phenomena.

2010