Effective transverse piezoelectric coefficient e(31,f) has been measured on (100)/(001) sol-gel Pb(ZrXTi1-X) thin films with compositions between 30% and 45% Zr. A maximum value of 8.07 +/- 0.36 C/m(2) at 40% Zr is found. The influence of the poling field ranging from 50 kV/cm to 250 kV/cm has been evaluated.