Surface characterization of MnxGe1-x and CryMnxGe1-x-y dilute magnetic semiconductors

Harald Brune, Laurent Claude, Pietro Gambardella, Stefano Rusponi
2007
Article

Résumé

We have used x-ray photoemission electron microscopy (XPEEM) and x-ray absorption spectroscopy (XAS) to characterize MnxGe1-x and CryMnxGe1-x-y films grown by molecular beam epitaxy. The surface layers of the as-grown films probed by XPEEM present segregation of Mn-rich phases. XAS using both total electron yield and fluorescence yield detection shows that the films are heavily oxidized after exposure to air. Etching in HF and HCl can be used to reduce oxidation, but inhomogeneities in the surface composition might not be completely eliminated depending on the Mn concentration. X-ray magnetic circular dichroism (XMCD) measurements reveal that neither the etched nor the as-grown films present remanent ferromagnetic behavior down to a temperature of 5 K within the probing depth of the fluorescence yield (similar to 20 nm). Mn is paramagnetic in both the oxidized and etched samples, with an increased tendency to order magnetically toward the interior of the films. Cr in CryMnxGe1-x-y possesses a paramagnetic moment only in the oxidized form. A comparison of the XAS line shapes obtained in the present study with those of Mn impurities deposited on Ge and GaAs surfaces demonstrates that the interpretation of XAS spectra of Mn-doped dilute magnetic semiconductors in the literature is often affected by residual oxidation.

Official source

https://infoscience.epfl.ch/record/135839?ln=fr

À propos de ce résultat

Cette page est générée automatiquement et peut contenir des informations qui ne sont pas correctes, complètes, à jour ou pertinentes par rapport à votre recherche. Il en va de même pour toutes les autres pages de ce site. Veillez à vérifier les informations auprès des sources officielles de l'EPFL.

Concepts associés

Chargement

Publications associées

Chargement

In this thesis we report investigations on supramolecular architectures assembled at well-defined metal surfaces. Supramolecular chemistry is dedicated to the study and use of non-covalent interactions to build highly organized molecular arrangements, aiming ultimately at creating systems with tailored properties and useful functions. The adaptation of its powerful principles to fabricate molecular systems at surfaces has already been proven to be very promising; the extended possibilities for the choice of on the one hand molecules with defined size, shape, symmetry and function, and on the other hand substrates with controlled composition, symmetry and patterning allow for a quasi-infinite tuning of the structure and properties of the respective assemblies. The Scanning Tunneling Microscope (STM) is a tool particularly efficient for the nanoscale elucidation of supramolecular systems at surfaces, simultaneously providing topographic and spectroscopic information at the single-atom level. In this regard, a new Low-Temperature STM (LT-STM) operational at temperatures in the range 5 to 400 K has been constructed. A detailed description of the instrument is provided and the demonstration of its exquisite performance represents a major achievement. In addition to local STM studies, complementary experiments were performed with a synchrotron radiation source using integral techniques, namely X-ray Absorption Spectroscopy (XAS) and X-ray Magnetic Circular Dichroism (XMCD). We present results obtained with the linear organic linker 1,4-benzenedicarboxylic acid (terephthalic acid - TPA) on the Au(111), Cu(111) and Cu(100) surfaces. The three-dimensional design principles of supramolecular chemistry could be successfully adapted to these low-dimensional systems. TPA molecules adsorbed on Au(111) organize in two-dimensional molecular sheets, wherein the typical one-dimensional hydrogen-bonded chain motif is found. We show that the inhomogeneities induced by the surface reconstruction can be used to examine the response of the supramolecular self-assembly. In particular, variations in the hydrogen bond length of up to 20% are encountered. On Cu(111), a strict commensurability of the supramolecular sheet to the substrate is not possible because of the reduced lattice spacing of the latter, and the creation of defects is analyzed. Due to their peculiar reactivity, the elbow sites of the reconstructed Au(111) surface act as nucleation centers in the epitaxial growth of transition metals (Fe, Co, Ni), leading to the formation of regular arrays of nanoscale metallic islands. We take advantage of this patterning to steer the formation of metallosupramolecular nano-architectures. Co-deposited TPA molecules attack both Fe and Co clusters and metal-carboxylate linkages evolve. Depending on the deposition parameters, nanoporous grids, mesoscopically organized stripes or truly one-dimensional linkages are obtained. Furthermore, the dynamics of the formation of the nanogrids are monitored in situ. Finally, we report investigations of the magnetic and electronic properties of surface-supported coordination architectures by means of XAS and XMCD. We studied Fe-terephthalate systems engineered on a Cu(100) substrate. Both mononuclear Fe(TPA)4 compounds and diiron centers structures in 2D Fe-TPA lattices exhibit a paramagnetic behavior. Moreover, we demonstrate the decisive influence of the ligand rather than the substrate on the electronic ground state of the metal centers, thus illustrating new vistas to effectively tailor the valence state and magnetic moment of transition metal atoms at surfaces.

EPFL2004

Chargement

This thesis reports on the magnetism of low coordinated Fe and Co atoms in different chemical and electronic environments. The objective of this research was to contribute to the fundamental understanding of the magnetic properties, such as magneto-crystalline anisotropy energy (MAE), orbital and spin magnetic moment, of surface supported transition metal (TM) atoms and one atomic layer thick epitaxial TM films. A detailed knowledge on the interplay of electronic hybridization and magnetic properties is mandatory to elaborate new materials with high perpendicular magnetic anisotropy and acceptable writing field for future use in magnetic recording devices. The magnetic properties of the different experimental systems were investigated by x-ray absorption spectroscopy, x-ray magnetic circular dichroism, and magneto-optical Kerr effect (MOKE) and they were correlated to the morphology obtained by scanning tunneling microscopy (STM). The first part focuses on the effect of electronic hybridization between isolated 3d TM atoms and different kinds of substrates. First, we considered 4d and 5d TM substrates known for their high magnetic polarizability due to the close onset of ferromagnetism. Deposition of single Fe and Co atoms on Rh(111), Pd(111), and Pt(111) produces an increasing MAE going from Rh to Pd and finally to Pt that we directly correlate to the increasing spin-orbit constant of the substrate interlinking the induced magnetic moment and the MAE. Further we investigated single Fe and Co atoms on two different insulating layers, namely Al2O3/Ni3Al(111) and Cu2N/Cu(001), providing an efficient decoupling of the TM 3d states from the conduction electrons of the substrates. In case of the alumina film the absorption spectra of Fe and Co show a pronounced multiplet structure. On Cu2N the multiplet features of the adatoms are less defined due to the lower thickness of the screening layer. On both insulating layers we find a common out-of-plane easy axis, highly unquenched orbital moments, and giant MAE values of several meV/atom which are due to the formation of strong anisotropic bonds with the O and N atoms, respectively. The second part is dedicated to single atom thick layers of Fe and Co deposited on Pt(111) and Rh(111). We find the MAE to be strongly enhanced compared with bulk and we establish a direct proportionality between the induced magnetic moment of the topmost substrate layer and the MAE. The study of bimetallic Fe1-xCox alloys on platinum reveal a material with high MAE (0.5 meV at the equiatomic composition), large saturation magnetization (3μB to 2μB going from Fe to Co), and perpendicular magnetization easy axis. These characteristics hint at new possibilities for the further miniaturization of the grain size in recording devices. In the last part the theoretical description of the MOKE for ultra-thin films is extended to the transverse geometry and improved analytic formulae for the polar and longitudinal geometry are presented. This finding was used to optimize the Kerr signal for a new MOKE setup which is fully integrated in an ultrahigh vacuum chamber combining in situ MOKE and STM. The setup performance was demonstrated for a continuous film of 0.9 monolayers (ML) Co/Rh(111) with in-plane easy axis and for a superlattice of nanometric double layer Co islands on Au(11,12,12) with out-of-plane easy axis. The detection limit is 0.5 ML for transverse and 0.1 ML for polar Kerr geometry corresponding for island superlattices with the density of Co/Au(11,12,12) to islands composed of about 50 atoms. Moreover, the setup holds two independent ways to measure the MAE which is either by thermally induced magnetization reversal or by applying a torque onto the magnetization by turning the magnetic field. Both ways yield similar results for 1.1 ML Co/Au(11,12,12).

EPFL2009

Chargement

, , ,

The magnetic properties of individual Fe and Co atoms as well as of small Fe clusters adsorbed on two atomic layers of Al2O3 grown on Ni3Al(111) have been investigated by x-ray absorption spectroscopy and x-ray magnetic circular dichroism. We find ratios of the orbital over the effective spin magnetic moments of r=0.53 +/- 0.09 for Fe and r=0.91 +/- 0.06 for Co, which are both very close to the free-atom values of r=0.5 and 1, respectively. The magnetization curves acquired at the Fe and Ni edges demonstrate a distinctly different magnetization reversal of the transition-metal nanostructures and the substrate excluding magnetic dipolar or exchange coupling through the alumina film. Our data reveal an out-of-plane easy magnetization axis for Fe and Co originating from the spatially anisotropic hybridization of the 3d states of the adatom, with the 2p states of the oxygen terminated Al2O3 surface. We conclude that the alumina film effectively decouples the magnetic adatoms from the underlying metal substrate while providing a crystal-field environment giving rise to high magnetic anisotropy.

2010

Chargement

EPFL2004

EPFL2009