Characterization and modeling of twinned dendrite growth
Publications associées (86)
Graph Chatbot
Chattez avec Graph Search
Posez n’importe quelle question sur les cours, conférences, exercices, recherches, actualités, etc. de l’EPFL ou essayez les exemples de questions ci-dessous.
AVERTISSEMENT : Le chatbot Graph n'est pas programmé pour fournir des réponses explicites ou catégoriques à vos questions. Il transforme plutôt vos questions en demandes API qui sont distribuées aux différents services informatiques officiellement administrés par l'EPFL. Son but est uniquement de collecter et de recommander des références pertinentes à des contenus que vous pouvez explorer pour vous aider à répondre à vos questions.
The structure of the hardening η′-phase precipitates in Al–Zn–Mg alloys has been investigated by using precession electron diffraction and X-ray synchrotron radiation diffraction. The latter was recorded as a three-dimensional, continuous intensity distrib ...
Copper and copper alloys typically experience a sharp loss in ductility at intermediate temperature, induced by grain boundary damage and fracture processes. The susceptibility of the material to intermediate temperature embrittlement is, as a result, stro ...
The growth kinetics advantage of twinned aluminum dendrites over regular ones is still an unsolved problem of solidification. Although it is linked to the tip geometry, the influence of a coherent (1 1 1) twin plane on a < 1 1 0 > twinned dendrite tip is u ...
The main goal of this work was to manufacture an oxide dispersion strengthened (ODS) reduced activation ferritic steel from a pre-alloyed, gas atomised Fe-14Cr-2W-0.2Ti (in wt.%) powder mechanically alloyed with either 0.3%Y2O(3) or 0.5%Fe2Y particles and ...
Porosity is one of the major defects in castings because it reduces the mechanical properties of a cast piece [1]. Porosity formation results from the effect of two concomitant mechanisms, namely solidification shrinkage and segregation/precipitation of ga ...
Continuous hot-dip galvanization is a process during which steel sheets are coated with a layer of Zn-Al alloy to protect them against corrosion. As the name indicates, this is achieved by dipping the preheated sheet into a bath of molten alloy. The sheet ...
The main goal of this work was to manufacture an oxide dispersion strengthened (ODS) reduced activation ferritic steel from a pre-alloyed, gas atomised Fe-14Cr-2W-0.2Ti (in wt.%) powder mechanically alloyed with either 0.3%Y2O(3) or 0.5%Fe2Y particles and ...
The Haasen plot (inverse activation area 1/Delta alpha vs. offset flow stress sigma-sigma(s)) for solute-strengthened alloys is usually assumed additive, 1/Delta alpha = 1/Delta alpha(s) + 1/Delta alpha(f), with 1/Delta alpha(f) similar to beta(sigma-sigma ...
Twinned dendrite growth has been found to occur in aluminum alloys when critical thermal conditions (G approximate to 100 K/cm, nu(s) approximate to 1 mm/s) and a slight convection in the melt are present during directional solidification. Split in their t ...
Minerals, Metals & Materials Soc, 184 Thorn Hill Rd, Warrendale, Pa 15086-7514 Usa2009
A phase-field model for the solid-solid alpha -> gamma transition of Ti-Al binary alloys is presented based on analytical Gibbs free energies and couplings to the thermodynamical database ThermoCalc. The equilibrium values recover the alpha + gamma phase b ...