Dilute nitride InGaAsN/GaAs V-groove quantum wires emitting at 1.3 μm wavelength at room temperature
Elyahou Kapon, Alok Rudra, Marco Cantoni, Barbora Bártová, Romain Carron, Pascal Gallo, Marco Felici
2011
Article
2011
Article
Résumé
Site-controlled InGaAsN quantum wires (QWRs) emitting at 1.3 lm at room temperature were grown on V-grooved GaAs substrates by modulated-flux metallorganic vapor phase epitaxy. The nonplanar substrate template is shown to enhance the nitrogen uptake, evidenced by a redshift in photoluminescence wavelength twice larger for the QWRs than for the adjacent quantum well regions. The mechanism of this increase in nitrogen incorporation efficiency, achieved without degradation in optical properties, is explained by the extended gradient of In content at the step-rich QWR interfaces.
Source officielle
À propos de ce résultat
Cette page est générée automatiquement et peut contenir des informations qui ne sont pas correctes, complètes, à jour ou pertinentes par rapport à votre recherche. Il en va de même pour toutes les autres pages de ce site. Veillez à vérifier les informations auprès des sources officielles de l'EPFL.