Acier au carboneL’acier au carbone est un acier dont le principal composant d'alliage est le carbone, entre 0,12 et 2,0 %, les autres éléments d'alliages étant en quantité très faible. Plus la teneur en carbone est élevée, plus la résistance mécanique de l'acier peut être augmentée par traitement thermique, au détriment de sa ductilité. L'acier au carbone est un acier qui contient du carbone comme principal alliage. Il est solide, résistant et peu coûteux, mais il rouille facilement. L'acier inoxydable, quant à lui, contient principalement du chrome et de nickel.
Structural integrity and failureStructural integrity and failure is an aspect of engineering that deals with the ability of a structure to support a designed structural load (weight, force, etc.) without breaking and includes the study of past structural failures in order to prevent failures in future designs. Structural integrity is the ability of an item—either a structural component or a structure consisting of many components—to hold together under a load, including its own weight, without breaking or deforming excessively.
Seismic loadingSeismic loading is one of the basic concepts of earthquake engineering which means application of an earthquake-generated agitation to a structure. It happens at contact surfaces of a structure either with the ground, or with adjacent structures, or with gravity waves from tsunami. Seismic loading depends, primarily, on: Anticipated earthquake's parameters at the site - known as seismic hazard Geotechnical parameters of the site Structure's parameters Characteristics of the anticipated gravity waves from tsunami (if applicable).
Rupture (matériau)thumb|Courbe de traction idéale d'un matériau ductile thumb|Courbe de traction typique pour un matériau fragile En science des matériaux, la rupture ou fracture d'un matériau est la séparation, partielle (comme une crique ou une fissure ou une brisure) ou complète, en deux ou plusieurs pièces sous l'action d'une contrainte. Une rupture peut être souhaitée par le concepteur de la pièce comme dans le cas de la conception de dispositifs de sécurité ou au contraire celui-ci cherche à éviter cette rupture en mettant en adéquation la fonction de cette pièce avec les dimensionnements et choix des matériaux utilisés et des procédés de fabrication.
Ossature en acierlien=//upload.wikimedia.org/wikipedia/commons/thumb/2/2e/Lloyds_Axe_and_Willis.jpg/170px-Lloyds_Axe_and_Willis.jpg|vignette|200px|Ossature en acier rectangulaire, ou «charpente périmétrique» du bâtiment Willis (à droite) contrastain avec la charpente du 30 St Mary Axe, à Londres. L'ossature en acier est une technique de construction avec une ossature de colonnes verticales en acier et de horizontales, construites selon une grille rectangulaire pour supporter les planchers, le toit et les murs d'un bâtiment qui sont tous attachés à l'ossature.
Seismic analysisSeismic analysis is a subset of structural analysis and is the calculation of the response of a building (or nonbuilding) structure to earthquakes. It is part of the process of structural design, earthquake engineering or structural assessment and retrofit (see structural engineering) in regions where earthquakes are prevalent. As seen in the figure, a building has the potential to 'wave' back and forth during an earthquake (or even a severe wind storm). This is called the 'fundamental mode', and is the lowest frequency of building response.
Ultimate tensile strengthUltimate tensile strength (also called UTS, tensile strength, TS, ultimate strength or in notation) is the maximum stress that a material can withstand while being stretched or pulled before breaking. In brittle materials the ultimate tensile strength is close to the yield point, whereas in ductile materials the ultimate tensile strength can be higher. The ultimate tensile strength is usually found by performing a tensile test and recording the engineering stress versus strain.
T-beamA T-beam (or tee beam), used in construction, is a load-bearing structure of reinforced concrete, wood or metal, with a -shaped cross section. The top of the -shaped cross section serves as a flange or compression member in resisting compressive stresses. The web (vertical section) of the beam below the compression flange serves to resist shear stress. When used for highway bridges the beam incorporates reinforcing bars in the bottom of the beam to resist the tensile stresses which occur during bending.
Résistance des matériauxvignette|Essai de compression sur une éprouvette de béton, une pression croissante est appliquée verticalement sur l'échantillon pendant que deux appareils mesurent les déformations longitudinales et transversales de l'éprouvette. vignette|À l'issue du test, l'éprouvette s'est rompue. Notez la cassure longitudinale. La résistance des matériaux (RDM) est une discipline particulière de la mécanique des milieux continus, permettant le calcul des contraintes et déformations dans les structures des différents matériaux (machines, génie mécanique, bâtiment et génie civil).
AcierUn acier est un alliage métallique constitué principalement de fer et de carbone. Il se distingue des fontes et des ferroalliages par sa teneur en carbone comprise entre 0,02 % et 2 % en masse. C’est essentiellement cette teneur en carbone qui confère à l'acier ses propriétés. Histoire de la production de l'acier L’Âge du fer se caractérise par l’adaptation du bas fourneau à la réduction du fer. Ce bas fourneau produit une loupe, un mélange hétérogène de fer, d’acier et de laitier, dont les meilleurs morceaux doivent être sélectionnés, puis cinglés pour en chasser le laitier.