Solid solution strengtheningIn metallurgy, solid solution strengthening is a type of alloying that can be used to improve the strength of a pure metal. The technique works by adding atoms of one element (the alloying element) to the crystalline lattice of another element (the base metal), forming a solid solution. The local nonuniformity in the lattice due to the alloying element makes plastic deformation more difficult by impeding dislocation motion through stress fields. In contrast, alloying beyond the solubility limit can form a second phase, leading to strengthening via other mechanisms (e.
Yield (engineering)In materials science and engineering, the yield point is the point on a stress-strain curve that indicates the limit of elastic behavior and the beginning of plastic behavior. Below the yield point, a material will deform elastically and will return to its original shape when the applied stress is removed. Once the yield point is passed, some fraction of the deformation will be permanent and non-reversible and is known as plastic deformation.
AcierUn acier est un alliage métallique constitué principalement de fer et de carbone. Il se distingue des fontes et des ferroalliages par sa teneur en carbone comprise entre 0,02 % et 2 % en masse. C’est essentiellement cette teneur en carbone qui confère à l'acier ses propriétés. Histoire de la production de l'acier L’Âge du fer se caractérise par l’adaptation du bas fourneau à la réduction du fer. Ce bas fourneau produit une loupe, un mélange hétérogène de fer, d’acier et de laitier, dont les meilleurs morceaux doivent être sélectionnés, puis cinglés pour en chasser le laitier.
Matériau compositevignette|Multicouche, un exemple de matériau composite. Un matériau composite est un assemblage ou un mélange hétérogène d'au moins deux composants, non miscibles mais ayant une forte capacité d'interpénétration et d'adhésion, dont les propriétés mécaniques se complètent. Le nouveau matériau ainsi constitué possède des propriétés avantageuses que les composants seuls ne possèdent pas. Bien que le terme composite soit moderne, de tels matériaux ont été inventés et abondamment utilisés bien avant l'Antiquité, comme les torchis pour la construction de bâtiments.
Durcissement structuralLe durcissement structural est comme son nom l'indique un procédé permettant de durcir un alliage de métaux. Il nécessite un alliage métastable, dont la forme stable à température ambiante est un composé intermétallique constitué de deux phases différentes. Un recuit à l'intérieur du nez du diagramme TTT entraîne la germination de précipités de différentes nouvelles phases plus ou moins stables. Ces précipités, qu'ils soient cohérents ou incohérents avec la phase principale constituent des obstacles sur le chemin des dislocations ce qui augmente la dureté ainsi que les propriétés en traction du matériau.
Loi de Hall-PetchIn materials science, grain-boundary strengthening (or Hall–Petch strengthening) is a method of strengthening materials by changing their average crystallite (grain) size. It is based on the observation that grain boundaries are insurmountable borders for dislocations and that the number of dislocations within a grain has an effect on how stress builds up in the adjacent grain, which will eventually activate dislocation sources and thus enabling deformation in the neighbouring grain as well.
Tenseur des contraintesLe tenseur des contraintes est un tenseur d'ordre 2 utilisé en mécanique des milieux continus pour caractériser l'état de contrainte, c'est-à-dire les efforts intérieurs mis en jeu entre les portions déformées d'un milieu. Le terme a été introduit par Cauchy vers 1822. Comme les efforts intérieurs sont définis pour chaque surface coupant le milieu (on parle d'ailleurs également d'efforts surfaciques), le tenseur est défini localement, en chaque point du solide. L'état de contrainte du solide est donc représenté par un champ tensoriel.
DuctilitéLa ductilité est la capacité d'un matériau à se déformer plastiquement sans se rompre. La rupture se fait lorsqu'un défaut (fissure ou cavité) devient critique et se propage. Un matériau qui présente une grande déformation plastique à rupture est dit ductile, sinon il est dit fragile. C'est une propriété dite « purement géométrique » : elle ne caractérise qu'un allongement à la rupture (sans unité, ou l'allongement en mètre si la longueur pour l'essai de ductilité est normalisée), indépendamment de l'énergie ou de la contrainte nécessaire à cette rupture.
Specific strengthThe specific strength is a material's (or muscle's) strength (force per unit area at failure) divided by its density. It is also known as the strength-to-weight ratio or strength/weight ratio or strength-to-mass ratio. In fiber or textile applications, tenacity is the usual measure of specific strength. The SI unit for specific strength is Pa⋅m3/kg, or N⋅m/kg, which is dimensionally equivalent to m2/s2, though the latter form is rarely used.
Shear strengthIn engineering, shear strength is the strength of a material or component against the type of yield or structural failure when the material or component fails in shear. A shear load is a force that tends to produce a sliding failure on a material along a plane that is parallel to the direction of the force. When a paper is cut with scissors, the paper fails in shear. In structural and mechanical engineering, the shear strength of a component is important for designing the dimensions and materials to be used for the manufacture or construction of the component (e.