Evolution of the tensile properties of the tempered martensitic steel Eurofer97 after spallation irradiation at SINQ

Small disk tensile specimens of the reduced activation tempered martensitic steel Eurofer97 were tested from −100 °C up to 370 °C before and after irradiation in the spallation source SINQ at Paul Scherrer Institute. The calculated irradiation dose and helium content are respectively 11 dpa and 540 appm. Even for such a large dose, the tensile curves showed a significant total elongation at all testing temperatures. Fractographic observations revealed a predominance of cleavage facets at −100 °C for unirradiated and irradiated specimens while at higher temperature the fracture surfaces were dominated by ductile dimples. True stress/strain curves were derived using a finite element based inverse method for simulating small disk tensile tests. The finite element simulations indicated that the local fracture stress in the neck is consistent with that calibrated based on fracture tests and that the micro-mechanisms of fracture were not affected by helium up to 540 appm.

Finite element modeling and experimental study of brittle fracture in tempered martensitic steels for thermonuclear fusion applications

Pablo Federico Mueller

In this work we have studied brittle fracture in high-chromium reduced activation tempered martensitic steels foreseen as structural materials for thermonuclear fusion reactors. Developing the adequate materials that can withstand the severe irradiation conditions of the burning plasma in a future fusion reactor is one of the major challenges to be solved in order to make profit from the great advantages of thermonuclear fusion as an energy source. High-chromium tempered martensitic steels such as F82H and the most advanced version Eurofer97 are among the main candidate materials for structural applications in future fusion power plants due to low irradiation-induced swelling, good mechanical and thermal properties, and reasonably fast radioactive decay. The most concerning drawback of these kind of steels is irradiation embrittlement, which is manifested by a ductile-to-brittle transition temperature shift to higher temperatures after irradiation whose amplitude depends on the irradiation conditions (temperature, neutron flux, neutron fluence, etc). The aim of this work was to study and model brittle fracture in the ductile-brittle transition region of this kind of steels in the as-received unirradiated conditions. It is necessary to be able to transfer laboratory specimen fracture data to real components and structures in order to assess the performance of these steels in the different operating and transient conditions they could find during the operation life of a fusion reactor. In order to do so, the specimen geometry effects and specimen size effects on measured fracture toughness need to be properly understood, taken into account and predicted with an appropriate model. In particular, specimen size effect on measured toughness is a major concern for the nuclear materials research community owing to the limited irradiation volume in current and planed materials irradiation facilities. The main results of this PhD work are summarized below. The microstructure of Eurofer97 and F82H has been characterized and compared by means of optical microscopy, scanning electron microscopy, transmission electron microscopy and energy-dispersive X-ray spectroscopy in order to identify microstructural features that could play a role in the measured fracture toughness. Both steels have similar but slightly different chemical composition and final heat-treatments but the prior austenitic grain size measured in F82H is approximately 8 times larger than in Eurofer97. It was shown that the alloying element Tantalum, added to stabilize the austenite grain size, played a different role in both steels. After a careful analysis of the particles present in both steels, it was found that Tantalum in Eurofer97 formed carbides of an average size around 100 nanometers. In contrast in F82H it did not form small carbides but formed big oxide inclusions with a size up to 30 µm. These large particles do not effectively pin the grain boundaries. The different behavior of Tantalum in these steels is believed to be mainly a consequence of the larger content of Oxygen present and the smaller amount of Aluminum in F82H compared to Eurofer97. The Master-Curve ASTM-E1921 standard is a method initially developed to determine the ductile-to-brittle transition reference temperature, T0, in fission reactor ferritic steels from a small number of experiments. In this work the applicability of the Master-Curve method to reduced activation tempered martensitic steels such as Eurofer97 and F82H was studied in detail. Fracture tests with pre-cracked sub-sized compact tension specimens (three different sizes, 0.18T, 0.35T and 0.87T of Eurofer97) were carried out in the temperature range [-196 °C, -40 °C]. The toughness-temperature behavior and scatter were shown to deviate from the ASTM-E1921 standard predictions near the lower shelf. Using the method of maximum likelihood, the athermal component of the Master-Curve was calculated to better fit our fracture toughness data from the lower to the middle transition region. We showed that these Master-Curve adjustments are necessary to make the T0 values obtained near the lower shelf with 0.35T size C(T) specimens consistent with those obtained in the middle transition region with 0.87T C(T) specimens. The ASTM-E1921 specimen size limitations, setting the maximum toughness measurable with a given specimen size, were found to be too lenient for this kind of steels. This problem was especially evident in fracture toughness data of Eurofer97 and F82H obtained in the upper transition temperature range with two different specimen sizes. Thus a more stringent specimen size requirement was proposed to avoid inconsistent transition temperature determinations. A promising local fracture model with the potential of predicting cleavage fracture toughness was studied. Finite element simulations were undertaken for compact specimens, notched specimens and tensile specimens of Eurofer97 steel tested from 20 °C down to -197 °C. Three and two dimensional as well as axisymmetric simulations were run in order to calculate the stress and strain fields at the onset of brittle fracture. For each tested temperature, the calculated load-displacement curves were found to reproduce very well those of the experiments. A local approach fracture criterion was studied. This criterion states that when the maximum principal stress is larger than a critical stress within a critical volume ahead of the crack tip, notch or neck, cleavage is triggered leading to macroscopic fracture of the specimen. It was shown that this model is able to predict the minimum fracture load of the notched specimens with the same values of critical stress and critical volume that were calibrated to predict the lower bound of fracture in compact specimens. This local approach model was also successfully used to predict the strong size effect observed experimentally in pre-cracked compact tension specimens in the upper transition region. The critical fracture stress determined in the standard tensile specimens was found higher than that of the fracture specimens. It was suggested that this difference stems from a significant difference in the stress state between the different specimens (triaxiality). Finally, the comparison between the overall fracture behavior in the transition between F82H and Eurofer97 steels indicated that these two materials are quite similar. A difference in the reference temperature T0 of about 20 °C was found, with a nominal value of -100 °C and -80 °C for F82H and Eurofer97 respectively. However, some excessive scatter in the toughness data was found in F82H with more data points than expected lying below the 1% tolerance bound; this was not observed in Eurofer97. From an engineering point of view, the entire fracture databases of these two steels are encompassed practically by the same lower tolerance bound.

EPFL2009

Embrittlement induced by the synergistic effects of radiation damage and helium in structural steels

Kun Wang

Ferritic/martensitic steels are candidate materials for fusion reactor structural components, liquid metal containers of spallation neutron sources, and accelerator driven systems, with good radiation resistance and thermo-mechanical properties. However, embrittlement resulting from the combined effects of radiation induced displacement damage (measured in dpa = displacement per atom) and transmutation products, especially helium gas, is one of the key issues. Four different steels were selected for mechanical and microstructural studies to understand the mechanisms of embrittlement induced by the combined effects of displacement damage and helium after irradiation in SINQ, the Swiss spallation source. The irradiations conditions were in the range: 10.7 ¿ 20.4 dpa with 850-1750 appm He at 160-300 °C. The evolution of the mechanical properties after irradiation was investigated by tensile and hardness tests. Radiation-induced defect clusters and helium bubbles were quantified by transmission electron microscopy (TEM). Emphasis was put on the deformation mechanisms under the different observed fracture mode, (ductile, quasi-cleavage and intergranular), whose occurrence depends on the irradiation conditions (dpa, He content and irradiation temperature). The tensile stress-strain curves and the scanning electron microscopy images of fracture surfaces showed distinct fracture mechanisms under different irradiation and test conditions. The tensile tests showed a yielding stress increase and loss of ductility of irradiated specimens. Hardness was measured on the specimens before tensile testing. The hardness results demonstrated an increasing trend with irradiation dose and helium content. TEM observations were done for all irradiated fractured specimens. Small defect clusters were observed in the 12.3 dpa specimen, but large defect clusters with loop-shape were very few. In the specimens of 17.2, 17.7 and 20.4 dpa, many large dislocation loops were detected besides small clusters. In addition, helium bubbles were observed in all specimens. The average size of defect clusters increased from 4.2 nm to 11.8 nm with dose increasing from 12.3 dpa to 20.4 dpa, whereas the number density did not change significantly. Meanwhile, the average size of visible helium bubbles increased from 1.03 nm to 1.93 nm. The microstructures in deformed area of irradiated specimens were observed and defect free channels with {110} and {112} slip planes were found in some specimens, indicating plastic flow localization. The average width of the channels is about 100 nm. Regarding the brittle samples, the TEM-lamella were extracted directly below intergranular fracture surfaces or cleavage surfaces by focused ion beam. Strikingly, deformation twinning was observed as the main feature in three irradiated specimens at high dose. Only twins with {112} planes were observed in all of these samples. The average thickness of twins is about 34 nm. Twins started from a fracture surface became gradually thinner with distance away from the fracture surface and stopped in the matrix finally. Features such as twin-precipitates interaction, twin-grain boundary and/or lath boundary interaction were observed. Twinning bands were seen to be arrested by grain boundaries or large precipitates, but could penetrate martensitic lath boundaries. Unlike the case of defect free channels, inside twins small defect-clusters, dislocation loops and dense small helium bubbles were observed.

EPFL2015

Fracture toughness characterization in the lower transition of neutron irradiated Eurofer97 steel

Nazar Ilchuk, Philippe Spätig

This research investigated the evolution of tensile, hardness, and fracture properties of Eurofer97 tempered martensitic steel following neutron irradiation. The irradiation-hardening was measured with Vickers hardness tests on broken parts of sub-sized compact tension specimens as well as with tensile tests deformed at room temperature. The fracture toughness was measured with pre-cracked sub-sized 0.18T compact tension specimens. Two specimen sets were irradiated up to a nominal dose of about 0.35 dpa at two different temperatures, 423 and 623 K, in the experimental reactor at AEKI-KFKI in Budapest. The median fracture toughness-temperature curve K(T) was characterized in the lower to middle transition region for each irradiation condition using the master-curve method. The irradiation-induced temperature shifts of K(T) were determined by calculating the reference temperature T-0 at which the median toughness is 100 MPa m(1/2). A significantly larger shift was determined for Eurofer97 irradiated at 423 K than at 623 K. Indeed, an upper shift of 98 K was found for the 423 K irradiation while only 50 K was measured for the 623 K. On the one hand, that observation reflects the difference in the irradiation-hardening following those two irradiation temperatures. On the other hand, when compared with other published data, the Delta T-0 shift at 623 K irradiation was found to be greater than expected for the corresponding irradiation-hardening. Thus, it was suggested that non-hardening embrittlement mechanisms start to operate around 623 K. (C) 2013 Elsevier B. V. All rights reserved.