Electrochemical promotion of catalysts for gas phase reactions

Recent progress made in our lab. in the field of electrochem. promotion of heterogeneous catalytic gas reactions is reviewed. The phenomenon consists of electrochem. polarization of the catalyst/solid electrolyte interface resulting in a dramatic, non-Faradaic modification of the catalytic reaction rate. Two main aspects have been addressed, the mechanistic interpretation of the phenomenon and the development of bipolar cell configurations suitable for practical applications. Fundamental studies were made using single-pellet type electrochem. cells with yttria-stabilized zirconia (YSZ) solid electrolyte. Promotion of the redn. of NO by propylene over Rh/YSZ catalyst under oxidative conditions at 300C was found to be reversible over an active, essentially metallic, rhodium but irreversible over a deactivated, presumably partially oxidized, catalyst. It was shown that anodic current application with negligible power consumption might efficiently assist the recovery of accidentally lost catalytic activity of rhodium. In situ cyclic voltammetry of IrO2/YSZ catalysts showing a linear relation between voltammetric charge and combustion rate of ethylene suggested that promotion of IrO2 was ruled by the charge stored on it. In situ measurements of work function over RuO2/YSZ catalysts established a clear relation between catalyst work function and surface concn. of chemisorbed oxygen interpreted by formation of surface dipoles between adsorbed species and adsorption sites. Transient behavior of the work function-under and after polarization was closely related to the evolution of the combustion rate of ethylene supporting the idea of promoting oxygen species spreading out over the gas-exposed catalyst surface. On the application side, two new cell designs were developed, a ring-shaped and a multiple-channel configuration both operated in bipolar polarization mode. The current bypass of the ring-shaped cell detd. from current-voltage curves was very low whereas in the multiple-channel configuration both the current bypass and the cell voltage were much higher. Feasibility of electrochem. promotion was successfully demonstrated with both configurations. Promotion of the redn. of NO by propylene in ring-shaped bipolar Rh/YSZ cells and that of the combustion of ethylene in bipolar RuO2/YSZ cells of both configurations were non-Faradaic even at high open-circuit conversions. Realization of efficient bipolar cell configurations for electrochem. promotion is very promising in view of future applications in dispersed-catalytic systems. [on SciFinder (R)]

Electrochemical promotion of Pt catalysts for gas phase reactions

Arnaud Jaccoud

The subject of this work is the study of the electrochemical promotion of catalysis (EPOC), also called non-Faradaic electrochemical modification of catalytic activity (NEMCA). In this phenomenon, application of small currents or potentials on catalysts in contact with solid electrolytes leads to very pronounced strongly non-Faradaic and reversible changes in catalytic activity and selectivity. This work concerns the system composed of platinum film electrodes, deposited on the YSZ electrolyte (ZrO2 doped with 8% Y2O3), in contact with an oxygen containing atmosphere (the O2(g),Pt/YSZ system). The aim of this work was to focus on two points in the phenomenon of EPOC: 1) The nature of the species present on the surface of the catalyst and their impact on the catalytic activity. 2) The phenomenon of permanent promotion of catalysis (P-EPOC), for which the catalytic rate enhancement is not totally reversible, leading to a long lasting activated state. The Pt electrodes were prepared via three different methods (sputtering, thermal decomposition and screen-printing) and, as expected, the resulting microstructure, observed by scanning electron microscopy (SEM), was found to depend greatly on the preparation technique. The electrochemical response of each electrode was characterized by the technique of cyclic voltammetry. Due to the occurrence of different site-related electrochemical reactions, the voltammogram shape was highly influenced by the microstructure of the Pt/YSZ contact. Based on the preliminary studies, the cermet electrode was chosen for additional electrochemical experiments, using chronoamperometry, chronopotentiometry, cyclic voltammetry, steady state polarization and impedance spectroscopy. The results of all these techniques suggest that under anodic polarization, two parallel reactions take place. The first reaction is the oxygen evolution, giving rise to a steady state current under a constant applied potential. The other reaction is the oxygen storage (oxygen injection) in the form of Pt-O species. This second process gives rise to a time dependant current under a constant applied potential, and is therefore responsible for the pseudocapacitive behavior of the electrode. Moreover, linear sweep voltammetry measurements indicated that, by application of an anodic potential, at least three types of Pt-O species were stored, following distinct kinetics. Based on the amount of stored Pt-O and on the corresponding storage kinetics, they were attributed to three different locations on the electrode: 1) at the Pt/YSZ interface, 2) diffusing from the tpb toward the Pt/gas interface, 3) diffusing from the Pt/YSZ interface toward the bulk of the platinum electrode. It has been shown that the Pt film exhibited various activity states toward the catalytic oxidation of ethylene, depending on the oxygen species present at its surface. As evidenced by XPS measurements and in agreement with the thermodynamic data for the given system, the inactive (deactivated) state has been attributed to the formation of surface platinum oxide at T > 550°C. Decreasing the reaction temperature to 525°C caused the slow spontaneous reactivation of the catalyst and several days were necessary to reach the active state, where most of the catalyst was present in its metallic state. The catalyst activity recovery could be accelerated by the application of anodic potential pulses. In agreement with the mechanism of EPOC, this was explained by the oxide destabilizing effect of the anodically produced Oδ- species. Anodic polarization also caused reversible electrochemical promotion of catalysis at unusual high temperature (600°C). In addition, very intriguing catalytic relaxation transients were observed after prolonged anodic polarization times. Indeed, it was found that enhanced catalytic activity could be maintained for up to 10 hours after current interruption. Combination of these latter results, the related literature, the state of the art model of EPOC, and the results obtained by electrochemical techniques led to the proposition of an original model based on the processes of Pt-O storage/release at various locations of the O2(g),Pt/YSZ system. According to this model, anodic polarization produces Oδ- back-spillover species, promoting the catalytic activity, in agreement with the mechanism of EPOC. In parallel, hidden oxygen species are stored at the Pt/YSZ interface and diffuse toward the Pt phase. When the polarization is switched off, these hidden oxygen species diffuse to the gas-exposed surface and cause non-Faradaic promotion, as back-spillover Oδ- do. The large amount of stored charge and its slow diffusion controlled emergence causes the rate enhancement to last for hours.

EPFL2007

Chemical and electrochemical promotion of supported rhodium catalyst

Olena Baranova

The chemical and electrochemical promotion of highly dispersed nanofilm Rh catalysts (dispersion: about 10 %, film thickness: 40 nm) has been investigated for the first time. To this end Rh metal was sputter-deposited, either on a purely ionic conductor (8 % Y2O3-stabilized ZrO2) or on a mixed ionic-electronic conductor (TiO2), the latter being a highly dispersed layer of TiO2 (4 µm) deposited on YSZ. These catalysts are designated as Rh/YSZ and Rh/TiO2/YSZ, respectively. It was established analytically that both in the Rh/YSZ and in the Rh/TiO2/YSZ system, the catalyst films have a nanoparticle-size grain structure. The Rh supported on titania is rather porous, exhibiting a higher dispersion and surface area than Rh on YSZ. Both after reduction (H2, T=400 °C) and after oxidation (O2, T=400 °C), Rh supported on TiO2 was found to be in a more highly reduced state than Rh on YSZ. After reducing treatment, the Rh/TiO2/YSZ samples contain a larger amount of weakly bonded oxygen, which can be attributed to oxygen "backspillover" from the TiO2. A major feature of this research was the electrochemical characterization of the oxygen/Rh/solid electrolyte three-phase boundary by steady-state polarization measurements and by impedance spectroscopy. These are powerful techniques for extracting experimental trends and details that are useful for an understanding of the electrochemical promotion principles. It was shown that the exchange current densities at the Rh/solid electrolyte interface are lower on account of the TiO2 layer. The exchange current densities are more than twice lower at Rh/TiO2(4 µm)/YSZ than at Rh/YSZ, demonstrating that the former interface is much more polarizable. The mechanism of oxygen exchange occurring close to equilibrium (O2/O2- couple) was investigated for the first time at Rh catalyst electrodes interfaced with solid electrolyte. The processes of cathodic oxygen reduction and anodic oxygen evolution are not symmetric, but they are similar in the two systems, Rh/YSZ and Rh/TiO2(4 µm)/YSZ. The cathodic process consists of three steps: dissociative adsorption of oxygen at the gas-exposed Rh surface, atomic oxygen diffusion to the electrochemical reaction sites (ERS), and a two-electron transfer to this oxygen on the ERS. The cathodic process is limited by interfacial diffusion of oxygen atoms from the gas-exposed metal surface to the ERS. The anodic process includes two steps: two-electron transfer reaction, which is the rate-determining step, and oxygen desorption to the gas phase. With data obtained from impedance spectroscopy at the equilibrium potential, it was possible to confirm the reaction scheme proposed. It was demonstrated that Rh nanofilm catalysts interfaced with YSZ or TiO2/YSZ can be electrochemically promoted for the reaction of ethylene oxidation. Small anodic currents cause periodic oscillations in catalytic rate and potential of the Rh/YSZ catalyst, while at Rh/TiO2/YSZ they give rise to a stable and reversible rate enhancement by up to a factor 80. The increase in ethylene oxidation rate is up to 2000 times larger than the electrochemical rate, I/2F, of O2- oxidation. The pronounced electrochemical promotion behavior that has been observed is due to the anodically controlled migration of O2- species from the electrolyte to the Rh/gas interface. At the Rh surface, these species destabilize the formation of rhodium surface oxide (Rh2O3). The existence of backspillover oxygen species has been confirmed by impedance measurements under positive applied potential. Another significant result for heterogeneous catalysis is the finding that thick as well as thin films of Rh/TiO2/YSZ catalyst are open to chemical promotion of ethylene oxidation and partial methane oxidation, ie, they offer a higher catalytic activity and stability than the Rh/YSZ catalysts. The modification of catalytic activity observed for Rh/TiO2/YSZ was attributed to either a "long-range" electronic-type SMSI mechanism or to a self-driven electrochemical promotion mechanism. In both cases, the ultimate cause of promotion are different work functions of catalyst and support. Equilibration of the work functions of two solids in contact induces surface charging, a migration of O2- ions to the catalyst/gas interface, and a weakening of the Rh-O chemisorptive bonds. It facilitates reduction of oxidized surface sites. Another important achievement of the present work was that of exploring and confirming the possibilities of current-assisted activation of Rh/TiO2/YSZ catalysts. In partial methane oxidation using close to stoichiometric gas compositions (CH4 : O2 = 2 : 1) at 550 °C, the inactive (oxidized) Rh/TiO2/YSZ catalyst was successfully activated by applied currents, either positive or negative. This phenomenon is an example of "permanent" electrochemical promotion furnishing a permanent rate enhancement ratio of γ = 11. The activation by negative currents is explained in terms of an electrochemical reduction of rhodium surface oxide, while the activation by positive currents can be explained by the mechanism of electrochemical promotion.

EPFL2005

Promotion électrochimique des catalyseurs à base de rhodium et d'iridium

Justyna Eaves

In this thesis, the electrochemical promotion of lr and Rh based catalysts was studied for the complete combustion of ethylene and propylene. The study was performed by using two types of electrocatalytical cells: a classical, pellet type cell and a tubular cell. This work has two major goals. The first one is the optimization of the employed electrocatalytical systems from electrochemical point of view. The second one concerns the study of the mechanism of the electrochemical promotion. The major part of this work concerns the electrochemical characterization of two cell types: a pellet type cell and a tubular cell. On the basis of the obtained results the modélisation of the potential and current distribution was performed, providing key parameters for the development of more efficient cell configurations. On one hand, these configurations ensure an uniform current distribution on the working electrode and enable correct catalyst potential measurement. On the other hand, it minimizes the current bypass in the bipolar tubular cell. The aim of the investigation in a two-compartment reactor was to evaluate and to compare the Au and Ir electrodes used in this work. Under 400°C, gold was found to be much worse material than lrÛ2 both as reference and counter electrode. Its potential was affected by oxygen and propylene adsorption and no equilibrium of electrochemical reaction was obtained at such low temperature. On the base of this knowledge, several materials better adapted to electrochemical promotion conditions have been proposed. Using the two-compartment reactor potential measurements under steady state conditions allowed to verify the mechanism of the propylene combustion on Rh and that of ethylene combustion on lr based catalysts proposed in the literature. Ameliorations of the existent kinetic models were proposed. The kinetic measurements were then analyzed with the additional help of ex situ XPS analysis. This study allowed to link the oxidation state of the catalyst surface with the extent of electrochemical promotion of the catalysts. It also allowed the ex situ observation of the appearance of new oxygen (oxide) species on the gas exposed surface of Ir catalyst. This new type of oxygen was different from the oxygen of Ir02 oxide, and it can represent the promoting species, according to backspiïïover theory. The same oxygen species was observed on well oxidized Ir02 catalyst surface, even before the polarization of this catalyst. Its presence was associated to the catalyst-support effect. It explains the high activity of Ir02 catalyst by comparison with the catalytic activity of lr metal. XPS analysis of Rh based catalysts indicated the possibly formation of an inferior Rh oxide (close to RhO) due to polarization. This may be a possible explanation of the observed permanent electrochemical promotion. Voltammetric charge measurements in very narrow potential window were performed while changing the catalyst thickness. The charge was demonstrated to be proportional to the catalyst thickness, suggesting the presence of the charged species on the gas exposed catalyst surface. The analogy between this situation and that of the emerged electrodes in liquid state electrochemistry was emphasized. The voltammograms obtained in this study were interpreted in the quite new, original way, which allowed to calculate the capacity of the different catalyst interfaces, the gas/catalyst interface, and the triple phase boundary, in good agreement with reference values from impedance spectroscopy measurements. Finally, the reaction rate transients during galvanostatic polarization of lr based catalyst have been moralized. The model fits well the experimental results.

EPFL2004