Summary
A material is brittle if, when subjected to stress, it fractures with little elastic deformation and without significant plastic deformation. Brittle materials absorb relatively little energy prior to fracture, even those of high strength. Breaking is often accompanied by a sharp snapping sound. When used in materials science, it is generally applied to materials that fail when there is little or no plastic deformation before failure. One proof is to match the broken halves, which should fit exactly since no plastic deformation has occurred. Mechanical characteristics of polymers can be sensitive to temperature changes near room temperatures. For example, poly(methyl methacrylate) is extremely brittle at temperature 4 ̊C, but experiences increased ductility with increased temperature. Amorphous polymers are polymers that can behave differently at different temperatures. They may behave like a glass at low temperatures (the glassy region), a rubbery solid at intermediate temperatures (the leathery or glass transition region), and a viscous liquid at higher temperatures (the rubbery flow and viscous flow region). This behavior is known as viscoelastic behavior. In the glassy region, the amorphous polymer will be rigid and brittle. With increasing temperature, the polymer will become less brittle. Some metals show brittle characteristics due to their slip systems. The more slip systems a metal has, the less brittle it is, because plastic deformation can occur along many of these slip systems. Conversely, with fewer slip systems, less plastic deformation can occur, and the metal will be more brittle. For example, HCP (hexagonal close packed) metals have few active slip systems, and are typically brittle. Ceramics are generally brittle due to the difficulty of dislocation motion, or slip. There are few slip systems in crystalline ceramics that a dislocation is able to move along, which makes deformation difficult and makes the ceramic more brittle. Ceramic materials generally exhibit ionic bonding.
About this result
This page is automatically generated and may contain information that is not correct, complete, up-to-date, or relevant to your search query. The same applies to every other page on this website. Please make sure to verify the information with EPFL's official sources.
Related courses (5)
MSE-424: Fracture of materials
This course covers elementary fracture mechanics and its application to the fracture of engineering materials.
CIVIL-522: Seismic engineering
This course deals with the main aspects of seismic design of buildings and bridges. It covers different structural design and evaluation philosophies for new and existing reinforced concrete and unrei
Show more