DISCLAIMER: The Graph Chatbot is not programmed to provide explicit or categorical answers to your questions. Rather, it transforms your questions into API requests that are distributed across the various IT services officially administered by EPFL. Its purpose is solely to collect and recommend relevant references to content that you can explore to help you answer your questions.
In this study, silica glass, optical fiber Bragg gratings (FBGs) are used for torque-induced strain monitoring in carbon fiber reinforced polymer (CFRP) hollow shafts toward the development of a methodology for structural load monitoring. Optical fibers w ...
2021
, ,
Laminated composites are prone to fracture at layer interfaces. Such damage impairs their structural response and engenders important constraints in design. In this work, the influence of ply orientation on crack growth resistance was studied for three dif ...
Delamination in composite materials is often accompanied by fiber bridging that increases resistance to crack growth. Here, delamination of two unidirectional carbon/epoxy systems was studied under monotonic and displacement-controlled fatigue loading. One ...
ELSEVIER SCI LTD2021
,
Traction-separation relations due to large scale bridging in composites are very important in modeling their fracture response. Several works demonstrated that such relations are dependent upon the specimen's stiffness and loading conditions. Experimental ...
ELSEVIER SCI LTD2020
, ,
Delamination is a very frequent damage mechanism that affects the integrity of laminated composites. In this study, the effect of ply orientation on crack growth resistance was analyzed for three different anti-symmetric interfaces (+/- 30 degrees, +/- 45 ...
ELSEVIER SCI LTD2020
Multidirectional laminates are very often used in advanced structures. However, the existing data in the literature regarding their fracture response is not conclusive. In this work, the fracture response of a +45 degrees// -45 degrees interface is investi ...
ELSEVIER SCI LTD2020
, ,
Fiber reinforced polymers (FRPs) subjected to mode I fracture show important toughening due to the development of large scale bridging (LSB). Experimental studies of this phenomenon in unidirectional carbon/epoxy laminates using double cantilever beam spec ...
ELSEVIER SCI LTD2019
,
The mode I delamination behavior of a unidirectional glass-fiber reinforced polymer with a prototype elasto-plastic polyurethane matrix (GF/PU) was investigated and compared with that of glass/epoxy (GF/EP) using double cantilever beam specimens. Fracture ...
Delamination is a well-known damage mode exhibited by laminated composites which has been extensively studied in unidirectional laminates (UD). In this work, a novel strategy consisting of the introduction of a small interlaminar defect to enhance the frac ...
In this work the differences in R-curve response and traction-separation relations due to a finite damage zone or large-scale bridging (LSB) in mode I fracture on double cantilever beams (DCB) were investigated under end opening forces (EOF) and pure momen ...