KSm(MoO4)2, an incommensurately modulated and partially disordered scheelite-like structure

The incommensurately modulated scheelite-like KSm(MoO4)2 structure has been refined in the monoclinic superspace group I2/b(ab0)00 by the Rietveld method on the basis of synchrotron radiation powder diffraction data. The systematic broadening of satellite reflections has been accounted for by applying anisotropic microstrain line-broadening. The microstructure has been studied by transmission electron microscopy (TEM). The partial disorder of the K and Sm cations in the A position is best approximated by a combination of harmonic and complex crenel functions with (0.952Sm + 0.048K) and (0.952K + 0.048Sm) atomic domains. This combination yields a compositional wave distribution from {KMoO4} to {SmMoO4} observed in the ab structure projection along q. The specific features of KSm(MoO4)2 and degree of the A-cation ordering are discussed in comparison with the previously reported structure of KNd(MoO4)2.

LiZnNb4O11.5: A novel oxygen deficient compound in the Nb-rich part of the Li2O–ZnO–Nb2O5 system

Alla Arakcheeva, Gervais Chapuis, Philip Pattison

A novel lithium zinc niobium oxide LiZnNb4O11.5 (LZNO) has been found in the Nb-rich part of Li2O–ZnO–Nb2O5 system. LZNO, with an original a-PbO2 related structure, has been synthesized by the routine ceramic technique and characterized by X-ray diffraction and transmission electron microscopy (TEM). Reflections belonging to the LZNO phase, observed in X-ray powder diffraction (XRPD) and electron diffraction, have been indexed as monoclinic with unit cell parameters a=17.8358(9) A˚ , b=15.2924(7) A˚ , c=5.0363(3)A˚ and g=96.607(5)1 or as a-PbO2-like with lattice constants a=4.72420(3) A˚ , b=5.72780(3) A˚ , c=5.03320(3) A˚ , g=90.048(16)1 and modulation vector q=0.3a*+1.1b* indicating a commensurately modulated a-PbO2 related structure. The monoclinic cell is a supercell related to the latter. Using synchrotron powder diffraction data, the structure has been solved and refined as a commensurate modulation (superspace group P1121/n(ab0)00) as well as a supercell (space group P21/b). The superspace description allows us to consider the LZNO structure as a member of the proposed a-PbO2-Z (3+1)D structure type, which unifies both incommensurately and commensurately modulated structures. HRTEM reveals several types of defects in LZNO and structural models for these defects are proposed. Two new phases in Li2O–ZnO–Nb2O5 system are predicted on the basis of this detailed HRTEM analysis.

2010

Synthesis, crystal growth and physical properties of the frustrated spin ladder material BiCu2PO6

Shuang Wang

In recent years quantum antiferromagnets with an intrinsically disordered (“spin liquid”) ground state and an energy gap in the spin excitation spectrum have received a great deal of attention. In search for new experimental realizations of spin-ladder and related models, we have embarked upon a new interesting family of low-dimensional materials with the general formula BiCu2AO6 (A = P, V and As). Among them, BiCu2PO6 shows a structure where Cu spins appear to form a two-leg zigzag ladder, which is believed to be a valuable model of a quantum magnet. However, for detailed studies of quantum magnetism, single crystals are indispensible. Therefore, in this thesis, synthesis and characterization of the newly-discovered spin ladder material BiCu2PO6 (BCPO) and its derivatives in the form of powder and single crystal are presented. Polycrystalline samples of Bi(Cu1-xZnx)2PO6 (x= 0.01, 0.02, 0.03, 0.04, 0.05 and 1), Bi1-y(Ca, Sr, La )yCu2PO6 (y = 0.15, 0.5 and 1) and BiCu2(P1-zVz)O6 (z = 1) were synthesized in this work. The solid state synthesis reactions, phase purity and thermal properties of the samples, substitution solubility, and preliminary magnetic susceptibility have been studied by thermal analysis (TG-DTA), X-ray powder diffraction (XRD), and Scanning Electron Microscope (SEM) as well as DC magnetization measurements, respectively. The BiCu2PO6 structure shows a remarkable chemical flexibility and interesting substitution effects. For detailed studies of the magnetic properties, well characterized large single crystals are indispensable. Thus in this thesis, a number of single crystal growth experiments have been performed using the Travelling Solvent Floating Zone method (TSFZ). Under the elaborated crystal growth conditions (growth rate of ~1 mm/h, gas mixture of 20% O2 in Argon, total 3 pressure (6~6.5 bar), high quality cm -size single crystals of Bi(Cu1-xZnx)2PO6 (x = 0, 0.01, 0.03, 0.05) have been successfully grown for the first time. For these crystals phase purity, crystal morphology/orientation, defect density, chemical composition distribution, crystal structure (room temperature and 1.5 K) and single crystal quality were thoroughly studied based on X-ray and neutron powder diffraction, optical and scanning electron microscopy, X-ray/neutron Laue diffraction, ICP-OES/X-ray fluorescence and two-axis neutron diffraction. Moreover, the specific heat Cp (H,T), AC susceptibility χ(H,T) and DC magnetization M(H,T) measurements on well-characterized single crystal samples of the undoped BCPO and 5% Zn-doped BCPO with the field applied along main crystallographic axes were performed in order to study the unique low temperature magnetic behaviour exhibited in this system, such as anisotropy of the magnetic properties, impurity-induced magnetism by the substitution of non-2+ magnetic cations (e.g. Zn ) and frustration. The magnetic phase diagram (H-T) under low field has been constructed. Further results obtained by close collaborators, based on the measurements made on single crystal samples grown in this thesis, including field-induced quantum phase transitions, NMR, Raman studies are attached directly at the end of this thesis.

EPFL2013

Characterization at the Atomistic Level of Defective Structures in Complex Materials

Piyush Agrawal

Defects are key to enhance or deploy particular materials properties. In this thesis I present analyses of the impact of defects on the electronic structure of materials using combined experimental and theoretical Electron energy loss spectroscopy (EELS) in (Scanning) Transmission Electron Microscopy. The energy loss near-edge structure (ELNES) in EELS reflects the element-specific electronic structure providing insights into bonding characteristics of individual atomic species. New electron optical devices have boosted the analytical capabilities by which materials can be investigated with atomic resolution and single atom sensitivity using (scanning) transmission electron spectroscopy (STEM/TEM).With the help of aberration correctors for forming small electron probes, high intensity electron beams can nowadays be focused to clearly less than 100 pm which has enhanced the resolution and sensitivity in analytical scanning transmission electron microscopy (STEM). Various kinds of defects in different complex oxides were studied: point defects like oxygen vacancies in BiVO4 and SrMnO3, edge-dislocations in BiFeO3, and planar defects in GaAs. By comparison with experimental data, structures for these systems were proposed based on all-electron density functional theory (DFT) code Wien2k. By comparing theoretical calculations and experimental data, a pronounced surface reduction in the oxidation state of vanadium in BiVO4 from +5 to +4 was unveiled, which is due to a high density of oxygen vacancies, and its importance in potential application of BiVO4 in photoelectrochemical energy conversion. A similar study was performed on a series of SrMnO3 thin films with different epitaxial strain where theoretical investigations revealed the impact of oxygen non-stoichiometry and strain on the O-K ELNES. In the next study, molecular dynamics simulations were combined with FEFF-based EELS calculations and its comparison with experiments was helpful for the correct prediction of the edge dislocation core structure in BiFeO3. This study also confirmed the presence of Fe atoms in the core of the edge dislocation which possibly makes these defects ferromagnetic whereas the bulk structure is known to be antiferromagnetic. This thesis has established methodologies for utilizing different codes, illustrating how links between experimental and theoretical ELNES can be used in revealing structural information around defects and how defects affect materials properties. This tandem methodology of theory and experiments is applicable to various future materials where the reliable interpretation of EELS data is pivotal in unfolding mysteries of such technologically important materials.