Monodispersed Pd Nanoparticles for Acetylene Selective Hydrogenation: Particle Size and Support Effects

Monodispersed Pd nanoparticles (8, 11, and 13 nm in iameter) as confirmed by high resolution transmission electron microscopy were prepared via the reverse microemulsion method and deposited on structured supports consisting of carbon nanofibers (CNF) grown on sintered metal fibers (SMF). The CNF/SMF supports were subjected to oxidative treatments to introduce O-functional groups on the CNF surface. These groups were characterized by temperature-programmed decomposition (TPD) and X-ray photoelectron spectroscopy. The catalysts were used to study (a) the effect of Pd size and (b) the effect of the support nature on the selective acetylene hydrogenation. Antipathetic size dependence of TOF disappeared at particle size bigger than 11 nm. Initial selectivity to ethylene was found size-independent. The deactivation due to coke deposition was faster for smaller particles. The structure-sensitivity relations for the catalysts investigated are discussed in terms of “geometric” and “electronic nature” of the size effect and rationalized regarding Pd-Cx phase formation which is size-dependent. Supports with increased acidity diminished the formation of coke and changed the byproduct distribution toward ethane.

Novel catalytic applications of carbon nanofibers on sintered metal fibers filters as structured supports

Marina Ruta

Supported metal catalysts are important from both an industrial and a scientific point of view. They are used, amongst others, in large-scale processes such as catalytic reforming, hydrotreating, polymerization reactions and hydrogenations. Often, these catalysts consist of nanosized metal particles deposited on a suitable support, which acts as an anchor for the active phase and, in several cases, contributes to improve the overall catalyst performances. The growth of carbon nanofibers on sintered metal fibers filters (CNF/SMF) by hydrocarbons catalytic decomposition results in a structured composite material presenting all the suitable characteristics for its application as catalyst support. The main objective of this thesis was to develop novel catalytic systems based on CNF/SMF as catalytic support for continuous gas-phase hydrogenations. At first, the synthesis of CNF/SMF was optimized to tailor the properties of the material for further applications as catalytic support. The use of ethylene as carbon precursor and high synthesis temperature (973K) provided high yields of well-ordered CNF with increased specific surface area (SSA), up to 516 m2/g. On the other hand, the synthesis of CNF by ethane decomposition, which is less reactive than ethylene, resulted in a support with higher permeability, minimizing the pressure drop and being more suitable in a continuous-flow reactor. After the synthesis, the CNF surface was activated by treatment with O3 or H2O2. A novel technique, which consist of XPS analysis after step-wise TPD in UHV conditions, was developed and applied for the surface characterization. It allowed to assess the nature of the functional groups created on the CNF surface. The O3-activation was found the most effective for increasing the acidity of the CNF/SMF surface, yielding a relatively high amount of carboxylic functional groups. These groups are important because involved in the chemical anchoring and stabilization of the active metal deposited on the support. Industrially, many hydrogenations are performed over supported metal catalyst. The majority of these reactions are known to be structure sensitive reactions, so the control of the metal particle size is crucial in order to study the catalyst activity and selectivity. We prepared monodisperse-sized Pd nanoparticles (8, 11 and 13 nm) via the reverse microemulsion method and deposited on CNF/SMF and activated-CNF/SMF for a two-fold study: the effect of the nanoparticles size and the effect of the support nature on the selective hydrogenation of acetylene. The antipathetic size dependence of the TOF disappeared at particle size bigger than 11 nm. The initial selectivity to ethylene (∼60%) was found size-independent. The structure-sensitivity relations have been discussed in terms of "geometric" and "electronic" nature of the size-effect and rationalized assuming a Pd-Cx phase formation which is known to be size-dependent. CNF/SMF supports with increased acidity diminished the formation of coke and changed the by-products distribution, diminishing the catalyst deactivation. Subsequently, CNF/SMF was applied to develop a new catalytic system: the Structured Supported Ionic Liquid Phase (SSILP) catalyst, embedding an active Rh complex. The selective gas-phase hydrogenation of 1,3-cyclohexadiene to cyclohexene was used as model reaction. The SSILP based on CNF/SMF supports showed a high turnover frequency, up to 250 h-1 and selectivity > 96%. Multiple advantages of supporting a homogeneous active phase, dissolved in IL, on CNF/SMF have been demonstrated: the thin layer of IL was homogeneously distributed over the mesoporous support, so mass transfer limitations could be avoided, furthermore the chemical inertness of the CNF prevented any interaction between the active phase dissolved in IL ensuring an efficient use of the Rh complex. The SSILP concept can be applied not only for the "heterogenization" of a transition metal catalyst, but also to obtain metal nanoparticles with monodispersed size via the reduction of a metal precursor dissolved in IL. In this case, IL provides a suitable environment for the nucleation and growth of the nanoparticles. By applying the SSILP concept to the selective hydrogenation of acetylene, the influence of IL on the stability of the nanoparticles was investigated. Moreover, the different solubilities of reactants and products in the IL phase allowed to improve the selectivity toward ethylene. Monodispersed Pd nanoparticles of 5 and 10 nm in SILP on CNF/SMF showed excellent long-term stability. The lower solubility of ethylene than acetylene in the IL had the beneficial effect of allowing high selectivity to ethylene up to 85%, due to the inhibition of its consecutive hydrogenation to ethane. In conclusion, a novel catalytic system for continuous-flow, gas-phase hydrogenations was conceived, taking advantage of the suitable characteristics of CNF/SMF supports. The SSILP concept, involving both homogeneous and heterogeneous active phases has been demonstrated, indicating a great potential and flexibility for continuous-flow industrial applications.

EPFL2008

Nanofibres de carbone sur filtre métallique comme support catalytique structuré

Pascal Tribolet

The main objectives of this work are 2-fold : The development of a novel type of composite material based on carbon nanofibers supported on sintered metal fibers filters (CNF/SMF) and to explore the use of this material as a catalytic support for a model reaction: selective hydrogenation of acetylene. The advantages of this novel support are: Due to carbon nanofibers, it combines a graphitic structure with a high specific surface area without microporosity. Supported carbon nanofibers can be used in a fixed bed reactor without very high pressure drop. Combination of two materials with high thermal conductivity gives a composite which keeps this property. It is suitable for highly exo/endothermic reactions, diminishing temperature gradients in the catalytic bed. The synthesis of carbon nanofibers on SMF filters was carried out by ethane catalytic decomposition at 655°C directly on metallic filters. An oxidation of SMF followed by a reduction in H2 create surface roughness, leading to a larger area for CNF nucleation. The CNF formation mechanism includes several steps: it starts with carbon deposition on metallic surface followed by its diffusion into the metal leading to carbides formation. When the limit of carbon solubility is attained, a layer of carbon is formed on the surface of metallic fibers. High tension within the bulk metal leads to carbide dissociation and by phase separation to graphite formation, which pushes the metallic particles through the carbon layer. Nickel, stainless steel an Inconel (an alloy of mainly nickel, iron and chromium) filters were used. The latter gave the highest uniformity of the carbon nanofibers layer showing an excellent mechanical stability. In order to control carbon deposition on the filters, a formal kinetic analysis of the decomposition reaction was undertaken. Partial orders of 1 for ethane, -2 for hydrogen and an apparent activation energy of 235 kJ/mol were obtained. The observed kinetics suggests strongly that the C – C bond scission is the rate determining step and not carbon diffusion into the metal which is often reported in the literature. The synthesis procedures like time on stream and reaction temperature were optimized: 1 hour of a mixture C2H6:H2:Ar (3:17:80) decomposition over SMFInconel at 655°C lead to ∼6% of carbon, leading to a CNF layer of 1 µm thickness covering the metallic fibers entirely. This material presents a high specific surface area (22.2 m2/g) and a low pressure drop for the gas flowing through. The carbon nanofibers have a diameter between 20 and 50 nm and a crystalline structure with platelets morphology where the graphene layers are stacked one above the other. Their surface is composed almost exclusively of carbon and hydrogen. Amongst the multiple possible applications of this novel composite material, its use as a catalyst support was assessed. Selective hydrogenation of acetylene was carried out over palladium supported on CNF/SMF and compared with commercial supports (ACF, EGF and AGF). The activated carbon fibers cloth (ACF) led to a Pd activity at least twice as E-type glass fibers tissue (EGF) or EGF covered by an alumina layer (AGF). Reaction kinetics was studied for Pd/ACF, leading to acetylene and hydrogen partial orders of -0.5 and 2.4, respectively and apparent activation energy of 50 kJ/mol. The negative partial order for C2H2 suggests high adsorption strength of this compound compared to other reagents on palladium. This particularity allows Pd to be selective. Hydrogenations are known to be structure sensitive. Therefore the catalyst activity for the model reaction depends on Pd particle size. It increases for large particle sizes. The control of this parameter was a priority. Variations of the palladium precursor, of the support and catalyst treatment were carried out. Micro-wave plasma was used since it is fast and has low energy consumption allowing chemically modifying the carbon support surface and activating catalyst after impregnation. This controls not only palladium sintering, but also decomposes tetraaminopalladate more efficiently, resulting in a catalyst activity of one order of magnitude higher. In order to control the palladium deposition on CNF/SMFInconel composite, it is important to have surface functional groups. The activation of carbon nanofibers was carried out with a 4 hours treatment in a boiling aqueous solution of hydrogen peroxide. This led to an amount on surface oxygen containing groups, per mass of carbon, higher than in ACF. Palladium particle size on the composite was controlled by support activation, the use of several metal precursors or different loadings or by a thermal treatment in argon at 500°C. Optimisation of the procedure allowed to obtain in a controlled way an average palladium particle sizes between 3.6 and 25 nm. The activity and selectivity towards ethylene of Pd/CNF/SMFInconel were observed to be higher compared to palladium supported on activated carbon, alumina or barite. Graphitic nature of carbon nanofibers, leading to strong metal-support interaction, was accounted as responsible for these improvements. The high thermal conductivity of the composite CNF/SMF ensured good heat transfer released due to the exothermicity of the reaction and allowed to work close to isothermal conditions in the catalytic bed. Finally it can be concluded, that for the first time carbon nanofibers synthesis was carried out in one step on sintered metal fibers filters, resulting in a novel structured composite material combining different specific properties and having promising potential applications.

EPFL2006

Structure sensitivity of selective acetylene hydrogenation over the catalysts with shape-controlled palladium nanoparticles

Rocio Micaela Crespo Quesada, Artur Yarulin

The structure sensitivity of acetylene hydrogenation on catalysts with controlled shape of palladium nanoparticles was studied. Palladium particles of cubic (Pd-cub), cuboctahedral (Pd-co) and octahedral (Pd-oct) shapes were obtained by a colloidal method. Poly(N-vinyl)pyrrolidone (PVP) was used as the stabilizer of colloidal solutions. In order to eliminate the effect of the polymer on the properties of the catalyst, PVP was removed from the surface of the particles after their transfer to the support by simultaneous treatment with ozone and UV radiation. This allowed complete cleaning of the catalyst surface from the organic stabilizer without any change in the morphology of particles. The effectiveness of this treatment method was confirmed by X-ray photoelectron spectroscopy and scanning electron microscopy. It was found experimentally that the shape of nanoparticles does not influence the catalyst selectivity, but the activity decreases in the order Pd-oct > Pd-co > Pd-cub. Since octahedrons consist of (111) faces, the cubes contain only (100) faces, and the cuboctahedrons are composed of faces of both types, Pd-111 is more active than Pd-100. Calculations with the use of a statistical method showed that the similar to 3-nm Pd octahedrons are nanoparticles with optimum shape and size, giving maximum catalyst activity.