In situ dynamic observations of perovskite crystallisation and microstructure evolution intermediated from [PbI6](4-) cage nanoparticles

Ke Gao, Feng Liu, Yi Liu, Cheng Wang, Wei Zhang, Lichen Zhao, Rui Zhu
Nature Publishing Group, 2017
Journal paper

Abstract

Hybrid lead halide perovskites have emerged as high-performance photovoltaic materials with their extraordinary optoelectronic properties. In particular, the remarkable device efficiency is strongly influenced by the perovskite crystallinity and the film morphology. Here, we investigate the perovskites crystallisation kinetics and growth mechanism in real time from liquid precursor continually to the final uniform film. We utilize some advanced in situ characterisation techniques including synchrotron-based grazing incident X-ray diffraction to observe crystal structure and chemical transition of perovskites. The nano-assemble model from perovskite intermediated PbI6 cage nanoparticles to bulk polycrystals is proposed to understand perovskites formation at a molecular-or nano-level. A crystallisation-depletion mechanism is developed to elucidate the periodic crystallisation and the kinetically trapped morphology at a mesoscopic level. Based on these in situ dynamics studies, the whole process of the perovskites formation and transformation from the molecular to the microstructure over relevant temperature and time scales is successfully demonstrated.

Official source

https://infoscience.epfl.ch/record/229573?ln=en

About this result

This page is automatically generated and may contain information that is not correct, complete, up-to-date, or relevant to your search query. The same applies to every other page on this website. Please make sure to verify the information with EPFL's official sources.

Related concepts

Related publications

Piezoelectric anisotropy-phase transition relations in perovskite single crystals

Marko Budimir, Dragan Damjanovic, Nava Setter

The orientation dependence of the longitudinal piezoelectric coefficient, d(33)(), is investigated as a function of temperature in BaTiO3 and PbTiO3 crystals using the Landau-Ginsburg-Devonshire theory. We show that a presence of the ferroelectric-ferroelectric phase transitions in BaTiO3 leads to enhanced d(33)() along nonpolar directions. The reason for this is that in the vicinity of a phase transition temperature at which a polarization vector changes its direction (tetragonal-orthorhombic/monoclinic, orthorhombic/monoclinic-rhombohedral), the shear piezoelectric coefficients become high. It is shown for all ferroelectric phases of BaTiO3 that the shear stress deforms the crystal cell and changes the polarization direction in a similar way as the corresponding temperature-induced phase transition. The influence of the piezoelectric shear effect on the anisotropy of d(33)() is particularly pronounced in the orthorhombic/monoclinic phase where the piezoelectric shear coefficients are determined by the presence of both the high-temperature tetragonal and the low-temperature rhombohedral phases. In PbTiO3, which does not exhibit ferroelectric-ferroelectric phase transitions, the shear piezoelectric effect is weak and d(33)() has its maximum along the polar axis at all temperatures. These results can be generalized to include phase transitions induced by electric-field and composition variations and are valid for all perovskite materials, including complex relaxor-ferroelectric perovskites that have recently attracted attention for their exceptionally large piezoelectric properties. (C) 2003 American Institute of Physics.

2003

Conductivity, dielectric and piezoelectric properties of SrBi4Ti4O15

Strontium Bismuth Titanate is a very promising material for high temperature piezoelectric applications, its elevated ferroelectric phase transition (530°C), linear piezoelectric properties under low field and relatively low room temperature conductivity (compared to others Bismuth Titanates) make it very attractive for precision sensors. However, under severe conditions (low frequency, high field, high temperature or low oxygen partial pressure) some of those advantages disappear. Piezoelectric response is dominated by charge drift in general becomes unstable. Above all, at high temperature and low oxygen partial pressure, a large conductivity increase reduces the piezoelectric efficiency of the material, in this work, electrical conductivity, piezoelectric properties and dielectric permittivity of SrBIT ceramic have been investigated in conditions of high temperature, low oxygen partial pressure, low to moderate driving field and frequency. As a result of this research, a better understanding of SrBIT properties was achieved. Thanks to a careful study of SrBIT processing as a bulk ceramic, a reproducible route was established. Many basic mechanisms leading to both SrBIT crystallization and sintering have been identified. It was demonstrated that a detailed knowledge of the exact processing conditions is required in order to achieve high quality material. DC conductivity measurements were carried out as a function of temperature, oxygen partial pressure and dopant concentration. It was found that the apparent activation energy for conduction for undoped SrBIT was 1 eV between 140 and 220°C and 1.5 eV between 450 and 700°C. Decrease of the activation energy in the lower temperature range has been discussed considering grain boundary conductivity, as a transition from electronic to ionic conduction or as consequence of small polarons conduction. It was shown that lower activation energy resulted from Manganese doping (0.5 eV), this was interpreted as either growing influence of grain boundary conductivity as dopant concentration increases or as shallow hole trap formation. DC conductivity measurements and acceptor/donor doping experiments demonstrated p-type conductivity in the low temperature range (up to 220°C) as donor doping decreases conductivity, while oxygen partial pressure controlled measurements indicated n-type conductivity at higher temperature (above 700°C). An electrical impedance analysis was performed with several equivalent circuits. The aim of these models was to simulate the impedance of SrBIT. The best approximation was found with a distributed element of Havriliak-Negami type. However, as the physical justification for this circuit was not clear, the investigation of the grain, grain boundary and electrode impedances was performed with multiple discrete parallel RC elements. With temperature, grain size and oxygen activity variations, the identification of three separate contributions as grain, grain boundary and electrode was realized. The anisotropy of conductivity and permittivity was demonstrated with textured material and both DC and AC analysis. With the master curves built for the electrical modulus, it was found that the impedance probably related to Bismuth oxide layers produces an additional high frequency are. From this finding and by comparing characteristic relaxation frequencies of undoped, 2 mol.% Mn and 4 mol.% Nb SrBIT, it was determined that conductivity is higher in the ab plane direction than in the c direction within both perovskite units and Bismuth oxide layers. With conductivity measurements under controlled oxygen partial pressure, it was found that an acceptor-based (intrinsic or extrinsic) model could be used to describe the electrical conductivity under controlled oxygen partial pressure of both undoped and 2 mol.% Mn doped SrBIT. However, as neither a pO2-1/6 region (intrinsic oxygen vacancies compensated by electrons) for undoped SrBIT nor a pO2-1/4 region (oxygen vacancies compensated by singly ionized acceptors) for Mn doped SrBIT were seen, it was concluded that the acceptorcontrolled model is not sufficient for a complete description of SrBIT. For this reason and in order to include the low oxygen partial pressure behavior of undoped SrBIT, a donor-based (intrinsic) model was also considered. The source of intrinsic donors would be in that case Bi3+ cations sitting on Sr2+ sites in the perovskite sublattice. Considering Bismuth vacancies as the negative compensating species, both pO2-1/4 and pO2-independent regions could be predicted with the model. However, even if the donor-controlled model seems to better match conductivity measurements in the full PO2) range, rejecting the acceptor-based model would be an error. It is actually not demonstrated that in SrBIT the concentration of exchanged Bismuth cations is always (all temperature, pressure) larger than the natural acceptor impurity concentration. It is very likely that the cation exchange is dependent of the oxygen partial pressure. It is also not proved as suggested in the literature that direct compensation between exchanged Strontium and Bismuth exists, reducing the net donor-excess. With the acceptor-controlled model, the mass-action constants for reduction and for ionization of intrinsic carriers across the band gap were determined. The band gap of SrBIT was estimated to be 3.5 eV. The ionic conductivity of SrBIT was determined at high temperature with measurements under controlled oxygen partial pressure. It was found that the electrical conductivity of SrBIT is probably mixed (electronic and ionic) as the estimation of the transference number provided quite large values (t=0.8 at 800°C). From electronic and ionic conductivity data, mixed conduction can actually be predicted in a large temperature range (above room temperature). The piezoelectric measurements using direct effect demonstrated that it is actually possible to unlock piezoelectrically active ferroelectric domain walls and create non-linear piezoelectric properties in undoped SrBIT. This occurs above a threshold elastic field, which is thermally activated. With a piezoelectric composite, it was demonstrated that the electromechanical coupling between two different phases creates a piezoelectric relaxation. This one could be positive or negative depending on the respective properties of each composite's component. It was shown experimentally that a small temperature change is sufficient to transform a positive relaxation into a negative one. While these experiments did not provide a detailed microstructural explanation for the piezoelectric relaxation observed in 2 mol.% Mn doped SrBIT, they gave a first insight into an original phenomenological approach. Microstructure and piezoelectric properties were related with the calculation of a piezoelectric relaxation composite made of two textured samples. This demonstrated that a piezoelectric relaxation may occur just because of anisotropy. Microstructural reproduction of this coupling is actually an important feature of Aurivillius phases.

EPFL2000

Strontium barium niobate (SrxBa1-xNb2O6, shortly SBN) is a solid solution system with tetragonal tungsten bronze crystal structure. It exhibits a ferroelectric phase with only one polar axis and a transition temperature depending on the Sr/Ba ratio. This thesis studies the growth of SBN thin films, in order to obtain a ferroelectric thin film model system for the study of 180° domain switching close to the ferroelectric phase transition. SBN has been chosen not only because uniaxial, but because it is possible to tune the temperature of phase transition varying the Sr/Ba ratio. It is thus possible to study electric properties of the phase transition close to room temperature, where conduction phenomena related to defects are normally lower. Thin films of SBN were grown by Pulsed Laser Deposition in a vacuum system constructed during this thesis work. For the formulation of a model it is desirable to have a system as close as possible to a single crystal. Therefore deposition parameters have been optimized to grow SBN thin films with the polar axis oriented perpendicular to the film plane. The films are integrated in parallel plate capacitor structures, in order to measure dielectric properties. The stability of the ferroelectric phase is found to be sensitive to impurities; contaminants with concentration below 1% induce a lowering of the transition temperature of about 100°C. Strain as well has influence on the phase transition; in the case of substrate with thermal expansion coefficients different from the SBN ones, the SBN film is under stress. A 0.6% tensile strain induces a lowering of the transition temperature of about 100°C, this is the case of silicon single crystal substrate. Grown on strontium titanate single crystals (STO), whose thermo-mechanical properties are close to the one of SBN, the films exhibit a phase transition temperature compatible with the one measured on single crystals. The obtained films suffer from leakage that is reduced by thermal treatment in oxygen rich atmosphere. The oxygen vacancies, created during the deposition process, are considered to be responsible of leakage. Vacancies recovery upon annealing does not eliminate the problem, and measurement of polarization at room temperature is difficult. However, piezoelectric measurements performed on individual grains, with atomic force microscope, prove that these have ferroelectric properties; by these experiment has been proved that it is possible to switch the polarization. Films with a disordered structure of grains are much less leaky than the ones with columnar grains spanning the whole cross section. These observations lead to the conclusion that conduction goes trough the grain boundaries. On STO single crystals, SBN grows epitaxial in Volmer-Weber mode. With a suitable preparation of the substrate surface, it is possible to induce the growth of films with different orientations of the polar axis: in the film plane, perpendicular to it or inclined of 45°. A model is proposed, explaining the epitaxial relation with the substrate on the basis of the perovskite kernel contained in the unit cell of the tetragonal tungsten bronze structure. The film grows from the nucleation of the perovskite structure that rules the orientation of the film; the high temperature at which the substrate is kept during the deposition, assure the necessary mobility for the arriving atoms to organize in the SBN structure around these nuclei. The study of literature data allows to state that such a model is valid not only for substrates with perovskite structure, but can be extended to substrates with a cubic crystal structure, like magnesium oxide.

EPFL2005

Conductivity, dielectric and piezoelectric properties of SrBi4Ti4O15

EPFL2000

EPFL2005